Microstructural evolution of wrought Inconel 718 superalloy with different heat treatment conditions was studied. Heat treatment was performed via conventional(CHT), modified(MHT), Merrick(MeHT) and modified Merrick (MMeHT) methods. The size of ${\gamma}^{\prime}$ and ${\gamma}^{\prime\prime}$ precipitates which are principal strengthening phases in Inconel 718 superalloy increase in order of CHT, MHT, MeHT. For the case of MMeHT, a coexistence of fine ${\gamma}^{\prime\prime}$ precipitate and very coarse particles due to exess growth of ${\gamma}^{\prime\prime}$, which is called bimodal distribution, was observed. CHT gave the finest grain size. (Ti, Nb)C carbide and needle-like ${\delta}$ phase were formed together at grain boundaries for CHT, and were formed both inside and at boundaries of grains for MHT, MeHT and MMeHT. Morphology of partially serrated grain boundaries was developed in all heat treatment conditions except CHT.

In this study, we tried to describe the quantitative model of TiN film structure which was deposited by PECVD process. The macro-grain growth behavior was studied at the various deposition pressures and times. As a result, It was confirmed that TiN films had the typical Zone 1 structure, and macro-columnar grains were, without reference to the deposition pressure, grown ballistic type by the growth-death competition following the equation, $Y=aX^2$, approximately obtained by regression analysis. Also, the thickness and the crystallization of TiN thin films were increased, the chlorine contents were decreased according to the decreasing of deposition pressure.

This study is aimed to investigate the effect of various thermomechanical treatments($T_6$, $T_8$ and ITMT) on the microstructure and mechanical properties of an Al-Cu-Li-Ag-Mg-Zr alloy (Weldalite 049) which has been known to strong natural aging response, good weldablity and high strength in $T_6$ sand $T_8$ temper. This experiment was performed by means of differential scaning calorimetry, tensile test, optical and transmission electron microscopy. The tensile strength in the peak aged condition shows 620, 650 MPa in $T_6$ and $T_8$(40% cold work), respectively. Also, The tensile strength is increased with cold working in $T_8$ but decreased at 60% cold working. However, the tensile strength of the intermediate thermomechanical treated speciman(ITMT) is lower than that of $T_6$ temper about 20% but the elongation is higher than two times. It might be predicted that the ITMT is effective processing to improve the toughness of this alloy. In $T_6$, $T_8$ and ITMT, the major strengthening phase is $T_1(Al_2CuLi)$ phases. and the fine $T_1$ phase which are homogeneously precipited in matrix was observed much more in $T_8$ than $T_6$ and ITMT.

For the purpose of investigating the effect of austenitizing temperatures on the mechanical properties of 0.23% C-13.6%Cr martensitic stainless steel, tensile properties, hardness, impact value and carbide extraction were examined after changing the austenitizing temperatures and tempering temperatures. The results obtained are summerized as follows. The carbide laminations formed from hot rolling before austenitization could not be eliminated after austenitizing at $950^{\circ}C$. With increasing austenitizing temperature, hardness increased and showed maximum value at $1050^{\circ}C$ and then slightly decreased. With increasing tempering temperature up to $500^{\circ}C$, impact value and elongation appeard to be decreased but hardness showed nearly unchanged at austenitizing temperature of $1150^{\circ}C$ due to the fine $M_7C_3$ carbides precipitation. The abrupt increase in impact value, hardness and elongation above the tempering temperature of $500^{\circ}C$ appeared to change in carbide structure from fine $M_7C_3$ to coarse $M_{23}C_6$.

This study has been performed to investigate into some effects of the power density and traverse speed of laser beam on the optical microstructure, hardness and wear characteristics of medium carbon low alloy steel treated by laser surface hardening technique. The results obtained from the experiment are summarized as follows : (1) Optical micrograph has shown that finer lath martensite is formed and the amount of undissolved complex carbides increases as the traverse speed increases under the condition of a given power density, whereas the coarsening of lath martensite and the reduction of undissolved complex carbides occur with increasing the power density at a given traverse speed. (2) Hardness measurements have revealed that as the traverse speed increases, hardness values of outermost surface layer more of less decrease under low power densities, but are uniformly distributed under high power densities, also showing that they are uniformly distributed at low traverse speeds and more or less decrease at high traverse speeds with increasing the power density. (3) The effective case depth has been found to decrease from 0.26 mm to 0.17 mm with increasing the traverse speed from 1.5 m/min to 3.0 m/min at a given power density of $25.48{\times}10^3w/cm^2$ and to increase from 0.20 mm to 0.36 mm with increasing the power density from $19.11{\times}10^3w/cm^2$ to $38.22{\times}10^3w/cm^2$ at a given traverse speed of 2.0 m/min. (4) Wear test has exhibited that the amount of weight loss of laser surface hardened specimen with respect to sliding distance at a given load increases with increasing traverse speed at a given power density and decreses with increasing power density at a given traverse speed.