• JSTS:Journal of Semiconductor Technology and Science
• /
• v.13 no.6
• /
• pp.668-675
• /
• 2013

We investigate the effect of the ageing time and etching time on the etching rate of SiGe mixed etching solution, namely 1 vp HF (6%), 2 vp $H_2O_2$ (30%) and 3 vp $CH_3COOH$ (99.8%). For this etching solution, we found that the etch rate of SiGe layer is saturated after the ageing time of 72 hours, and the selectivity of $Si_{0.8}Ge_{0.2}$ layer and Si layer is 20:1 at ageing time of 72 hours. The collapse was appeared at the etching time of 9min with etching solution of after saturation ageing time.

• Journal of the Korean Vacuum Society
• /
• v.15 no.4
• /
• pp.387-394
• /
• 2006

In this study, the effect of using a neutral beam formed by low-angle forward reflection of a reactive ion beam on aspect-ratio-dependent etching (ARDE) has been investigated. When a SF6 Inductively Coupled Plasma and $SF_6$ ion beam etching are used to etch poly-Si, ARDE is observed and the etching of poly-Si on $SiO_2$ shows a higher ARDE effect than the etching of poly-Si on Si. However, by using neutral beam etching with neutral beam directionality higher than 70 %, ARDE during poly-Si etching by $SF_6$ can be effectively removed, regardless of the sample conditions. The mechanism for the removal of ARDE via a directional neutral beam has been demonstrated through a computer simulation of different nanoscale features by using the two-dimensional XOOPIC code and the TRIM code.

• Journal of the Korean Electrochemical Society
• /
• v.16 no.1
• /
• pp.1-8
• /
• 2013

This review article summarizes metal-assisted chemical etching (MAC etch or MACE), an anisotropic etching method for Si, and describes principles, main factors, and recent achievements in literature. In 1990, it was discovered that, with metal catalyst on surface and $H_2O_2$/HF as etchant, Si substrate can be etched anisotropically, in even in solution. In contrast to high-cost vacuum-based dry etching methods, MAC etch enables to fabricate a variety of high aspect ratio nanostructures through wet etching process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.2
• /
• pp.117-122
• /
• 2001

In this paper, we report on photoelectrochemical etching process of 6H-SiC semiconductor wafer. The etching was performed in two-step process; anodization of SiC surface to form a deep porous layer and thermal oxidation followed by an HF dip. Etch rate of about 615${\AA}$/min was obtained during the anodization using a dilute HF(1.4wt% in H$_2$O) electrolyte with the etching potential of 3.0V. The etching rate was increased with the bias voltage. It was also found out that the adition of appropriate portion of H$_2$O$_2$ into the HF solution improves the etching rate. The etching process resulted in a higherly anisotropic etching characteristics and showed to have a potential for the fabrication of SiC devices with a novel design.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1250-1253
• /
• 1994

(100), (110) and (111) Si wafers are etched by isotropic etching method, anisotropic etching method using KOH etchant and EPW etchant and combined two-step etching method to compare the results. Isotopic etching method is effective in fabrication of wedge-shaped tips, especially (110) Si. Anisotropic etching method of (100) Si using EPW etchant can fabricate sharp cone-shaped tips and isotropic etching after anisotropic etching of (100) Si can fabricate wedge-shaped tips.

• Journal of the Korean Electrochemical Society
• /
• v.14 no.4
• /
• pp.191-195
• /
• 2011

Wet chemical etching methods were utilized to conduct Si surface texturing, which could enhance photoelectrochemical hydrogen generation rate. Two different etching methods tested, which were anisotropic metal-catalyzed electroless etching and isotropic etching. The Si nano-texture that was fabricated by the anisotropic etching showed ~25% increase in photocurrent for H2 generation. The photocurrent enhancement was attributed to the reduced reflection loss at the nano-textured Si surface, which provided a layer of intermediate density between water and the Si substrate.

• Journal of the Korean Vacuum Society
• /
• v.6 no.S1
• /
• pp.59-65
• /
• 1997

Efficient Si(100) etching by thermal H atoms at low substrate temperatures has been achieved. Gas-phase etching product $SiH_4$(g) upon H atom bombardment resulting from direct abstraction of $SiH_3$(a) by impinging H atoms was detected with a quadrupole mass spectrometer over the substrate temperature range of 105-408 K Facile depletion of all surface silyl ($SiH_3$) groups the dissociative adsorption product of disilane ($Si_2H_6$) at 105K from Si(100)2$\times$1 by D atoms and continuous regeneration and removal of $SiD_3$(a) were all consumed. These results provide direct evidence for efficient silicon surface etching by thermal hydrogen bombardment at cryogenic temperatures as low as 105K We attribute the high etching efficiency to the formation and stability of $SiH_3$(a) on Si(100) at lowered surface temperatures allowing the $SiH_3$(a) abstraction reaction by additional H atom to produce $SiH_4$((g).

• Bulletin of the Korean Chemical Society
• /
• v.35 no.5
• /
• pp.1523-1528
• /
• 2014

Silicon quantum dots (Si QDs) were synthesized by etching silicon nanopowder with aqueous hydrofluoric acid (HF) and nitric acid ($HNO_3$). Then, the hydride-terminated Si QDs (H-Si QDs) were functionalized by 1- octadecene (ODE). By only controlling the etching time, the maximum luminescence peak of octadecylterminated Si QDs (ODE-Si QDs) was tuned from 404 nm to 507 nm. The average optical gap was increased from 2.60 eV (ODE-Si QDs-5 min) for 5 min of etching to 3.20 eV (ODE-Si QDs-15 min) for 15 min of etching, and to 3.40 eV (ODE-Si QDs-30 min) for 30 min of etching. The electron affinities (EA), ionization potentials (IP), and quasi-particle gap (${\varepsilon}^{qp}_{gap}$) of the Si QDs were determined by cyclic voltammetry (CV). The quasi-particle gaps obtained from the CV were in good agreement with the average optical gap values from UV-vis absorption. In the case of the ODE-Si QDs-30 min sample, the difference between the quasi-particle gap and the average optical gap gives the electron-hole Coulombic interaction energy. The additional electronic levels of the ODE-Si QDs-30 min and ODE-Si QDs-15 min samples determined by the CV results are interpreted to have originated from the Si=O bond terminating Si QD.

• Korean Journal of Metals and Materials
• /
• v.49 no.10
• /
• pp.797-804
• /
• 2011

In this study, the mechanisms of the three steps (the polymer deposition step, the polymer etching step and the Si etching step) that constitute the Bosch process were investigated. The effects of radicals and ions on each step were quantitatively analyzed by comparing the simulated aspect ratio dependency of the deposition or etch rate with the experimental results. In the polymer deposition step, fluorocarbon polymer is deposited by chemical reactions of $CF_x$ radicals, of which the reaction probability is 0.13. Although the polymer etching step and the Si etching step were conducted under the same conditions, the etching mechanisms of polymer and Si were found to be quite different. In the polymer etching step, both chemical etching and physical sputter-etching contribute to the polymer etching. Whereas, in the Si etching step, Si is chemically etched by F radicals, of which the reactivity is greatly increased by the bombardment of energetic ions.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.72.2-72.2
• /
• 2010

Nowadays, the crystalline Si Solar cell are expected for economical renewable energy source. The cost of the crystalline Si solar cell are decreasing by improvement of its efficiency and decrease of the cost of the raw Si wafers for Solar cells. This Si wafer based crystalline Si solar cell is the verified technology from several decade of its history. Now, I will introduce one method that can be upgrade the efficiency by using simple and economical method. The name of this method is Rear Side Etching(RSE). The purpose of rear side etching is the elimination of n+ layer of rear side and increase of the flatness. The effects of rear side etching are the improvement of Voc and increase of efficiency by reducement series resistance and forming of uniform BSF. The experimental procedure for rear side etching is very simple. After anti-reflection coating on solar cell wafer, Solar cell wafer is etched by the etching chemical that react with only rear side not front side. This special chemical is no harmful to anti-reflection coating layer. It can only etched rear side of solar cell wafer. We can use etching image by optical microscope, minority carrier life time by WCT 120, SiNx thickness and refractive index by ellipsometer, cell efficiency for the RSE effect measurement. The key point of rear side etching is development of etching process condition that react with only rear side. If we can control this factor, we can achieve increase of solar cell efficiency very economically without new device.