Equal channel angular pressing (ECAP) technique had been adapted to the Mg alloy (AZ31) for achieving effective grain refinement through severe deformation. The average grain size of $2.5{\mu}m$ could be obtained after 4 passes. The stability of the ECAPed structure at elevated temperatures was examined by annealing the ECAPed materials over a wide range of temperature between 473 and 748 K. The average activation energy, Q, for static grain growth of 1, 2 and 3 passes was 33.7 kJ/mole (=0.25QL, activation for lattice diffusion). The abnormally low Q value in the lower temperature range may indicate that grain growth occurs in the unrecrystallized microstructure where non-equilibrium grain boundaries containing a large number of extrinsic dislocations exist. The yield stresses of the ECAPed alloys decreased whereas the elongations increased after the ECAP process. These results should be related to the modification of texture for easier slip on basal plane.

Because of the social needs for energy saving and the rigid environmental regulation, the development of light materials and new economical manufacturing technologies have been actively investigated. Recently, the hydroforming of high strength aluminum tube has attracted great interest due to its good strength-to-weight ratio, which could play an important role in lightweighting of automobile. However, the limited formability of high strength aluminum alloys is considered to hinder the active application of the hydroforming process. In this paper, the hydroformability of aluminum tubes with different heat treatments was investigated as the basic research of the hydroforming process for the high strength aluminum tubes.

The changes of microstructural and mechanical properties were evaluated for the high burn-up fuel claddings after the neutron irradiation of $1.8{\sim}3.1{\times}10^{20}n/cm^2$ (E>1.0 MEV) in HANARO research reactor. After the irradiation, the spot-type dislocations (a-type dislocations) were easily observed in most claddings, and the density of the dislocations was different depending on the grains and was higher at grain boundaries than within grains. As the final annealing temperature increased, the density of spot-type dislocations increased and the line-type dislocations (c-type dislocations) which was perpendicular to the <0002> direction, appeared sporadically in some claddings. However, the types of precipitates in the fuel claddings after the irradiation were not changed from that in unirradiated claddings. The mechanical properties including the hardness, strength and elongation after the irradiation were changed due to the formation of spot-type dislocations. That is, the increase in hardness and strength as well as the decrease in elongation after the irradiation was occurred simultaneously with increasing the final annealing temperature. Owing to the Nb contribution to the formation of spot-type dislocation during the irradiation, the increase in hardness and strength in higher Nb-contained Zr alloys after the irradiation was higher than that in lower Nb-contained Zr alloys.

Compared with the hydroforming technology for steel, the hydroforming technology for aluminum has not been actively investigated. Recently, the hydroforming of high strength aluminum tubes has attracted great interest because of its good strength to weight ratio. In this study, front side member (FSM) is fabricated with the hydroforming of aluminum tube and the mechanical properties and dimensional accuracy of the hydroformed FSM is investigated. For hydroforming process, extruded aluminum tubes with ribs to improve the structural rigidity are used. To ensure the mechanical properties, the aluminum tubes are T6 heat-treated before hydroforming.

In this study, the influence of heat treatment and Ca contents on the electrochemical behavior was investigated. Mg-Ca alloys, i.e., Mg-0.22wt%Ca, Mg-0.56wt%Ca, Mg-1.31wt%Ca are prepared by ingot metallurgy. As-cast Mg-Ca alloys exhibited better electrochemical properties than pure Mg. Especially, Mg-0.22wt%Ca alloy improves its anode efficiency up to 62% and lowers the OCP up to -1.72VSCE. Microstructure and XRD patterns of Mg-Ca alloys show that additive Ca element is mainly solid-solutioned. While, the others show the microstructure and XRD pattern with large $Mg_2Ca$ at grain boundary. To assess the effect of heat treatment on the as-cast Mg-alloy, the specimens were heat treated at $200^{\circ}C$ for 2 hours under $CO_2$ gas atmosphere. Although corrosion properties of Mg-Ca alloys are somewhat deteriorated by heat treatment at $200^{\circ}C$ Mg-0.22wt%Ca alloy with uniformly distributed nano-sized $Mg_2Ca$ phase in ${\alpha}$-Mg matrix show still better corrosion properties than pure Mg specimen.