The effect of alloy composition on the glass forming ability (GFA) of the Ca-rich Ca-Mg-Zn alloys has been investigated in $Ca_{65}Mg_{5+x}Zn_{30-x}$ and $Ca_{55+x}Mg_{15}Zn_{30-x}$ (x=0, 5, 10, 15, 20) alloys. In a wide composition range of 15-25% Zn and 10-20% Mg bulk metallic glass (BMG) samples with the diameter larger than 6 mm are fabricated by conventional copper mold casting method in air atmosphere. Among the alloys investigated, the $Ca_{65}Mg_{15}Zn_{20}$ alloy exhibits the highest GFA enabling to form BMG sample with the diameter of at least 15 mm. The crystalline phase formed during solidification of $Ca_{65}Mg_{15}Zn_{20}$ ($D_{max}=15\;mm$) could be identified as a mixture of $Ca_3Zn$ and $CaMg_2$ cause by the redistribution of the constituent elements on long-range scale. The compressive fracture strength and fracture elongation of the $Ca_{65}Mg_{15}Zn_{20}$ BMG are 602 MPa and 2.08% respectively. The ${\sigma}$ parameter which has been recently proposed for evaluating GFA exhibits better correlation with GFA of Ca-Mg-Zn alloys than other parameters suggested so far such as ${\Delta}T_x$, $T_{rg}$, K, ${\gamma}$, and ${\Delta}T^*$ parameters.

Inclusions in Ti investment castings are generally known to have detrimental effects on the performance of the castings. However, actual inclusions are infrequent and hard to be located. As a result, it is extremely difficult to obtain sufficient amount of fatigue test specimens of titanium investment castings having inclusions in the gage section. Thus, in-depth research of the adverse influence of inclusions is also hindered. To address this problem, a new casting methodology of specimens containing hard alpha inclusions was developed in this study. To guarantee successful introduction of an inclusion and casting, a carefully designed mold with 8 legs and a special tool were employed. After solidification, castings were cut, and X-ray radiography determined that the inclusions were successfully incorporated into the castings. The castings were further prepared to obtain multiple test specimens and they were fatigue-tested consecutively. Fractography analysis confirmed that fatigue cracks initiated at the hard alpha inclusion. In a nonlinear regression model, the fatigue life can be modeled as an exponential function with a negative exponent of the cross-sectional area of an inclusion. The fatigue life of Ti specimens containing inclusions is inversely proportional to the cross-sectional area of an inclusion.

Contact material is widely used as electrical parts. Ag-Cd alloy has a good wear resistance and stable contact resistance. But the disadvantages of Ag-Cd alloy are coarse Cd oxides and harmful metal, Cd. To solve the disadvantages of that, Ag-Sn alloy that has stable and fine Sn oxide at high temperature has been developed. In order to optimize Sn amount that affects the formation of the oxide layer on the surface, we worked for the microstructures and properties of Ag-Sn material fabricated by rapid solidification process. The experimental procedure were melting using high frequency induction, melt spinning, and internal oxidation. We have shown that the optimized Sn amount for high hardness is 7.09 wt%Sn. Surface oxide layer forms when Sn amount is over 9.45 wt%. The size of Sn oxide is 20 nm.

Metal-mold reactions between investment mold and TiAl alloys were investigated for the economic net-shape forming of TiAl alloys. The effect of mold preheating temperatures on the metal-mold reaction were investigated using a vacuum induction-melting furnace. In the case of TiAl alloys, there were no ${\alpha}$-case formation reactions. There were neither interstitial nor substitutional ${\alpha}$-case formations as TiAl alloys have both negligible solubility of oxygen and low activity in molten states. The fluidity of TiAl alloys increases with mold preheating temperature since they have a peritectic reaction that appears in the form of envelope, surrounding each particles of the primary constituent. The results of the investment casting of TiAl alloys confirm that the casting route in our study can be an effective approach for the economic net-shape forming of TiAl alloys.