This paper describes the weldability of carbon steel and stainless steel using 5㎾ $CO_2$ laser system with nearly multi-mode beam and a parabolic focusing mirror. In the laser welding of steels, major welding parameters are focal point, travel speed, beam power, shield gas and gap tolerance, etc.. Two kinds of gases(Ar, He) were used as a assist gas and supplied through the external nozzle. It is very important for optimum condition to remove plasma plume which absorbs laser beam and to obtain deep penetration and sound weld bead. Bead-on-plate welding tests were carried out for the experiments. Penetration data were obtained with various welding parameters and the effects of welding parameters were discussed. Butt welding tests were performed with various conditions. Only the optimum laser parameters assured good weld quality As a result of this study, We achieve the fundamental weldabilities using a high power $CO_2$ laser for carbon steel and stainless steel.

This paper introduces the monitoring scheme of laser welding quality using neural network. The developed monitoring scheme detects light signal emitting from plasma formed above the weld pool with optic sensor and DSP-based signal processor, and analyzes to give a guidance about the weld quality. It can automatically detect defects of laser weld and further give an information about what kind of defects it is, specially partial penetration and porosity among the interior defects. Those could be detected only by naked eyes or X-ray after welding, which needs more processes and costs in mass production. The monitoring scheme extracts four feature vectors from signal processing results of optical measuring data. In order to classify pattern for extracted feature vectors and to decide defects, it uses single-layer neural network with perceptron learning. The monitoring result using only the first feature vector shows confidence rate in recognition of 90%($\pm$5) and decides whether normal status or defects status in real time.

This study is about Jig used in wiring when we make Probecard and Large Scale Intergrated Electronic Circuit. The most universal wiring method is molding with Bond. Polymer film is punched down and adhesives is applied after wiring. Due to shrinkage and modification many problems still have happened in the process of molding. To solve these problems, ceramic plate was introduced in the study. Using Laser, an experiment of microhole treatment on ceramic plate was proceeded. Laser energy, assistance gas, and special features by purity degree were analyzed with the 35W low capacity YAG-Laser. In the condition of energy 0.08J, frequency 20Hz and interval time 200$mutextrm{s}$, about 70${\mu}{\textrm}{m}$ microhole was adequate for the Probecard Jig. In the purity experiment of ceramic materials, high purity ceramic met with good result for microhole. But the price is too high. The shape and size of holes machined combustion gas $O_2$ were better than those in $N_2$ and Ar, the inert gas.

This research was conducted as a fundamental study to apply tailored blank welding technique into automotive production process. The materials used in this study were 2.0mm thickness low carbon steel sheets and 1.2mm Zn-coated low carbon steel sheets. To ensure the reproducibility and to consider various factors, experiments were. conducted by applying Taguchi experimental method with 6 factors. Every welding process was repeated 3 times to offset the effect of uncontrolled factors. Elongation and LDH(Limited Dome Height)were measured to evaluate formability of specimens and Optical microscopy, XRD, SEM, and EDS analysis were performed to observe the microstructures and to determine the solidification mode in the weld. The elongation of specimen welded with optimum condition was 83% of base metal, and LDH was 84% of base metal. In case of laser treated specimen where Zn coating was removed, elongation was 85% of base metal, and LDH was 85% of base metal. In fusion zone, phases were consisted of quasi-polygonal ferrite, banitic ferrite, and martensite.

The laser induced forward transfer(LIFT) technique employs a pulsed laser to transfer parts of a thin metal film from an optically transparent target onto an arbitrary substrate in close proximity to the metal film on the target. In this work, a two-step method, the combination of LIFT process, in which a Au film deposited on the $Al_2$O$_3$ substrate by Nd:YAG laser and subsequent Au electroless metal plating on the by LIFT process generated Au seed, was presented. The influence of laser parameters, wavelength, laser power, film thickness and overlap ratio of pulse tracks, on the shapes of deposit and conductor line after electroless plating is experimentally studied. As a results, the threshold power densities for ablation, deposition and metallization were determined and comparison of threshold value between the wave length 1064nm and the second harmonic generated 532nm. In odor to determine a possible application in the electronic industry, a smallest conduct spot size, line width and isolated line space were generated.