Aluminum nitride (AlN) thin films were prepared by using nitrogen ion beam assisted reactive radio frequency (RF) magnetron sputtering on the glass substrates without intentional substrate heating. After deposition, the effect of nitrogen ion beam energy on the structural and optical properties of AlN films were investigated by x-ray diffraction (XRD), atomic force microscope (AFM) and UV-Vis. spectrophotometer, respectively. AlN films deposited with $N^+$ ion irradiation at 100 eV show the higher (002) peak intensity in XRD pattern than other films. It means that $N^+$ ion energy of 100 eV is the favorable condition for low temperature crystallization. AFM images also show that surface average roughness is increased from 1.5 to 9.6 nm with $N^+$ ion energy in this study. In an optical observation, AlN films which deposited by $N^+$ ion beam energy of 100 eV show the higher transmittance than that of the films prepared with the other $N^+$ ion beam conditions.

The influences of Bi addition on morphological modification of $Mg_2Si$ phase and mechanical properties were investigated in Mg-7%Al-0.5%Si casting alloy. It was found that the addition of 0.3%Bi changed the $Mg_2Si$ morphology from coarse Chinese script type to polygonal type, and significantly decreased the size to ~5 ${\mu}m$ or less with the increase of number density. The modification of $Mg_2Si$ phase by the addition of Bi resulted in the improvement of tensile properties of the Mg-Al-Si alloy at RT and $175^{\circ}C$.

Single layer Sn doped $In_2O_3$ (ITO) films and ITO 50 nm / Au 10 nm / ITO 40 nm (IAI) multilayer films were prepared with electron beam assisted magnetron sputtering on glass substrates. The effects of the Au interlayer, post-deposition atmosphere annealing and intense electron irradiation on the methanol gas sensitivity were investigated at room temperature. As deposited ITO films did not show any diffraction peaks in the XRD pattern, while the IAI films showed the diffraction peak for $In_2O_3$ (400). In this study, the gas sensitivity of ITO and IAI films increased proportionally with the methanol vapor concentration and an intense electron beam irradiated IAI film shows the higher sensitivity than the others film. From the XRD pattern, it is supposed that increased crystallization promotes the gas sensitivity. This approach is promising in gaining improvement in the performance of IAI gas sensors used for the detection of methanol vapor at room temperature.

The influence of the cooling condition after solution treatment on the high temperature fatigue resistance of 23Cr-26Ni heat resistant steel was investigated. Two different cooling conditions were applied to the steel after solution treatment at $1200^{\circ}C$ for 3 hours. One specimen was water quenched immediately after the solution treatment. The other one was furnace cooled at a rate of $0.5^{\circ}C/min$ down to $750^{\circ}C$ after the solution treatment. Then, both specimens were aged at $750^{\circ}C$ for 5 hours. Under two different heat treatment conditions, the low cycle fatigue (LCF) test was performed at $600^{\circ}C$ and room temperature (RT). Only cyclic hardening continued from the beginning until fracture at all strain amplitudes during LCF at $600^{\circ}C$. This phenomenon was attributed to the increase in the dislocation density due to cyclic deformation, which resulted in the interaction between the newly created dislocations and precipitates. Cyclic hardening followed by saturation and cyclic softening was observed at RT. Cyclic softening was attributed to the dislocation annihilation rate exceeding the dislocation generation rate. Other probable factor for cyclic softening was some cavities formed around grain boundaries after 20 cycles. WQ and FC have a similar LCF behavior at RT and $600^{\circ}C$ as shown in the cyclic stress response curves.