The effects of Ni and N addition to 304 stainless steel on mechanical properties and microstructure were investigated within temperature ranged from $-196^{\circ}C$ to $25^{\circ}C$. The addition of nickel and nitrogen induced the stability against the formation of provide significantly enhanced ductility at $-196^{\circ}C$ and reduce the Md temperature. Fe-18Cr-10Ni-0.2N alloy showed the ${\gamma}$ phase in deformed structure which it was beneficial to enhance the tensile strength and elongation at $25^{\circ}C$ and $-196^{\circ}C$.

The steady-static creep behaviors of Ti-6Al-4V alloy, using the constant stress creep tester, were investigated over the temperature range of $510{\sim}550^{\circ}C$(0.42~0.44Tm) and the stress range of 200~275 MPa($20.41{\sim}28.06kg/mm^2$). The stress exponents(n) for the static creep deformation of this alloy were 9.85, 9.35, 9.24 and 8.85 at the temperature of 510, 525, 535 and $550^{\circ}C$, respectively. The stress exponent(n) decreased with increasing the temperature and became close to about 5. The apparent activation energies(Q) for the static creep deformation were 254.4, 241.8, 234.4 and 221.9 kJ/mole for the stress of 200, 225, 250 and 275MPa, respectively. The activation energy(Q) decreased with increasing the stress. From the above results, it can be concluded that the static creep deformation for Ti-6Al-4V alloy was controlled by the dislocation climb over the ranges of the experimental conditions. Larson-Miller Parameter(P) for the crept specimens of Ti-6Al-4V alloy under the static creep conditions was obtained as $P=(T+460)({\log}\;t_r+21)$. The failure plane observed by SEM showed up dimple phenomenon at all range.

Austempered Ductile Iron (ADI) castings having various chemical composition and heat treatment conditions were investigated. Especially, this study was investigated the influence of various parameters on austempering temperature and alloying elements. The addition of Mo, Cu, and Ni individually or combined in these alloys also investigated. The alloying elements influence the austempering reaction, the microstructures, mechanical properties and amount of retained austenite. In this study, the mechanical properties (ultimate tensile strength(UTS), hardness, elongation) are analysed to show the relationship between alloying elements, austempering temperatures and amount of retained austenite. The amount of retained austenite was the range of 15 - 40%. In case of the alloy to witch Mo, Cu, and Ni was added, the amount of retained austenite was the largest at a constant austempering temperature.