440A martensitic stainless steels which were modified with reduced carbon content (${\sim}$0.5%) and addition of small amount of nickel, vanadium, tungsten and molybdenum were manufactured. Effects of alloying elements and heat treatment on the pitting corrosion in 3.5% NaCl were investigated through the electrochemical polarization tests. The lowest pitting potential, $E_p$, was obtained when austenitizing temperature was $1250^{\circ}C$ and this is because of the grain coarsening. When austenitized at $1050^{\circ}C$ and tempered at $350{\sim}750^{\circ}C$, the highest $E_p$ was obtained at $350^{\circ}C$, while the lowest at $450^{\circ}C$ and $550^{\circ}C$ regardless of alloying elements added. But $E_p$ was increased a little at the tempering temperature of $450^{\circ}C$ and $550^{\circ}C$ when 0.4 wt.% of tungsten was added. More pitting was observed at $450{\sim}550^{\circ}C$, and pitting was formed at regions where Cr concentration is low or grain boundaries are intersecting and showed irregular shape.

Precipitate formations and grain size variations in various Mg-Sn-Zn alloys have been investigated and their effects on the tensile properties and sheet metal formability were evaluated. MgSn and MgZn precipitates were observed in the alloy sheets, however any clear difference in morphology or size for the precipitates could not be found even though MgSn precipitates tend to be larger than MgZn. The highest formability in terms of conical cup value was found in the Mg-4 wt%Sn-2 wt%Zn where the high tensile elongation and the reduced grain coarsening at elevated temperatures were observed.

Effects of retained austenite contents on ductility of medium carbon spring steels according to steel alloy compositions and heat treatment conditions were studied. Contents of retained austenite varied with steel compositions and heat treatment conditions, and some retained austenite were found to transform to martensite on stress. Reduction of area (RA) increased with contents of retained austenite, then saturated through its maximum, and subsequently decreased. Increase in RA with retained austenite contents could be due to crack blunting effect by retained austenite on stress, however, more contents of martensite transformed from retained austenite in its higher contents could cause decrease in RA.

The effect of high temperature gas nitrding (HTGN) on the surface microstructure in pure Ti was investigated. Two phases of TiN and $Ti_2N$ appeared at the outmost surface, and the wide ${\alpha}$-Ti layer was formed at the next layer. On the other hand, the interior region, where the nitrogen was not permeated, exhibited ${\alpha}$'phase. The outmost surface of TiN and $Ti_2N$ showed the maximum hardness of 1000Hv, while the interior ${\alpha}$'phase was ${\sim}350$ Hv. The permeation depth of nitrogen increased with increasing the gas nitriding temperature and time. The nitrogen concentration of the surface layer seems to be over 12.7% at $1100^{\circ}C$.

In this study, the casting process using forged insert was investigated to characterize the manufacturing process by which good mechanical properties can be obtained when compared with existing casting products. Process analysis for the casting design was performed by using FVM (Finite Volume Method) software. In pouring process, three kinds of candidate gating systems are considered and analyzed respectively. The molten metal behavior in gating system is so important that it affects the solidification behavior of the cast. The results show that as the number of gates is increased, hardness of cast was increased and gaps of cast with forged insert were decreased.

Effect of isochronic aging on transformation behavior of Ti-50.85at%Ni alloy were investigated by differential scanning calorimeter (DSC). The martensitic transformation temperature increases with increasing annealing temperature until reaching a maximum, and then decreases with further increasing annealing temperature. This can be rationalized by interaction between the distribution of $Ti_3Ni_4$ precipitates and Ni content in the matrix. The R-phase transformation temperature increases with increasing annealing temperature until reaching a maximum, and then decreases with a further increase of annealing temperature. This is attributed to the change of Ni content in the matrix caused by precipitation of $Ti_3Ni_4$. The occurrence of the multiple-stage martensitic and R-phase transformation is attributed to precipitation-induced inhomogeneity of the matrix, both in terms of composition and of internal stress fields.