In the die casting process, the flow of liquid metal has significant influence on the quality of casting products and die life. For the optimal process design of gear housing of automobile transmission, various analyses were performed in this study by using computer simulation code, MAGMAsoft. The simulation has been focused on the molten metal behaviors during the mold filling and solidification stages for the sound casting products. Also internal defects were predicted by application of air pressure and feeding criteria.

Electroforming is a process that employs technology similar to that used for electroplating but which is used for manufacturing metallic articles, rather than as a means of producing surface coatings. Electroforming provides a cost-effective means of producing alloys and fully dense nanocrystalline metals as foils, sheets and complex shapes. Fe-Ni nanocrystalline alloy foils with composition in the $36\~80wt\%$ Ni range were fabricated by electroforming. The thickness of electroformed foils was in the range of $5\~30{\mu}m$. TEM and XRD analysis was applied for measuring the grain size. Very fine grain size$(\~10nm)$ was obtained in alloy foils. The yield and tensile strength of electroformed Fe-Ni alloy were 2000-2800 MPa and 2500-3300 MPa respectively. The magnetic permeability at high frequency of electroformed Fe-Ni foil was higher than that of thicker foils.

The isothermal forging design of a Ti-6Al-4V wing shape was performed by 3D FE simulation. The design focuses on near-net shape forming by the single stage. The process variables such as the die design, pre-form shape and size, ram speed and forging temperature were investigated. The main design priorities were to minimize forging loads and to distribute strain uniformly in a given forging condition. The FE simulation results for the final process design were compared with the isothermal forging tests. The instability of deformation was evaluated using a processing map based on the dynamic materials model(DMM), including flow stability criteria. Finally, a modified process design for producing a uniform Ti-6Al-4V wing product without forming defects was suggested.

This paper presents a study on defects in pearlite lamella structure of high carbon steel by means of finite-element method(FEM) simulation. High-carbon pearlite steel wire is characterized by its nano-sized microstructure feature of alternation ferrite and cementite. The likely fatigue crack is located on interface of the lamella structure where the maximum amplitude of the longitudinal shear stress and transverse shear stress was calculated during cyclic loading. The FEM is proposed for maximum shear stress from loading of lamella structure, and a method is predicted to analyze the likely fatigue crack generation. It is possible to obtain the important basic data which can be guaranteed in the ductility of high carbon steel wire by using FEM simulation.

It was investigated that curved aluminum products with 'ㄷ' section or with 'h' section could be bended during extrusion by the extru-bending process. In order to make bending at the exit section of die, the flow of billet inside die cavity was controlled by the shape of billet. As results of the analysis of $DEFORM^{™}-3D$, it was known that the bending phenomenon at the die exit can be happened by the asymmetric section of billet. And it was known by the experiment with plasticine or aluminum material that an symmetric product with 'c' channel section and the product with flanged 'h' section could be bended because of asymmetric shape of billet.

The objective of this study is to develop an optimal drawing die for the clad wire drawing process. Cu-clad wire, which has the advantages of the high strength of a steel core and the electro-conductivity, corrosion resistance of a copper layer, is widely being used in the field of the telecommunications, electric-electronic and military technology industries. It is important to obtain uniformly coated rate when producing clad wires. Drawing process of clad wire will be influenced on damage and coated rate of core and sleeve for process variables such as semi-die angle and reduction in area. Therefore, in this study, the finite-element result obtained in this study was analyzed to the effect of the various forming parameters, which included the semi-die angle and reduction in area. The coated rate will be predicted with observation of copper coated rate variation according to total reduction in area and the optimal pass schedule will be set up through proper reduction in area and semi-die angle variation.

Design modification of the stamping die for the upper member of a front end module carrier is carried out in order to improve the surface quality of the final product. The small inferiority induced by wrinkling near the wall of the upper member has been inspected after the draw-forming process. The finite element analysis is pursued with the whole geometry in order to consider the complicated shape. The simulation shows that the excess metal is developed by the irregular contact of the blank the tool and it remains after the final stroke. This paper proposes two guidelines for the modification. One is to add the draw-bead near the critical region in order to increase the draw-in force. The other is to modify the tool shape such as the forming shape at the wall in order to absorb the excess metal before the final stroke. Simulation results show that the proposed guidelines both guarantee the improved surface quality.

In the present study about extru-bending of angle product, the bending of extruded angle products with the $'\Lambda'$ section and 'ㄱ', section can be obtained using two extrusion billets by the hot metal extru-bending machine with the two punches moving in the different velocity. The bending curvature can be controlled by the different velocity of billets through the two-hole container. This paper describes simulations and experiments of extru-bending process that can make bending during extruding by the difference of stem velocities. And they are applied to two kinds of dies, that is, one of them is conical dies with symmetry $'\Lambda'$ section and the other one is conical dies with asymmetry 'ㄱ' section. The results of the forming simulation by $DEFORM^{TM}-3D$ and results of experiments show that the bending phenomenon at the die exit during extrusion can be obtained with two extrusion billet by the two stems moving in the different velocity. And it was known that it is possible to design the structure of conical cavity of extrusion dies and to control the curvature of product through the simulation and experiment of extru-bending process.