This study has been focused on the influence of the metallic mold cooling effects on the solidification structures and the mechanical properties for Al-10%Si alloy castings by the variation of pouring temperatures, metallic mold temperatures and Cooling part of metallic mold. The dendrite arm spacing of Al-10%Si alloy was decreased with increasing cooling rate. In case of bottom cooling of metallic mold, DAS was appeared to be $20-22{\mu}m$ and in the middle cooling, it was increased to $36-40{\mu}m$. The DAS decreased proportionally $with(cooling\;rate)^{-3/2}$ at pouring temperatures $680^{\circ}C$ and $(cooling\;rate)^{-1/2}$ at pouring temperature $760^{\circ}C$, but it was proportionally increased to $(local\;solidification\;time)^{1/2-1/3}$ at pouring temperature $680^{\circ}C$ and $760^{\circ}C$. The maximum tensile strength of Al-10%Si alloy casting was obtained in case of bottom cooling of mold at pouring temperature $680^{\circ}C$ and metallic mold temperature $320^{\circ}C$.

Mechanical and chemical properties of the 17-4PH have been investigated after recycled melting. As the result, it has been ascertained that the change of Ni, Cu, Nb, C amount affects the mechanical and chemical properties. It is important to minimize contamination of impurities and to control the amount of Ni, Cu, Nb, C.

It has been known that the grain refinement of Cu base alloys greatly improved mechanical properties, castability, workability and hot shortness resistance etc. In this study CuZr50, CuP7, CuFe7, CuMg10 binary alloys were added as grain refiners in CuZn36 alloy. The alloys melted in vacuum and controlled in mixed gas conditions and casted at $1050^{\circ}C$. Zr-P-X compound has significantly grain refined but oxygen has been found detrimental to grain refinement. In the case of Zr /B ratio below 4, B acted as grain growth element in this alloy.

In this study, the effect of Mo addition on the microstructure and mechanical properties of ductile cast iron have been investigated. The amounts of Mo and the thickness of specimen have been varied from 0 to 4.79wt% and 13mm, 10mm and 6mm, respectively. As the casting thickness decreases, the average size of spheroidal graphite is decreased and the hardness increases. By increasing the Mo content, the tensile strength of ferrite and pearlite matrix increases and shows maximum which is about $30{\sim}40%$ higher than ordinary ductile cast iron. After the maximum, adding more Mo results in gradual transformation of ferrite and pearlite to bainite and thus tensile strength decreases again. The elongation decreases continueously with Mo content. The addition of Mo about $0.5{\sim}1.0wt%$ improves the wear resistance and tensile strength of thin ductile cast iron.

In this study, it was examined the relationship between the microstructure, fatigue properties, mechanical properties and retained austenite volume of Mo-Ni ADI corresponding to various austempering temperatures. When the austempering temperature is increased to $370^{\circ}C$, acicular bainite structure was found to be transformed to feathery bainite structure. But at the austempering temperature of $420^{\circ}C$, the dissolved bainite lath was showned. Up to the austempering temperature of $370^{\circ}C$, the volume of retained austenite was increased. However at the austempering temperature of $420^{\circ}C$ a large amount of retained austenite was decreased. In this study, the retained austenite volume was determined by XRD(X-ray diffraction). It was observed that the optimum fatigue properties can be obtained at the condition of austempering temperature $370^{\circ}C$. Under the such conditions, fatigue limit determined as the value of 290 MPa, tensile strength 877MPa elongation 6%, hardness 285(BHN), impact values(CVN) 9.2J and retained austenite volume 30.3%, respectively.