The in-process monitoring of $CO_2$ welding of Zn-coated steel plates has been studied and compared with that of conventional thin plates. Relationships between weld defects and plasma emission signals were evaluated in laser lap joint of thick Zn-coated steel. According to the study, weld defects were found to increase with Zn content. As a result, measured plasma emission signals also decreased. In case of plate with $15{\mu}m$-thick Zn-coated layer, defects caused by evaporation of Zn could, therfore, controled by gap of 0.1mm, resulting in a stable emission signals. However, the amplitude of signals fluctuated very widely. Variation of amplitude sould be limited in 3-8V by FFT smoothing.

In this study, laser welding of aluminum AA5182 with AA5356 filler wire was carried out and the formability of the weld joint was evaluated through Erichsen test according to laser power, welding speed and wire feed rate. Fracture was occurred in both directions, perpendicular and parallel to the weld line at 0.75 of Erichsen ratio. Second order Regression model to estimate Erichsen ratio with experimental variables was proposed and the performance of model was evaluated with F-test and average error rate.

In this paper, polyimide (PI) surface was modified by UV Laser with a low laser fluence and investigated changes of surface geometry and chemical characteristics by SEM (scanning electron microscope), X-ray diffraction (XRD), XPS (x-ray photoelectron spectroscopy) and the measurements of contact angle of water. PI surface was peeled off and modified with microstructure fabrications by photochemical ablation over the laser fluence of 50 mJ/cm2. As laser fluence increased, delamination of PI surface was occurred largely and strongly. In chemical characteristics, the O/C and N/C atomic ratios increased and contact angle decreased from $80^{\circ}$ to $40^{\circ}$.

In this study, fundamental experiment was conducted with various strength of UHSS (Ultra High Strength Steel) by $CO_2$ laser. And then, butt and lap joint laser welding with boron alloyed steel and Al-Si coated boron alloy steel have been done by changing laser beam feature, existence of gap and existence of coating layer to know welding characteristics of those materials. As a result, in case of fundamental experiment with various strength steel, hardening was found in the weld metal of all tested materials and softening was found at the heat affected zone of SGAFC 1180. In case of laser butt welding of UHSS, mechanical properties was improved by using small laser beam diameter and Al-Si coating layer caused fracture of weld metal. In case of laser lap welding of UHSS, Al-Si coating layer resulted in formation of intermetallic compound at the fusion boundary where fracture occurred. Al-Si coating layer caused lowering mechanical properties of weld metal.