The deformation behaviors of full annealed and T6 treated 6061, 7075 aluminum tubes are investigated at various temperature performing uniaxial tensile test. Full annealed Al 6061 and Al7075 tubes, and T6 treated Al7075 tube don't show sharp local necking with an elongation of 50% at $300^{\circ}C$. So it is expected that influenced by elevated tempterature. At $300^{\circ}C$ and strain rate of 0.001/s, many micro-cracks are observed in T6 treated Al 6061 tube, which is believed to be responsible for the decrease of total elongation.

The fatigue properties of Ti-Ni shape memory alloy wires were investigated. In Ni-rich Ti-Ni shape memory alloys, $Ti_3Ni_4$ precipitates formed by aging treatments are believed to vary the shape memory and mechanical properties. In this study, the effect of aging temperature and aging time on shape memory properties and fatigue life were investigated using Ti-50.9 at% Ni alloy wires. The specimens were solution-treated at 1073 K for 3.6 ks followed by aging at 573 K, 673 K and 773 K for periods between 3.6 ks and 3600 ks. It was found that the fatigue life under a constant stress decreased with increasing aging temperature. When the specimens were aged at 573 K for periods between 36 ks and 360 ks, superior shape memory and fatigue properties were obtained. The fatigue life also decreased when the test temperature and strain amplitude increased. It was concluded that the fatigue life exhibited a linear relationship with the critical stress for slip.

In this study, brazing characteristics of the dissimilar Ti and Cu metals using a Zr-base amorphous filler ($Zr_{41.2}Ti_{13.8}Cu_{12.5}Ni_{10.0}Be_{22.5}$ in at.%) have been investigated for various bonding temperatures. In the sample brazed at $790^{\circ}C$ for 10 min., the Ti-rich phases in the joint were observed, while the Cu-rich phases were obtained in the sample brazed at $825^{\circ}C$ for 10 min.. Such a different microstructure and composition in the joints could be explained by the degree of the dissolution reaction. At $790^{\circ}C$, the reaction between the Zr-rich liquid phase and the Ti base metal was actively occurred to form Ti-rich liquid phase in the joint. As the temperature increased to $825^{\circ}C$, however, the reaction between the Ti-rich liquid phase and the Cu base metal was promoted to form the Cu-rich liquid phase in the joint finally. Such a different interface reaction is attributed to the reactivity or solubility between the Zr as a main element in the filler and the Ti and Cu as a base metal element.

Effects of ferrite grain size on static and dynamic deformation behaviors of SCM415 stels were investigated in this study. Dynamic torsional test was conducted using torsional Kolsky bar with the strain rate of $1.6{\times}10^3/s$. Specimens with three different grain size of ferrite, $4.6{\mu}m$, $11{\mu}m$, $35.5{\mu}m$ were used. Dimple fracture mode of the dynamic test specimens showed adiabatic shear bands on the beneath of fracture surface. Increased uniform elongation and decreased non-uniform elongation appeared as grain size of ferrite decreased in dynamic torsional test. However, shear strength was independent on grain size of ferrite.