• Advanced Composite Materials
• /
• 제16권4호
• /
• pp.385-394
• /
• 2007

In this study, the effect of molding condition on the tensile properties for plain woven hemp fiber reinforced green composite was examined. The tensile properties of the composite were compared with those of the plain woven jute fiber composite fabricated by the same process. Emulsion type biodegradable resin or polypropylene sheet was used as matrix. The composites were processed by the compression molding where the molding temperature and its heating time were changed from 160 to $190^{\circ}C$ and from 15 to 25 min, respectively. The following results were obtained from the experiment. The tensile property of hemp fiber reinforced polypropylene is improved in comparison with polypropylene bulk. The strength of composite is about 2.6 times that of the resin bulk specimen. Hemp fiber is more effective than jute fiber as reinforcement for green composite from the viewpoint of strength. The molding temperature and time are suitable below $180^{\circ}C$ and 20 min for hemp fiber reinforced green composite. Hemp fiber green composite has a tendency to decrease its tensile strength when fiber content is over 50 wt%.

• Journal of the Korean Wood Science and Technology
• /
• 제41권1호
• /
• pp.64-76
• /
• 2013

이 연구에서는 녹차-목재섬유 복합보드의 강도성능과 기능성을 보강한 건축내장재를 개발하기 위하여, 목재섬유에 녹차와 흑탄, 백탄, 활성탄 등 3종류의 숯을 혼합한 녹차-숯-목재섬유 복합보드를 제작하였고, 구성원료의 종류 및 그 배합비율이 복합보드의 정역학적 성능에 미치는 영향을 조사하였다. 녹차-숯-목재섬유 복합보드의 휨 강도성능은 백탄함유 복합보드에서 평균적으로 가장 높은 값을 나타내었으나, 숯의 종류에 따른 휨 강도성능의 차이는 크지 않았다. 그러나 그 값은 선행연구의 녹차-목재섬유 복합보드보다 현저한 휨 강도성능의 향상을 나타내었고, 녹차와 숯의 배합비율이 증가할수록 휨 강도성능의 감소가 확인되었다. 바인더로 사용된 요소수지의 종류에 따른 차이는 $E_1$급 요소수지를 사용한 복합보드가 $E_0$급 요소수지를 사용한 그것보다 높은 휨 강도성능을 나타냈지만, 양 수지간의 차이는 선행연구의 녹차-목재섬유 복합보드에 비해 현저히 감소하였다. 복합보드의 박리강도는 백탄 $$\geq_-$$ 활성탄 > 흑탄함유 복합보드의 순이었고, 백탄함유 복합보드에서는 목재섬유로만 구성된 대조보드와 거의 비슷한 값을 나타내는 것이 확인되었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 춘계 학술논문 발표대회
• /
• pp.19-20
• /
• 2013

Green Frame is a column-beam system constructed by composite precast column and beam connected by embedded steel of their. From when the precast concrete beam of Green Frame is installed, until the concrete of slab and connection joint is cured, the self load of beam shall be supported by the embedded steel of it. Therefore, the concrete of beam could be separated from the embedded steel if the shear connector of beam of Green Frame is designed by the code on Structural standard. So, this study suggest an equation for the shear connection of composite precast concrete beams of Green Frame. The result of this study will be used as the main equation of the calculation model for shear connectors of composite precast concrete beams.

• 한국건설관리학회논문집
• /
• 제13권3호
• /
• pp.34-42
• /
• 2012

국내 공동주택의 리모델링 수월성 및 이에 따른 장수명화를 위해 그린 프레임 공법이 개발되었다. 그린 프레임 공법은 합성 프리캐스트 콘크리트 부재를 이용한 라멘구조로 벽식 구조와는 달리 양중 및 설치가 골조공사의 주공정으로 작용한다. 따라서 그린 프레임에 의한 적정 골조공사 공기 산정을 위해서는 체계적인 양중계획이 필요하다. 그러나 양중계획은 그린 프레임을 구성하는 요소인 합성 PC 부재(기둥, 보)의 단위 양중공정에 대한 분석이 선행되어야 한다. 따라서 본 연구는 그린 프레임 합성 PC 부재의 양중공정을 분석하는 것을 목적으로 한다. 이를 위해 합성 PC 기둥과 보의 양중절차와 시간을 도출하고, 그 결과를 사례 프로젝트에 적용하여 기준층의 양중 사이클을 분석한다. 본 연구의 결과는 향후 그린 프레임에 의한 골조공사 양중계획 시 핵심자료로 사용된다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 추계 학술논문 발표대회
• /
• pp.92-93
• /
• 2014

Green Frame is a method for Rahmen structure construction composed of composite PC members. The composite PC members of Green Frame which are based on in-situ production can reduce the construction cost and are more likely to secure quality when compared to production in factories. Previous studies developed forms for in-situ production of Green Frame composite PC members and proposed algorithms to arrange them on site. However, it requires not only their arrangement, but also calculation of an accurate production period to produce the required PC members in a limited space and supply them in a timely manner. In particular, it is necessary to clearly define the properties of detailed processes for in-situ production of PC members and to calculate the time required for respective process. To do so, this study is a basic research on calculating the time for in-situ production using a linear scheduling method.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 춘계 학술논문 발표대회
• /
• pp.176-177
• /
• 2013

The composite PC rahmen structure, called Green Frame, allows the main structural members such as PC column and beam to be produced on the site, resulting in a reduction of PC member transportation cost and the margin of PC plant (operation cost and profit), making it more economic than the bearing wall structure. To apply the Green Frame to practice, not only installation but also insitu-production process should be considered. Therefore, this study analyse the influence factors on insitu-production and installation schedule of composite precast concrete members. The results shall be used as basic criteria on the planning of insitu-production and installation of Green Frame.

• Fibers and Polymers
• /
• 제7권4호
• /
• pp.380-388
• /
• 2006

Fully biodegradable and environment-friendly green composite specimens were made using ramie fibers and soy protein concentrate (SPC) resin. SPC was used as continuous phase resin in green composites. The SPC resin was plasticized with glycerin. Precuring and curing processes for the resin were optimized to obtain required mechanical properties. Unidirectional green composites were prepared by combining 65% (on weight basis) ramie fibers and SPC resin. The tensile strength and Young's modulus of these composites were significantly higher compared to those of pure SPC resin. Tensile and flexural properties of the composite in the longitudinal direction were moderate and found to be significantly higher than those of three common wood varieties. In the transverse direction, however, their properties were comparable with those of wood specimens. Scanning electron microscope (SEM) micrographs of the tensile fracture surfaces of the green composite indicated good interfacial bonding between ramie fibers and SPC resin. Theoretical values for tensile strength and Young's modulus, calculated using simple rule of mixture were higher than the experimentally obtained values. The main reasons for this discrepancy are loss of fiber alignment, voids and fiber compression due to resin shrinking during curing.

• Corrosion Science and Technology
• /
• 제8권1호
• /
• pp.27-39
• /
• 2009

Non metallic composite materials, for example, GECM(graphite epoxy composite material) show high specific strength because of low density. These kinds of non metallic composite materials improved the structural effectiveness and operation economics. However, if these materials contacted several metals, corrosion can be arisen since non metallic composite materials have electrical conductivity. This paper dealt with galvanic corrosion between graphite epoxy composite material and several metals. Base on the electrochemical galvanic corrosion test between GECM and metals, corrosion current of carbon steel and aluminium increased with time but corrosion current of stainless steels and titanium decreased and galvanic potential increased. This behavior shows the galvanic corrosion depends upon the presence of passive film. Also, galvanic effect of GECM coupled with ferrous alloys and non-ferrous alloys was lower than that of 100% graphite, which is attributed to lower exposed area of graphite fiber in the GECM than apparent area of the GECM specimen used for the calculation of galvanic current in this work.

• Journal of Electrochemical Science and Technology
• /
• 제2권2호
• /
• pp.116-123
• /
• 2011

Herein, a novel preparation method of highly homogeneous carbon-silicon composite materials was presented. In contrast to conventional solvent evaporation method, a milled silicon-graphite or its oxidized material were directly reacted with petroleum-derived pitch precursor. After thermal reaction under high pressure, pitch-graphite-silicon composite was prepared. Carbon-graphite-silicon composite were prepared by an air-oxidization and following carbonization. From energy dispersive spectroscopy, it was observed that small Si particles were highly embedded within carbon, which was confirmed by disappearance of Si peaks in Raman spectra. Furthermore, X-ray diffraction and Raman spectra revealed that carbon crystallinity decreased when the strongly oxidized silicon-graphite was added, which was probably due to oxygen-induced cross-linking. From the anode application in lithium ion batteries, carbon-graphite-silicon composite anode displayed a high capacity ($565\;mAh\;g^{-1}$), a good initial efficiency (68%) and an good cyclability (88% retention at 50 cycles), which were attributed to the high dispersion of Si particles within cabon. In case of the strongly oxidized silicongraphite addtion, a decrease of reversible capacity was observed due to its low crystallinity.

• Journal of the Korean Wood Science and Technology
• /
• 제39권6호
• /
• pp.538-547
• /
• 2011

이 연구에서는 녹차와 목재섬유를 복합한 친환경 복합보드를 건축내장재로 활용하기 위하여, 목재섬유에 대한 녹차의 배합비율을 달리한 녹차-목재섬유 복합보드를 제작하였고, 복합보드의 동적탄성률에 미치는 녹차의 배합비율 및 바인더로 사용한 접착제의 영향을 조사하였다. 녹차-목재섬유복합보드의 동적탄성률은 녹차를 넣지 않은 대조보드(control boards)의 그것보다 적었고, 녹차배합비율이 증가할수록 커지는 경향을 나타내었다. 또한, 보드제조에 사용된 바인더의 종류에 따라 동적탄성률의 차이가 나타났는데, $E_1$급의 요소수지가 $E_0$급의 요소수지보다 1.06~1.54배의 높은 값을 나타내었으며, 녹차의 배합비율이 커질수록 양자의 차이는 커지는 것이 확인되었다. 한편, 녹차-목재섬유복합보드의 동적탄성률과 휨 강도성능과는 비교적 높은 상관관계가 확인되어 일부 편차가 큰 조건을 제외하고 동적탄성률로부터 정적 휨 강도성능의 예측이 가능할 것으로 확인되었다.