Mun, Hyun Joo;Jeon, Jae-Hyun;Gong, Tae-Kyung;Seo, Ki-Woong;Oh, Jeong Hyun;Kim, Sun-Kyung;Choi, Dong-Hyuk;Son, Dong-Il;Kim, Daeil
121
GZO single layer, Ni buffered GZO(GZO/Ni), Ni intermediated GZO (GZO/Ni/GZO) and Ni capped GZO (Ni/GZO) films were prepared on poly-carbonate (PC) substrates by RF and DC magnetron sputtering without intentional substrate heating and then the influence of the Ni (2 nm thick) thin film on the optical, electrical and structural properties of GZO films were investigated. As deposited GZO single layer films show the optical transmittance of 81.3% in the visible wavelength region and a resistivity of $1.0{\times}10^{-2}{\Omega}cm$, while GZO/Ni/GZO trilayer films show a lower resistivity of $6.4{\times}10^{-4}{\Omega}cm$ and an optical transmittance of 74.5% in this study. Based on the figure of merit, it can be concluded that the intermediated Ni thin film effectively enhances the opto-electrical performance of GZO films for use as transparent conducting oxides in flexible display applications.