Ag coating on the textured YBCO was prepared by means of a Ag$_2$O brushed coating method. The contact between Ag coating and textured YBCO was examined by sharp knife cut and by the observation of SEM. The critical current densities of different textured YBCO samples, which included YBCO with and without Ag coating, and YBCO with Ag coating after hot moist text, were compared. The Ag coating does not influence the oxygen absorption of textured YBCO, but Ag coating can protect YBCO well from moisture and $CO_2$

In the YBCO matrix, 10wt.% Y$_2$BaCuO$\_$5/ (211 phase) was added, the final 211 content of YBCO made by MTG process could reach about 20wt.% which was the optimum value for the critical current density. And also 10wt.% Ag was added in the matrix of YBCO, which was nearly about the saturate solubility of silver in textured YBCO. SmBaCuO crystal was grown by the melted-condensed process. A 5${\times}$5${\times}$2㎣ single crystal of SmBaCuO was used to be the seed in the preparation of YBCO. It was proved the orientation of YBCO was the same as the orientation of the SmBaCuO seed. The oxygen absorption of bulk oriented YBCO was studied and the heat treatment of oxygen absorption would be in flowing oxygen, at 400$^{\circ}C$ for about 24 hours. the magnetic hysteresis loops were measured by Vibrating Smaple Magnetometer and the J$\_$c/ was calcuated by means of Bean's model.