• Journal of the Korean Wood Science and Technology
• /
• v.38 no.2
• /
• pp.117-123
• /
• 2010

The objective of this research was executed to investigate the effect of molar ratio of formaldehyde to urea and melamine (F/(U+M)) of urea-melamine-formaldehyde (UMF) resin on bonding high and low moisture content veneers. For that purpose, UMF resin types with 5 different F/(U+M) molar ratios (1.45, 1.65, 1.85, 2.05, and 2.25) synthesized were used in present study. First, their curing behavior was evaluated by differential scanning calorimetry. Second, their adhesion performance in bonding high and low moisture content veneers was evaluated by probe tack and dry and wet shear strength tests. Curing temperature and reaction enthalpy decreased with the increase of F/(U+M) molar ratio. And the dry and wet shear strengthsof plywood manufactured from low moisture content veneers were higher than thoseof plywood manufactured from high moisture content veneers. Also, the maximum initial tack force on the low moisture content veneer was higher than that on the high moisture content veneer.

• Journal of the Korean Wood Science and Technology
• /
• v.33 no.2 s.130
• /
• pp.24-28
• /
• 2005

Monte Carlo simulation was performed on theoretical models of plywood warp for southern yellow pine plywood originating from the United States. The objective of the investigation was to determine which plywood layers was more warp sensitive to veneers that were manufactured to an undesired thickness. This study found that for a balanced panel (a panel of equal target thickness for each of five layers) manufactured veneers of undesired thickness would experience minimal warp. The veneers of undesired thickness placed in the center of the plywood panel also provided a minimum change of plywood warp properties. The panel warp was very sensitive to surface veneers constructed with undesired thickness. Conversely, this study confirms that monitoring of veneer thickness and proper allocations within the plywood lay-up were critical.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.4
• /
• pp.22-28
• /
• 1997

This research was carried out to obtain the fundamental data for the development of the technology and practical use of far-infrared radiation(IR) drying of quarter-sliced decorative veneers of walnut and red oak. The average drying rates of IR drying were about one and half to four times those of kiln drying and this tendency was prominent in thin veneer. The end wavinesses of the IR-dried veneers were smaller than those of kiln-dried veneers. These were largely recovered by the cold treatments after drying. The consumed electric power for IR drying was about one-fifth to two-fifthes compared to that for kiln drying.

• Journal of the Korea Furniture Society
• /
• v.26 no.3
• /
• pp.286-290
• /
• 2015

The wood veneers were clearly rainbow-colored with natural dyes. As shown through Korean-style jacket with stripes of multi-colors beyond traditional obang colors (red, blue, yellow, black and white colors), eco-friendly coloring methods representing Korean colors familiar from old times could be used nobly by coloring natural wood veneer being raw material of wood products. In terms of industrialization, the study to manifest korean color, substituting chemical stains such as dye and pigment, would be necessary. In order to realize this purpose, the study about economical dyeing materials and characteristics, that is, mordant, dyeing and drying techniques showing environment-friendly coloring and high coloration level ought to be followed. In addition to this, investigating discoloration transition by fading test for interior and exterior uses would have to be carried out.

• Journal of the Korean Wood Science and Technology
• /
• v.26 no.1
• /
• pp.87-96
• /
• 1998

The bending performances were evaluated at the radiata pine plywood through veneer compositions encompassing veneer quality, ply-numbers and overlays of the high density- or medium density-phenol resin impregnated sheets (hereafter abbreviated as resin sheets) on the raw plywood. In addition, a prediction on the bending MOE of veneers and plywoods was carried out by the nondestructive testing with stresswave timer. The summarized results were as follows: I. Bending strength and bending MOE of resin sheets-overlaid plywoods in parallel surface grain direction through 5 and 7ply were increased by 13 to 45% and 17 to 34%, respectively. Resin sheets-overlay occurred an increasing effect of the strength efficiency i.e. strength perpendicular-to-grain direction versus that parallel-to-grain direction, showing the phenomenon that the plywood strength becomes greater at the perpendicular-to-grain direction of 7ply than at that of 5ply. Displacement at bending failure had a greater trend at 7ply than at 5ply, and was decreased by resin sheets-overlay. 2. After the nondestructive bending MOEs were measured for individual veneers, these veneers were rearranged in plywood-manufacture. In these plywoods, including resin sheets-overlay, the actual MOE was predictable with feasibility of $R^2$=0.53, and also the nondestructively-evaluated MOE was lower by 20% in raw plywood, and higher 20% in LVL than actual bending MOEs.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.1
• /
• pp.11-16
• /
• 2010

Unlike other composites boards such as fiberboard and particleboard, plywood is manufactured with sheets of veneers. When the plywood manufactured, the adhesive is spreaded through gluelines on each surface of veneers. For that reason, formaldehyde emission of plywood can be considered as different way. Therefore, this research was conducted to understand the formaldehyde emission pattern of plywood. To measure formaldehyde emission, four different specimen preparing methods were used. The test specimen taken by a total surface area, a given number and a total side area showed inconsistent results. On the other hand, the result of formaldehyde emission showed consistency when considered only the length of adhesive layers.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.6
• /
• pp.907-916
• /
• 2020

This research was conducted to investigate the linear expansion and resistance properties of a composite board (com-ply). This board was made of medium-density fiberboard (MDF) laminated using avocado (Persea americana), mahogany (Swietenia mahogani), and pine (Pinus merkusii) veneers. These three types of veneers were laminated on both surfaces of the MDF using adhesives, namely, epoxy and isocyanate. Glue (250 g·m^-2) was spread on the surface, followed by cold press for 3 h with an applied pressure of 15 kg·cm^-2. The research result revealed that com-ply exhibited an increased dimensional stability compared with MDF, indicated by reduction in water absorption, thickness swelling, and linear expansion. The com-ply made of the pine veneer and isocyanate adhesive exhibited high density, water absorption, thickness swelling, and screw withdrawal load. The com-ply that exhibited the strongest resistance to drywood termite attacks was the one made of the mahogany veneer and isocyanate adhesive. Moreover, the com-ply that exhibited the biggest weight loss (3.6 %) was made of the pine veneer and epoxy adhesive. The results of this research may facilitate in manufacturing com-ply using the selected veneer and adhesive without the application of hot press.

• Journal of the Korean Wood Science and Technology
• /
• v.33 no.4 s.132
• /
• pp.23-29
• /
• 2005

The fancy veneer flooring board is high value-added wooden material. The classification of the flooring boards by the observation with the naked eye causes color difference among fancy veneers. It turned out that this inaccuracy of color difference among fancy veneers increased in case of the identification by metamerism or the flooring construction. Therefore, this study was performed to classify fancy veneers produced from 3 species such as Tilia sp., Betula sp., and Acer sp. which were identified with the naked eye by Light and Dark grade, by using CIELAB. In addition, each specie's threshold on CIERGB was investigated and a range of hue, saturation and intensity by an application of HSI color model were studied. Intensity of the HIS color model could be the best value to be used when color, saturation and intensity of the HSI color model were used for the classification of the flooring board's color. In addition, it seemed that color range of all three criteria lied between $45^{\circ}$ and $55^{\circ}$. In the case of identification by threshold of RGB element, considering only specific color element value is unlikely to lead to accurate classification of fancy veneers of flooring board.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.4
• /
• pp.344-350
• /
• 2011

In this study, LVLs of radiata pine were fabricated with non-preservative treated veneers, CuAz treated veneers, and ACQ treated veneers, using aqueous vinyl urethane adhesive and phenol modified resorcinol resin adhesive. Then density gradient, bonding strength, bending properties and decay resistance of LVLs were evaluated. As results, the cone-shaped and higher density gradient pattern was found in layer close to glueline. After cyclic water boiled test, the LVL bonded with aqueous vinyl urethane resin adhesive was delaminated in all layers or partly delaminated including check, chasm in glueline layer. In the case of LVL bonded with phenol modified resorcinol resin adhesive, despite slight cupping due to great glueline stress and vertical check between glueline layers, it was observed that the bonding strength to delamination was higher, owing to most absence of delamination through overall glueline. On the other hand, in the decay test, mass loss by brown rot fungi was greater than white rot fungi in LVL bonded with aqueous vinyl urethane resin adhesive. However, in LVL bonded with phenol modified resorcinol resin adhesive, the mass loss by brown rot fungi was slight and non-preservative treated LVL was low. The mass loss of preservative-treated LVL was 0 (zero), showing the high decay resistance effect.

• Journal of the Korean Wood Science and Technology
• /
• v.10 no.3
• /
• pp.152-164
• /
• 1982

1. In order to make the improvement of plywood quality, this study has been made. The pretreatments applied to the veneers are as follows. a) The soaking treatment of the veneer in 30 percent methanol solution for 24 hours was applied to remove some resinous materials which may cause many stain discolouring on the face of finished plywood. b) The preservative treatment of the veneer in 2 percent malenit solution for 2 to 3 minutes was adopted to make resistance against decay and insect damages. c) The fire retardant treatment of the veneer in 40 percent ammonium phosphate solution for 2 hours was applied to give retardation effect against fire burning. 2. The results summarized in this study are as follows. a) One percent resinous materials was extracted, after the soaking of the veneers in 30 percent diluted methanol. b) No marks of the dirty stains of resinous materials on the face of the treated plywood was shown, although many quite dirty stains on the face of untreated plywood have contrary seen. c) However, the strip shear test strength of the treated plywood was not decreased. It means that there is no difference in the strength between the treated plywood and the untreated plywood. The strength values were 25.08 kg/$cm^2$ and 24.98 kg/$cm^2$, respectively. d) The strip shear test strength of plywood made of the treated veneers in 2 percent malenit solution was not decreased. e) The slight decrease of the strip shear test strength of the treated plywood made of the treated veneer in 40 percent ammonuim phosphate solution was shown. However, the remarkable difference of the fire retardation activities between the treated specimens and the untreated specimens has seen as in Table 10, that is, the fire proofed specimens had taken about 28 seconds to start to burn, while the untreated specimens had taken 15 seconds to reach to burning. This means that the fire retardation effect of the fire proofed plywood was greater than that of the unproofed plywood.