Poly(methyl acrylate)-poly(acrylonitrile) 공중합체의 응력완화 실험은 용매기를 부착한 인장 시험기를 사용하여 여러 온도의 공기 중, 증류수 용액에서 실행하였다. Eyring-Halsey 모델의 이론적인 응력완화식에 응력완화 실험 결과를 적용하여 여러 가지 유동 파라메타를 계산하였다. 비결정성 영역에서의 유동단위의 고찰을 위하여 유동 파라메타와 결정크기로부터 섬유고분자 물질의 자체확산, 홀 부피, 점성, 열역학파라메타 등을 계산하였다. 이들 시료의 유동 파라메타는 유동 단위의 홀부피, 자체확산, 유동 열역학 파라메타와 직접적인 연관을 갖는 것으로 규명되었다.

Single crystals of cobalt(II) and nickel(II) complexes of 4-nitrobenzoic acid have been successfully grown by gel diffusion technique. The grown crystals were characterized by elemental analysis, FT-IR and UV-Visible spectroscopy. The structure of the grown crystals was elucidated using single crystal X-ray diffraction studies. The title compounds $[Co(Pnba)_2(H_2O)_4]{\cdot}2H_2O$ 1 and $[Ni(Pnba)_2(H_2O)_4]{\cdot}2H_2O$ 2 where PnbaH=4-nitrobenzoic acid, crystallize in centrosymmetric triclinic space group P-1. Magnetic susceptibility measurements reveal that the compounds are paramagnetic in nature. The mechanical strength of the grown crystals was determined by Vicker's microhardness studies. The ligand (4-nitrobenzoic acid) and the complexes have been screened for their biological activity against various bacteria and fungi. The activity data show that the biological activity of the complexes is higher than that of the ligand.

국내 배경지역인 제주도 한라산 1100 고지에서 2012년 가을철에 $PM_{10}$, $PM_{2.5}$ 미세먼지를 채취하여 이온 및 원소 성분을 분석한 결과로부터 대기경계층(ABL) 미세먼지의 화학조성과 입자크기별 분포 특성을 조사하였다. $PM_{2.5}$ 미세입자($d_p$ < $2.5{\mu}m$)에서는 2차 오염물질인 nss-$SO{_4}^{2-}$, $NH_4{^+}$, $NO_3{^-}$ 농도가 각각 4.84, 1.98, $1.27{\mu}g/m^3$로 상대적으로 높고, 전체 질량의 58.2%를 차지하였다. 반면에 $PM_{10-2.5}$ 조대입자($2.5{\mu}m$ < $d_p$ < $10{\mu}m$)에서는 이들 세 성분의 농도가 각각 0.63, 0.21, $1.10{\mu}g/m^3$로 전체 질량의 22.8%를 차지하였다. 또 수용성 이온성분들 중 $NH_4{^+}$, nss-$SO{_4}^{2-}$, $K^+$, $CH_3COO^-$은 주로 미세입자에 분포하고, $NO_3{^-}$은 미세입자와 조대입자에 고르게 분포하나, $Na^+$, $Cl^-$, $Mg^{2+}$, nss-$Ca^{2+}$은 조대입자에 더 많이 분포하는 특징을 나타내었다.

2013년 국내에서 시판된 7개의 이부프로펜과 11개의 덱시부프로펜의 광학순도를 키랄 HPLC로 조사하였다. Chiralcel OD-H 칼럼과 LUX-Cellulose-1 칼럼을 키랄 정지상으로 사용하였고, hexane:isopropanol:acetic acid가 100:1:0.1로 혼합된 용액을 전개용매로 사용하여 흐름속도 1.0 mL/min에서 분석하였다. 각 시료를 최소 3회 이상 분석하여 얻은 평균값을 각각 계산하여 데이터로 이용하였고, 이들의 상대표준편차 평균값도 0.19%로 아주 작게 나타나 실험의 정밀도가 높음을 확인하였다. 실험에 사용된 11개 덱시부프로펜의 광학순도 평균값은 처음 판매가 허가된 2004년의 평균값인 99.2%에 비해 낮아졌지만 2010년의 평균값인 95.6% 보다는 높은 97.5%를 보였다. 그리고 실험에 이용된 모든 이부프로펜 두 거울상 이성질체의 조성비는 2010년 조사값(44:56)과는 달리 거의 50:50으로 얻어졌다.

A column solid phase extraction procedure based on modified polyurethane foam (PUF) by a newly synthesized Schiff base ionophore, named 2,2'-{iminobis[propane-3,1-diylnitrilo(1E)prop-1-yl-1-ylidene]}diphenol, was developed for preconcentration step of trace amounts determination of copper ions in water samples by atomic absorption flame spectroscopy. The influence of parameters on the adsorption process such as sample pH, amount of modified PUF packed in the column, type and volume of stripping reagent and its flow rate were investigated and optimized. Under optimum experimental conditions, the calibration graph was linear in a relatively wide range ($0.005-210{\mu}g/ml$) with a limit of detection $0.002{\mu}g/ml$ of copper. The proposed method allows achieving to a concentration factor of >133. The capacity of a column (1.6 cm i.d.) packed by 6 g of PUF modified by 12 mg of the Schiff base was found to be $247.7({\pm}2.1){\mu}g$ of copper. It was found that the adsorption process was highly selective towards copper ions with respect to some associated metal ions. The presented procedure was successfully applied for determination of copper in some water samples.

Electrochemical copolymerization of o-chlorophenol (oCP) with o-hydroxyphenol (oHP) was carried out in aqueous $H_2SO_4$ by using cyclic voltammetry (CV) technique. In addition, CV was used to evaluate the differences in electrochemical characteristics of the copolymer in comparison with the corresponding homopolymers, poly(o-chlorophenol) (PoCP) and poly(o-hydroxyphenol) (PoHP). The variation of peak currents with respect to sweep rates was compared between copolymer and homopolymers, PoCP and PoHP, films. Further support for copolymer characterization was obtained by recording UV-visible, IR spectra and elemental analysis. The mechanism of the electrochemical polymerization has been discussed. The monomer reactivity ratios ($r_1$ and $r_2$) were calculated using Fineman-R$\ddot{o}$ss method and was found to be 0.4 and 1.3 repetitivelly and the copolymer structure is a block structure and more rich in oHP units.

The synthetic route to coumarin systems is well established and one approach of particular interest leads to the intermediate 7-diethylamino-3-formylcoumarin. A combination of the N,N-diethylamino-coumarin donor with a wide range of acceptor groups of varying electron withdrawing strength should permit the synthesis of a series of extended coumarin dyes with absorption maxima range from 500 to 600 nm, or even beyond. In this communication, a novel efficient synthesis of indoles, benzothiazole and benzoxazole based on coumarin chromophores were achieved and the coloristic and fluorophoric properties of these chromophores were studied.

본 연구에서는 전수로 시행된 국가수준 학업성취도 평가의 중학생 과학 성취도를 다문화 탈북 집단별 성취특성, 문항별 집단별 정답률 및 변별도, 내용영역별, 정답률 차이가 큰 문항유형별 특성을 계량적, 질적 방법으로 분석하였다. 연구결과, 다문화 탈북 가정 학생의 과학과 학업성취도는 일반 학생에 비해 매우 낮았으며, 기초학력과 기초미달 학생의 비율이 매우 높았다. 또한 다문화 탈북 가정 학생의 하위집단별로 과학과 학업성취도가 다르게 나타났으며, 특히 중도입국 학생과 탈북 가정 학생의 학업성취도가 가장 낮았다. 일반 학생과의 정답률 차이가 큰 문항을 분석한 결과, 중도입국 학생과 탈북 가정 학생의 경우는 전 영역에서 고르게 취약한 반면, 외국인 가정 학생의 경우는 특정 영역에서 취약함을 보였다. 이로부터 다문화 탈북 가정 학생을 위한 교수 학습 및 교육 지원이 각각 집단의 상황을 고려하여 적합한 방식으로 이루어지도록 교육적 함의를 도출하였다.

이 연구의 목적은 예비 화학교사의 PCK를 신장시키기 위하여 교육실습과 연계된 대학 강좌를 개발하는 것이다. 연구자는 교육실습 연계 대학 강좌의 실러버스와 교수학습 자료를 개발하고, 교육실습을 나갈 화학교육과 예비교사를 대상으로 '화학수업의 실제'란 강좌를 개설하여 개발한 교육과정을 적용하였다. 연구 참여자를 대상으로 반구조화된 면담을 실시한 결과, 예비교사들은 이 수업이 이론과 실제를 연계 지어줌으로써 좋은 과학수업에 대한 안목을 형성할 수 있게 하였으며 실습에 대한 실제적 준비를 할 수 있었고, 반성적 성찰을 가능하게 하여 결과적으로 교수 능력을 신장시킬 수 있었다고 언급하였다. 이 연구를 통해 실습과 연계된 대학 교과목의 실습 전후 교육으로 교육실습 경험을 재구성함으로써 예비교사의 수업 전문성을 신장시킬 수 있음을 확인할 수 있었다.

이 연구에서는 초등 과학 영재 학생들의 과학 영재 수업에 대한 반성의 특징을 분석하였다. 이를 위해, 초등학교 4~6학년 과학 영재 학생 20명이 작성한 총 91개의 반성 일지를 '생산적 반성' 관점에서 분석하였다. 연구 결과, 반성 일지에 포함된 수업 측면의 수를 의미하는 '포함 점수'의 평균은 5점 만점 중에 2.99이었으며, 학생들의 학년과는 통계적으로 유의미한 상관이 없었다. 대부분의 반성 일지에는 '과학 영재 학생(93.4%)' 측면이 포함되어 있었으며, '과학 영재 교수 전략 및 지도(70.3%)', '과학 내용 지식(68.1%)', '과학 영재 교육 과정(57.1%)' 측면이 포함된 경우도 많았다. 그러나 '과학 영재 교육 평가(9.9%)' 측면이 포함된 경우는 매우 적었다. 생산적 반성 수준의 지표가 되는 것으로 반성 일지에 통합된 수업 측면의 수를 의미하는 '통합 점수'의 평균은 5점 만점 중에 2.84이었으며, 학년과 통계적으로 유의미한 상관이 없었다. 반성 일지 중에서 전혀 통합이 없는 경우는 6.6%, 2가지 측면이 통합된 경우는 34.1%, 3가지 측면이 통합된 경우는 39.6%, 4가지 측면이 통합된 경우는 25.3%였으며, 5가지 측면이 모두 통합된 경우는 없었다. 특히, 모든 반성 일지에서 '과학 영재 학생(100.0%)'과 다른 측면들이 통합되어 있었으며, '과학 영재 교수 전략 및 지도(70.3%)', '과학 내용 지식(65.9%)', '과학 영재 교육 과정(53.8%)' 측면과 다른 측면이 통합된 경우도 많았다. 그러나 '과학 영재 교육 평가(9.9%)' 측면과 다른 측면이 통합된 경우는 매우 적었다. 실험 중심 수업과 이론 중심 수업의 '포함 점수' 및 '통합 점수'의 차이는 통계적으로 유의미하지 않았다. 그러나 이론 중심 수업보다 실험 중심 수업에서 포함 유형과 통합 유형이 좀 더 다양해졌고, 더 많은 측면들이 함께 포함되거나 통합되는 경향이 있었다.