The tensile property of A5082 and A6060 aluminium wrought alloys was investigated, in terms of the strain rate sensitivity on alloy conditions by heat treatment and bake hardenability on pre-strain prior to strain ageing. The tensile test was carried out in a range of strain rate of 4.17 × 10^-5 s^-1 ~ 4.17 × 10^-5 s^-1 in room temperature and the nominal range of pre-strain was 3.0 ~ 10.5%. The tensile deformation of A5082 alloys is characterized as typical case of dynamic strain ageing with negative strain rate sensitivity for all conditions, and the tensile strength indicates a similar level regardless of alloy conditions, except only in full annealed condition. The stress-relief annealing on A6060 alloys can induce practical decrease in strength level of over approximately 100 MPa without any ductility loss, compared to as-rolled condition, while a full annealed and aged condition leads remarkable strengthening effect with the decrease of tensile elongation. Additionally, the bake hardenability of A5082 alloy by strain ageing indicates a negative dependence upon the increase of pre-strain, while A6060 alloy exhibits a positive sign even in low level relatively compared with conventional SPCC.

The purpose of this study was to investigate comparatively the microstructural characteristics and hardness of discontinuous precipitates (DPs) in Mg-9%Al alloy, which were formed by continuous cooling (CC) from 678 K to RT and isothermal aging (IA) at 413 K, respectively. In as-cast state, the Mg-9%Al alloy consisted of partially divorced eutectic β(Mg₁₇Al₁₂) particles with a small amount of DPs showing (α+β) lamellar morphology adjacent to the β particles. The DPs formed by CC had interlamellar spacings in a broad range of 0.85~2.12 ㎛ (1.51 ㎛ in average) owing to the various formation temperatures in response to continuous cooling process. Meanwhile, the DPs formed by IA had relatively narrower interlamellar spacings of 0.14~0.29 ㎛ (0.21 ㎛ in average), which is associated with the low and constant formation temperature. Thinner and higher volume fraction of β phase layers were noticeable in the DPs formed by IA. Higher hardness values were obtained in the DPs formed by IA than the DPs formed by CC, which may well be ascribed to the finer lamellar structure and higher β phase content of the DPs formed by IA.

The crystallographic texture plays an important role in both the plastic deformation and the macroscopic anisotropy of magnesium alloys. In previous study for AZ80 magnesium alloy, it was found that the main texture components of the textures vary with the deformation conditions at high temperatures. Also, the basal texture was formed at stress of more than 15-20 MPa and the non-basal texture was formed at stress of less than 15-20 MPa. Therefore, in this study, uniaxial compression deformation of AZ80 magnesium alloy was carried out at high temperature (stress of 15-20 MPa). The uniaxial compression deformation is performed at temperature of 723 K and strain rate 3.0 × 10^-3s^-1, with a strain range of between -0.4 and -1.3. Texture measurement was carried out on the compression planes by the Schulz reflection method using nickel filtered Cu Kα radiation. EBSD measurement was also conducted in order to observe spatial distribution of orientation. As a result of high temperature deformation, the main component of texture and its development vary depending on deformation condition of this study.

In this study, materials characterization of pure copper and copper based carbon nano-tube composite prepared by powder metallurgy method were investigated. Prior to evaluate materials characterization, spark plasma sintering processing variables such as sintering temperature, pressure, thickness and diameter of compacts was optimized to ensure the microstructure and materials property of pure Cu and Cu-CNT composite. In addition, corrosion behavior of Cu-based CNT composite produced by powder sintering method was investigated. It was confirmed from this study that the corroded surfaces of the composite shows less dissolution compared with pure copper in 3.5 wt% NaCl solution. The measured corrosion current density (I_corr) indicates improved corrosion property of Cu based composite containing small additions of CNTs in chloride containing media. Micro-galvanic activity between Cu and CNT was not observed in given sintering condition.