Because do placing joint after smallest $1{\sim}3$ day about concrete that is placed beforehand in field, it is difficult that remove laitance happening harden concrete. This laitance happens a problem of bond properties, deterioration in strength. In this research got following conclusion as result that do research about bond properties the way of disposal placing joint. Air Jet is loft interior and exterior. Water Jet appeared that laitance Removal Capacity is superior to dimension within 5%. Deterioration in strength is measured 37% by splitting tensile strength test result by laitance. Deterioration in strength by laitance do more than 30% that removal of laitance is predicted must consist necessarily at concrete horizontality placing joint stroke.

This study investigates the field application, Songdo the # 1st WORLD, on zero-crack construction of the fundamental mass concrete using double bubble sheets and applying low heat mixture. Experimental results of hydration heat analysis showed that crack modulus of concrete incorporating 20% of blast furnace slag cement was 1.0 in 120 hours, representing 50% probability of crack occurrence, thus requiring additional measures. As for a curing method, a specimen insulating two layers of vinyl chloride+double bubble sheets exhibited only $16.5^{\circ}C$ difference between upper and lower sections, and it also showed favorable workability as well as competitive economic side. Therefore it was determined to use it for curing method in this field. For the curing results of practical field, using 2 layers of vinyl chloride+double bubble sheets and applying low heat mixture on the fundamental mass concrete in 3A residential building exhibited less than only $15^{\circ}C$ difference between surface and center section of that in 5 days elapse and less than $20^{\circ}C$ in 9 days. This means that the crack by hydration heat was prevented, and other fields structures also resisted the plastic shrinkage by insulating the vinyl, sinking crack by second temping, even drying shrinkage by the mixture of low unit water. Therefore the crack on the placement has not been found so far, since the construction was started before 6 month.

In recent years, construction site has developed lots of new methods and materials for Time-Cost Trade-off and improving constructability. In the case of underground construction, especially, there are many restrictions and difficulties. Shortening of the construction time in construction of underground, we use top-down method in undergroud wall. A open slab has been designed for the purpose of overcoming a weak point of former top-down method. This study based on open slab on the under ground top-down method, to more improve constructability, to introduce the effect and the performance of top-down method.

This study investigates filed application in Daebul Free Trade Zone of a flowing method using drying shrinkage-reducing superplasticizer(SRS) and an insulating curing method using double bubble sheets. Test showed that fresh concrete satisfied target slump and air content. A structure adding SRS significantly decreased the total bleeding capacity and accelerated the setting time. As for the crack occurrence, the structure applying the flowing method and double bubble sheets simultaneously exhibited the most favorable crack endurance, while conventional concrete showed more than 1mm size of crack in overall, and a structure applying only the flowing method partially presented micro crack. For the area proportion of crack occurrence, the structure using the double bubble sheets indicated 9.8%, while others applying flowing method was 28%, compared with 100% of conventional one. Standard curing specimens had about $3{\sim}6%$ higher compressive strength than that of specimens cured at adjacent field construction. In addition, using SRS improved about $5{\sim}7MPa$, than that of conventional concrete at 91 days elapse.

It often happen water leakage that roof membrane have a poor condition such as direct exposed to rain, ultraviolet lays, temperature change compare with other part of waterproofing. There are difficult to maintain the quality of waterproofing and durability due to use only few waterproofing materials in practical in spite of development and use the various waterproofing material as solution of these poor condition. Therefore, in this thesis, I would like to know the property to apply field and suggest other method to develop for this waterproofing method to adopt various field condition for roof tops, as searching exposed and complex waterproofing technology for roof tops which is reinforced sheet using rising system have a regular pitch, depth, space.

This study investigates field application of flowing concrete in order to improve workability, duality and economic evaluation of concrete. Test results showed that slump of fresh concrete satisfied the target value before and after flowing concrete, and setting time indicated 3 hours difference depending on the mixture proportion of ready-mixed-concrete company. As for the hardened concrete, compressive strength of standard curing specimens, both control and flowing concrete, presented designed value at 28 days elapse. However, the specimens curing at atmosphere decreased the value, due to the lower curing temperature, but also performed the designed value at 91 days. For the evaluation of construction fee by value engineering(V.E) concept, a flowing method declined 4.89% of concrete construction fee, which is 4.9% reduction for materials and 25% reduction for labor expenses, compared with previous construction methods.

The contiguous construction in downtown area requires an appropriate substructure construction method since it results in the insufficient working spaces and frequent public resentment by noise and vibration. In particular, Top-down method usually is applied for downtown construction, and followed by several difficulties in casting the slab concrete for substructure. In this study, we focus on the improvement workability for substructure construction.

Experimental test results of field construction, Cheongju University Educational Liberal Art Building, applying the insulating curing method on slab concrete showed that the quality of concrete in fresh and hardened state satisfied all target values. Temperature history of slab concrete in A and B area secured more than $7.8{\sim}9.2^{\circ}C$ higher than outside atmosphere. After completing certain curing period of time on the surface of the structure, crack occurrence was not found. It is concluded that the preventing vaporization of moisture by the insulating curing method reduces plastic and drying shrinkage as welt as improves durability.

This Study is based on manufacture non-sintering cement(NSC) by adding phosphogysum and waste lime to GBFS as sulfate and alkali activators. This study also investigates the basic physical properties and duality of NSC, and evaluates its reusing possibility as construction materials. Therefore, we design 40MPa and 60MPa for compressive strength using OPC and NSC by binder. And There is a purpose to present fundamental data, applying in field and analyzing quality control of concrete using NSC according to rate of replace between OPC and NSC.

In this study, there is purpose that is on a concrete defect happen from aggregate minute's particle mixing in process that make waste concrete as recyclable cement puts to practical use constructing basic data for design of mix proportion used recyclable cement and solves strength fall problem using micron separator, and does general recyclable cement high quality. As a result of X-ray diffraction(XRD) of rater HR-C than NR-C is aware that it come out the micron-separating to decrease the $SiO_2$-peak below 50%. And a construction field which apply for strength's $24{\sim}28MPa$ HR-C in order to realize NR-C of 44% and 51%. Recycle concrete capacity through improved recycle cement of manufacturing technique by micron-separating's new distribution more better improvement. Therefore, in this study, it need to more various study a recycle cement of high quality for reasonable and utility recycling than disposal concrete.

The Hwangtoh is one of the traditional construction material used in wall, plastering material, and ondol (Korean underfloor heating system) with stone and wood. It is an important greenness material and it has much advantages such as; high storage of heat, auto-purification, antibiotic ability, and emission of far infrared rays. But, it is not developed and not used in modern construction because of its low strength and properties of dry shrinkage crack. According to the recent researches and studies, it is evaluated for natural pozzolanic material like flyash or pozzolan. It's possibility on construction material is high because it's chemical and mineralogical proportion is like as Metakaolin and Kaolinite. In this point of view, this study aims to analyze the physical properties on Hwangtoh mortar through an experiment with various activation condition of Hwangtoh, which is natural pozzolanic material, for the purpose of increase the using possibility in construction material.

Modern residing equipment developed much quantitatively along with economic growth but improvement for agreeable residing space of indoor environment is insufficient situation yet. Also, the latest sick-building syndrome discharging room contaminant such as Formaldehyde, toluene, radon etc. built house or buildings newly human body threaten. Radon of them is real condition that raise origination of lung cancer next to smoke. So, wish to in this research by one of solution way of these problems adsorption performance and specie performance excellent activated carbon to concrete bricks for deconstipating suppository that is room finish fare mix and examine closely after grasp physical, mechanical special quality, hazardous substance and specie performance effect. According to result that estimate environment efficiency evaluation, the $CO_2$ absorption amount displayed decrease effect more than about 90% in activated carbon metathesis rate 40% and radon release amount displayed tendency that decrease about $76{\sim}96%$ in activated carbon metathesis rate 40%.

The objection of this study is to investigate the properties of cement mortar with the kinds and addition of expansive additives. 3 kinds of expansive additives produced in our country and 0, 5, 10, 15, 20% of ratio of addition rate are selected for this experiment. According to experimental results, flow of cement mortar with expansive additives is nearly same with flow of plain mortar and compressive strength, tensile strength, bend strength of cement mortar with expansive additives at 28 days is higher than that of plain mortar.

This study proposes the physical properties of the hardened lightweight cement using the polyethylene tube and to make the fundamental data regarding a new lightweight concrete development. The aerated concrete is displaying various effects such as lightweight, insulation characteristic and it is coming to be widely applied the slab layer of apartment as an insulating material but currently the aerated concrete has many problems. Therefore, demonstrating similar property of former aerated concrete and improving the defects, developing new hardened cement is needed. In this study, we predict adopting possibility of hollow core polyethylene tube, as a material to make cement hardening containing a lot of void. So we changed the mixing ratio, a diameter and length of the polyethylene tube and improved the compressive strength and unit capacity weight of the lightweight cement hardening body. From the test results, we judge that the aerated concrete is a developmental possibility.

Urethane, epoxy, acrylic have common property to adhere on the concrete dried surface in the waterproofing materials at present. In the wet condition, however, the materials such as urethane, epoxy, acrylic need a long hardening time and it become a reason of water leakage as the materials breaking down. it is one of the problem to adhere to the substrate. Therefore, in this thesis, I focused to assure the structural safety and durability and quality for waterproofing and safe of construction cost by cut down the cost of labor and reduce the term of works as searching the application of field condition for hish adhesive spray type of degenerated and rubberized asphalt membrane material.

This study investigates the properties of light weight foamed concrete designed with various incorporating ratios of CKD and adding ratios of PS. Test showed that increase of CKD and PS decreased fluidity of fresh concrete, which need more addition of superplasticizer to secure proper fluidity. As for the sinking depth of specimens, using more CKD or PS decreased the value, due to the improvement of viscosity by micro particles of CKD and reduction of air loss by PS. Those methods are very effective to solve the sinking problem of light weight foamed concrete, which has been highly concerned. For the hardened concrete, compressive strength of specimens exhibited that using around 10% of CKD or 0.02% of PS increased the strength value, but decreased when incorporated or added more amounts of that, due to reduction of the sinking depth, caused by filling effect of the micro particle and improvement of the viscosity.

The introduction of materials and methods of construction which are appropriated to property of green roofs could be a decisive factor in a long-range durability and economical maintenance cost, moreover, it support to variety construction system and organization. In this paper I focused to assure the basic system for waterproofing materials and root barrier apply to green roof as searching the application of field condition. And I suggest proper waterproofing and root barrier as considering the mutual connection and plant growth. and it can be a standard model to adopt to domestic green roof system.

Recently, more highly effective construction materials are needed for the reasonable and economical structure system is required as the construction structures become more multi storied, large-sized and diversified. That is to say, the highly qualified concrete is positively promoted as a part of plan to establish the effective space according to the dead load of structures and diminish of segment profile and to build up the economic structures. However, the high strength concrete has the problems such high brittleness and low ductility. Specially, for the high strength concrete, it has different strength from normal concrete as the internal temperature goes up steadily due to high heat of hydration by the quantities of highly level of cement, so the concrete which is mixed with various miscible materials is used. As the development and study for high strength concrete (more than $100N/mm^2$) is under way actively and the strength of high strength concrete increases, the strength different from the existing high strength concrete of ten than $100N/mm^2$, but the study for this is not adequate and indefinite. In addition, the study and report to apply the strength expression and analysis results of internal structure. Therefore, this study is an experiment about using the miscible materials affects what happens to the longitudinal physical property.

This study investigates engineering properties of concrete using recycled coarse aggregated manufactured by bar-crusher. Test showed that Bar-crusher(S) had more effective results at fresh state than cone-crusher(C) and impact-crusher(I). In case of specimens manufactured by S, increase of spindle velocity, incorporating ratio of recycled aggregate and maximum size of aggregate inclined fluidity. As for the hardened concrete, compressive strength of specimens by C or I exhibited lower value than that of S. In addition, specimens using recycled aggregate manufactured by 400rpm and 500rpm of spindle velocity showed less than 10% reduction rate of strength, which is not significant reducing value. It is found that 500rpm of the spindle velocity had the best strength performance, while 600rpm was the worst. Strength value of specimens decreased as incorporating ratio of recycled aggregate inclined, but the strength value of most specimens exhibited less than 10% of reducing rate, assuming favorable result, only at less than 25% incorporating ratio of recycled aggregate.

This study investigates the temperature history of slab mock-up specimens for hot weather concreting applying various surface insulating methods, in order to improve concrete quality at hot weather condition. Test showed that the use of insulating blanket or a bubble sheet on upper section of slab prevented from abrupt increase of temperature and vaporization of moisture during early curing at hot weather circumstance. In addition, it secured higher strength at early age. Therefore it is concluded that concrete construction insulating with the bubble sheet will reduce the plastic and drying shrinkage as well as improve strength at early age, thus securing concrete duality.

The way to shorten a construction period is considered to an very important technology development element as reducing the formwork removal periods with promoting strength revelation own concrete. This study executed experiment to review usability of early strength revelation chemical admixture which is judged in ways effective with premature removal of form about concrete. Use of early strength revelation AE water reducin admixture is apperaing so that strength revelation by early hydration promotions is excellent. The results of being applied proposed work process are that compressive strength are appeared more than 5MPa within 16 hours so that removal of vertical form was possible. the concrete compressive strength satisfied with a more than 2/3 of specified concrete strength for removal of horizontal form are appeared in 42 hours of 27 MPa proportioning strength, in 36 hours of 30, 35 MPa proportioning strength so that the 6 days cycle time of concrete structural frame work is cut by 2 days as shortening delayed period in works of removing slab forms. So construction cost reductions and a construction period shortening are judged so that it is possible.

This study investigates spalling properties of high performance concrete, 60MPa clan, made with the various types of coarse aggregate and adding ratio of polypropylene(PP) fiber. As experimental parameters, totally sixteen specimens of ${\phi}100{\times}200mm$ in size are prepared: one specimen for control without fiber, ten specimens with different coarse aggregate types, along with 0.05, 0.1, 0.15 percent of PP fiber in each. 1 hour fire test is conducted and then spalling appearance, spalling degree and residual compressive strength are examined. In addition, sit specimens made with two types of coarse aggregate site, along with same adding ratio of fiber are supplementally done, and only spalling properties is examined. Test results showed that control concrete and most specimens containing 0.05% of PP fiber exhibited 4 to 3 level of spalling degree, resulting severe explosive spalling, except for the specimen using basalt aggregate(Bc) showing 2 to 3 level of that. Especially, the Bc specimen containing 0.1% of the fiber exhibited that residual compressive strength value was 32%, which is 10% higher than other specimens using limestone or granite. Spalling resistance performance was also effective as aggregate size increase.

This paper reviews the relevant literatures and investigates spalling mechanism of high strength concrete, in order to clearly inform spalling problem in fire. Firstly, we studies literatures on spalling occurrence and resistance methods. Secondly chemical change of concrete components in elevated temperature was presented. Finally, mechanism of the spalling occurrence and spalling resistance were carried out with fiber content. In addition, our research team introduced spalling mechanism, being different from other points of view, which has been generally accepted. To secure this mechanism theory, we investigate spalling properties of certain specimens fabricated by roller spindle and made with mortar or concrete condition.

This study investigates spalling properties of 60MPa class, high performance concrete, made with the various influential parameters, such as, blaine of cement, mineral admixture and polypropylene(PP) fiber contents. Totally 21 parameters of ${\phi}100{\times}200mm$ in size was fabricated; three specimens for variance in blaine of cement, 4 specimens for combination of mineral admixture type, along with 0.05, 0.1, 0.15% of fiber adding ratio. After that, one hour unloading fire test was conducted, and then spalling appearance and spalling degree of specimens was examined. Test showed that a specimen made with high blaine of cement(H) improved early strength but exhibited similar value to a specimen made with low blaine(L) at the age of 28 days, thus indicating comparable spalling appearance. In conclusion, spalling easily occur in higher strength and smaller particle shape of cement and mineral admixture.

The purpose of this study is to suggest a reference data for the development of high workable and normal strength concrete using Polycarboxylate superplasticizer and granulated blast furnace slag as concrete admixtures. So in this study, it is quantitatively evaluated the workability, compressive strength, the heat of hydration and dry shrinkage of high workable concrete on normal compressive strength($21{\sim}27MPa$) for the practical use in construction field. As a result of this study, it is appeared that the performance of high workable and normal strength concrete is superior than that of ready-mixed concrete of the same strength through the B/P tests in the plants.

This paper is to investigate the chemical composition and physical properties of cements collected at different crushing process line of ordinary portland cement to verify the possibility for producing special purpose cement based on the particle distribution technique. According to test results, six different cement samples with different blaine were gathered. loss on ignition and chemical composition of cements gathered were satisfied with KS L 5201. Cement collected at line 5 had the lowest blaine value while cement at line 4 had the highest blaine value. The coarser the cement particle is, the larger the fluidity of cement is. The compressive strength of cement was highly affected by the blaine value of cement. It is confirmed that the use of cement produced by the process of particle distribution control may be applied for special purpose cement without modification of chemical composition.

This study intends to suggest the effective methods for water leakage prevention around the windows in stone works to up-grade the outdoor public space that has been taken much portion of apartment housing trends. The subjects of the study was selected among the domestic subcontractors of stone works. There are four methods for water leakage prevention around the windows; Firstly, the painting water-proof method after the masonry. Secondly, the urethane water-proof method after galvanizing panels on the gap. Thirdly, the separation method between stone and substructure and the last one is water-proof method that they put some water-proof screen between stone and substructure with the EPDM sheets. According to the analysis of the water-proof effects, constructability and planning, we could approach to conclusion that the most influent items to the water-leakage are the filling material's deformation, the state of oxygenation and deterioration of work skill. Among the water-proof methods in construction the EPDM sheet is most excellent water-proof method to meet the technical conditions. However, we have to apply it to stone works as a water-proof method for the decrease of the leakage defects after standardizing the materials, test and construction skill because there are many work skills according the subcontractors.

Existing Deck Plate for a one of system forms, there is various advantage and application actual results increasing rapidly. But design of deck is depending on engineering data collections or design data on deck manufacture ordinarily. When construct, is responsible for deflection occurrence, And Because confirmation of crack occurrence region is impossible, there is difficulty of repair, reinforcement about crack and water leakage. According to got following conclusion as result that economic performance, preservation administration and repair reinforcement develops easy using steel truss snap tie by wedge pin on coating plywood that is slab Panel Wood System Form method of construction there is Deck Plate's advantage. (1) In stab lower part is exposed disjointing in which a criminal is fastened to be interrogated after construction acceptance and repair, reinforcement of crack is possible (2) Construction cost curtailment effect of about 29.2% than conventional type and about 10% than deck plate (3) Construction period reduction of about 3 day than conventional type and about 0.3 day than deck plate (4) Labor curtailment effect more than about $29{\sim}50%$ from conventional type

Depot have a lagged behind structure in the side of building up the view. With this reason, people have been recognized depot as hatred facility causes to have car noise, air pollution. In the other hand, depot become a underground and complex facility as a higher-value added building, and moreover, it need to understand the environment that depot structure have a specific field condition to apply green roof system. 1) Analysis proper waterproofing material and root barrier apply to depot need root penetrating test method 2) Suggest root barrier and waterproofing material relate to maintain and construction for green roof system 3) Construction condition for depot have crack movement of structure by vehicle vibration and root penetrating force by plant growth

Can examine cause that the construction industry is faced in crisis of skill exhaustion in two sides. One is the tribe of actuality production manpower by entry evasion and graying of young man class specially new manpower to the tribe of skill manpower. Another is qualitative decline of skill manpower. Generally, problem of the systematic knowledge tribe and the picking up tribe about new technology etc, exists because learn skill for shoulder beyond in spot. In cutting phenomenon of skill that is depended on personal relationships availability with skilled worker in hereafter, problem that worker who is old or enter through rain skilled worker does not learn all life skill is detected. These problems institute entry of young man class and necessity of systematic vocational education training specially new human strength strongly. This study does presentation of way to promote construction industry entry of young man class and improvement way of vocational education training system that can do to train these by function manpower by purpose.

The indoor air quality of new apartment buildings, which is known to cause sick housing syndrome, has become a major concern among apartment residents as well as construction companies in Korea. In this study, the effects of environmentally friendly materials and ventilation system are evaluated to compare the strategies applied to improve indoor air quality at the pre-occupancy stage. Six residential units are tested under three conditions : one unit is consisted of environmentally friendly materials and ventilation system, another unit is consisted of environmentally friendly materials and non-ventilation system, and the other four units are consisted of common materials and non-ventilation system.

There has been growing concern regarding IAQ(Indoor Air Quality) recently, and IAQ problems from the air-tightness and use of chemical materials addition to the building materials have become increasingly important factors in the built environment. Ventilation is supposed as the solution of healthy indoor quality, and Korea government requests that all new apartment buildings must have a ventilation system as a matter of duty since January, 2006. The purpose of this study is to investigate the indoor concentration change of VOCs include the Formaldehyde according to many different ventilation supply types. Results showed that the reduction effect of target pollutants by the ventilation system was very slight. The cause of these results was attribute to increase the emission rate of building materials by increasing the ventilation rate.

Of the total defects that have occurred recently in the Korean construction market, over 30% are caused by the construction of defective waterproofing, and the phenomenon of air pockets in the waterproofing layer, which is caused by the concrete vapor pressure, is known to be the primary cause of defective waterproofing. Accordingly, in this study the theory about the relationship between water pressure and temperature as well as the damp-proofing volume of concrete and, then, the change of vapor pressure volume was measured and analyzed by making a test sample after spraying a dampness remover and a waterproofing material to a prepared test body. As a result of measuring the water vapor pressure for the surface temperature of the waterproofing layer with the fluid-applied membrane temperature based on about $10^{\circ}C$, which is the average temperature of Seoul, it was found that first, the fluid-applied membrane elevated up to about $40^{\circ}C$, and the water vapor pressure generated from the fluid-applied membrane was about $0.3kgf/cm^2$ when the surface temperature of the waterproofing layer was raised up to about $80^{\circ}C$. Second, when the fluid-applied membrane temperature of the waterproofing layer was raised from $30^{\circ}C\;to\;35^{\circ}C,\;about\;0.1kgf/cm^2$ of water vapor pressure was generated, and when supplying a thermal source to raise the fluid-applied membrane temperature of the waterproofing layer from $35^{\circ}C\;to\;40^{\circ}C$, approximately $0.05kgf/cm^2$ of water vapor pressure was generated.

It is generally referred that life cycle of concrete construction is depend on whether durability of concrete is obtained or not. Nevertheless, it has not been yet applied that new material and technology to improve durability of concrete such as seaside concrete construction. In this study, chemical agent which is capable of improving durability added to 2 types seaside concrete mixs and evaluated engineering properties such as slump, air content, setting time and compressive strength. Besides shrinkage crack with an restraint condition and chloride ion penetration tests were executed to measure resistance of concrete added chemical agent and then compared non-added. It was appeared that engineering properties and resistant for chlorides was possible to improved. But resistant for shrinkage crack was not noticeable improvement than non-added. Therefore it is necessary that more consideration and following study to improve durability aspect to shrinkage crack and chlorides resistant.

This study aims to uncover the problems that are embedded on the detailed design processes of the major domestic EPC companies. To set the research frame, previous studies were analyzed and interviews were conducted for the industry experts. To draw fundamental factors that may affect on the effectiveness of detailed design processes, questionnaire surveys were conducted to those who involved in detailed design and who have design experiences. Analysis results indicated that there are rooms for improvement on the detailed design processes. This study will be a guidance for future researches that must be followed.