A Numerical technique has been developed for the coupled heat transfer and fluid flow calculation during the casting process. In this method the SMAC technique was coupled with the concept of Volume of Fluid(VOF) to calculate melt free surface and velocity profiles within the melt, and the Energy Marker method coupled with the finite difference method was proposed for the convective and conductive heat transfer analysis in the casting. When comparing numerical calculations with experimental observations, a close correlation was evident. It has been shown that this technique is useful for proper gating and casting design, especially for thin-walled castings.

Ductile cast iron has a good ductility and toughness than those of gray cast iron, because the shape of graphite is spheroidal. Also, it has been reported that, additional strengthening and toughening of the ductile cast iron can be obtainded from the proper combination of matrix structures by the heat treatment and addition of alloying elements. In this study the effect of special heat treatment and addition of alloying elements(Ni, Mo) on the multi-phase(ferrite-bainite-martensite) structures, strength and toughness of ductile cast iron were studied systematically. In water quenching from $770^{\circ}C$, the martensite volume(%) increased, but the ferrite volume(%) decreased with increment of Ni content. In as cast, pearlite volume(%) and hardness increased with increment of Mo and Ni contents. And with the increment of the destabilization austempering holding time, the bainite volume(%) increased but the martensite volume(%) decreased. As destabilization austempering holding time is same, bainite volume(%) decreased, martensite increased with the increment of Ni and Mo contents. The hardness and tensile strength decreased, but impact energy increased with the decrease of Ni and Mo contents, and increment of holding time of destabilization austempering treatment.

SiC particulate reinforced magnesium matrix composites were fabricated by melt stirring method. The effet of several factors on mechanical properties and the efficiency of melt stirring method from the viewpoint of these properties were investigated. The tensile strength increased and the elongation decreased with decrease of the particle size or the increase of the paticulate volume fraction for pure magnesium matrix and Mg-5%Zn alloy matrix composites. A longer stirring time improved the tensile strength of these composites. The tensile strength of Mg-5%Ca alloy matrix composites which shows no uniform paticulate distribution was a little lower than that of matrix alloy. Rapid solidification rate is preferred for the improved tensile strength of these composites. The pure magnesium matrix and Mg-5%Zn alloy matrix composites have tensile strength of about 400MPa. This value agrees with the tensile strength of some magnesium matrix composites fabricated by liquid infiltration method or powder metallurgy method at the same volume fraction of reinforcements of whisker or particle. Therefore, the melt stirring method which has the advantages of simple process is considered to be efficient in fabricating magnesium matrix composites.

AC4C alloy casts in the metallic mold, zircon sand mold, silica sand mold and shell mold with the pouring temperatures of 680, 710 and $740^{\circ}C$ have been investigated. The tensile strength, elongation and hardness of AC4C alloy castings have been influenced by the kind of molds used. The mechanical properties in zircon sand mold castings were greater than those in other sand mold castings, but were inferior to the properties in metallic mold castings. Eutectic Si particle size and DAS were increased in the order of metallic mold, ziron sand mold, silica sand mold and shell mold. Also, they were increased with the increase of pouring temperatures. DAS, eutectic Si particle size and grain size decreased with the increase of mechanical properties as the cooling rate increased. The eutectic Si particle size and DAS of AC4C alloy castings after T6 treatment were decreased in as-cast. The variation of eutectic Si particle size has been effected on the tensile strength, elongation and fractured surface.

A numerical analysis on the microstructural evolutions of microcellular and cellular ${\alpha}-aluminum$ phase in the gas-atomized Al-8wt. pct droplets was represented. The 2-dimensional non-Newtonian heat transfer and the dendritic growth theory in the undercooled melt were combined under the assumptions of a point nucleation on droplet surface and the macroscopically smooth solid-liquid interface enveloping the cell tips. It reproduced the main characteristic features of the reported microstructures quite well. It predicted a considerable volume fraction of segregation-free region in a droplet smaller than $l0{\mu}m$ if an initial undercooling larger than 100K is given. The volume fractions of the microcellular region($g_A$) and the sum of the microcellular and cellular region($g_a$) were predicted as functions of the heat transfer coefficient, h and initial undercooling, ${\triangle}T$. It was shown that $g_A$ and $g_a$, in the typical gas-atomization processes with $h=0.1-1.0W/cm^2K$, are dominated by ${\triangle}T$ and h, respectively, but for h larger than $4.0W/cm^2K$, a fully microcellular structure can be obtained irrespective of the initial undercooling.

The influence of substrate materials on the degree of basal porosity during spray casting process has been investigated. Different conditions of droplet spreading on the substrate were induced by varying the substrate material. Flat sections of cast iron and aluminum have been spray deposited via spray casting process onto an aluminum substrate, a low carbon steel substrate, and an alumina based refractory substrate. Results for cast iron and aluminum sprayed onto the aluminum substrate showed significant improvements in the surface condition and degree of basal porosity with evidence of substrate deformation that round pits ranging from $5{\mu}m$ to $20{\mu}m$ in diameter are distributed on the surface of aluminum substrate. The lowest level of porosity was developed in alumina based refractory material. Several mechanisms for porosity formation were discussed with droplet impact pressure and droplet spreading. Adopting a spray cutting mechanism for removing the periphery of spray cone, porosity level was remarkably decreased.