The static creep behaviour of AlSl 420F stainless steel was investigated over the temperature range of $540{\sim}585^{\circ}C$ and the stress range of $13{\sim}19kg/mm^2$ (127.4~186.2MPa). Constant stress creep tests were carried out in the experiment. Measured stress exponent, n, for the creep deformation of the alloy under the given conditions was found to vary at the range of 9.59, 9.15, 8.78, and 8.53 for the temperature of 540, 555, 570, and $585^{\circ}C$ respectively. The activation energy, Qc, for the creep deformation was 106.42, 102.58,97.81, and 94.58 kcal/mole for the stress of 13, 15, 17, and $19kg/mm^2$, respectively. Lason-Miller parameter, P, for the crept specimens for AlSl 420F stainless steel was measured as $P=T(log\;t_T+21)$. The empirical static creep rate obtained by the regression analysis was as follows. $${\varepsilon}={\exp}[(3.79{\times}10^{-2}{\sigma}+2.722)T-3.0747{\sigma}+28.109]{\times}{\sigma}^{(-2.367{\times}10^{-2}T+22.33)}{\exp}\left[-\frac{(-2.015{\sigma}+132.580){\times}10^3}{RT}\right]$$ The failure plane were observed, intergranular fracture was dominated by r (round) type crack over the experimental range.

Addition of Ca element and nonequilibrium heat treatment which promotes shape modification of eutectic Si and ${\beta}$ intermetallic compound were conducted to improve the mechanical properties of Al-Si-Cu alloy. Modification of eutectic Si and dissolution of needle-shape ${\beta}$ intermetallic compounds were possible by nonequilibrium heat treatment in which specimens were held at $505^{\circ}C$ for 2 hours in Al-Si-Cu alloy with Fe. Owing to the decrease in aspect ratio of eutectic Si by the heat treatment of the alloy with 0.33wt.% Fe, the increase in elongation was prominent to be more than double that in the as-cast specimen. Dissolution of needle-shape ${\beta}$ intermetallic compounds in the alloy with 0.85wt.% Fe led to the improvement of tensile strength as the length of ${\beta}$ compounds decreased to 50%.

The Ti-Al-V-N films have been deposited on various substrates by d.c and r.f reactive magnetron sputtering from a Ti-6Al-4V alloy target in mixed $Ar-N_2$ discharges. The films were investigated by means of XRD, AES, SEM/EDX, microhardness, TG and scratch test. The XRD and SEM results indicated that the films were of single B1 NaCl phase having dense columnar structure with the (111) preferred orientation. The composition of Ti-Al-V-N film was the Ti-7.1Al-4.3V-N(wt%) films. Adhesion and microhardness of Ti-Al-V-N films deposited by r.f magnetron sputtering method were better than those deposited by d.c magnetron sputtering method. The anti-oxidation properties of Ti-Al-V-N films were also superior to that of Ti-N film deposited by the same deposition conditions.

The effects of added elements, such as Co or Nb, on wear properties of high speed steel by powder metaliurgy(PM-HSS) had been eluminated in auther's previous paper. In addition, it is generally known that the wear properties of materials have been influenced by heat-treating conditions as well. Therefore, a study has been done to clarify the effects of heat-treating conditions on wear properties of PM-HSS. The wear tests have been performed under the same conditions as the previous paper using heat-treated PM-HSS(5%Co-1%Nb) with different quenching and tempering temperatures. The result of this paper shows that wear resistance of PM-HSS is improved with relatively high quenching temperature. However, tempering temperature is not sensitive to the wear resistance in the range of high quenching temperature. It may be deduced by the fact that the shear strength of matrix by strengthening mechanisms due to not only the quenching aging but also dispersion-hardening is improved.

There has been a considerable attention on Invar alloys due to its low thermal expansion property. A low thermal expansion property of Invar alloys, lower than $10^{-6}$ near the room temperature, is attractive for electric transmission lines and precision machine tools. However, the expansion property of Invar alloys is limited below about 520K, and mechanical properties are relatively low to apply to electric transmission line. In order to improve mechanical properties in this alloy, Ti alloying element was added to the $Ni_{38}-Mo_2-Cr_1-Fe$ invar alloy. The microstructure Ti added alloy showed finer than that of the unalloyed one. It was found that the (Mo, Ti), Mo carbide formed by Ti addition obstacled grain growth by pinning effect and supplyed recrystallization sites during heat-treatment. Optimum heat-treatment conditions with Ti addition were also discussed in the modified Invar alloy.