• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1993.05a
• /
• pp.96-99
• /
• 1993

Electrical properties of the Thin Film Transistor(TFT) electrode metal films were investigated through the Test Elements Group(TEG) experiment. The main purpose of this investigation was to characterize the electrical resistance properties of patterned metal films with respect to the variations of film thickness and TEG metal line width. Aluminum(Al), Tantalum(Ta) and Chromium(Cr) that are currently used as TFT electrode films were selected as the probed metal films. To date, no work in the electrical characterizations of patterned electrodes of a-Si TFT was accomplished. Bulk resistance$(R_b)$, sheet resistance$(R_s)$, and resistivities($\rho$) of TEG patterned metal lines were obtained. Electrical continuity test of metal film lines was also performed in order to investigate the stability of metallization process. Almost uniform-linear variations of the electrical properties with respect to the metal line displacements was also observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.160-160
• /
• 2010

In this work, we investigate ohmic contacts to p-type GaN using a Pt/Cu/Au metallization scheme in order to achieve low resistance and thermally stable ohmic contact on p-GaN. An ohmic contact formed by a metal electrode deposited on a highly doped InGaN/GaN superlattice sturucture on p-GaN layer. The specific contact resistance is $1.56{\times}10^{-6}{\Omega}cm^2$ for the as-deposited sample, $1.35{\times}10^{-4}{\Omega}cm^2$ for the sample annealed at $250^{\circ}C$ and $6.88{\times}10^{-3}{\Omega}cm^2$ for the sample annealed at $300^{\circ}C$.

• ETRI Journal
• /
• v.24 no.5
• /
• pp.349-359
• /
• 2002

With Ni/Au and Pd/Au metal schemes and low temperature processing, we formed low resistance stable Ohmic contacts to p-type GaN. Our investigation was preceded by conventional cleaning, followed by treatment in boiling $HNO_3$:HCl (1:3). Metallization was by thermally evaporating 30 nm Ni/15 nm Au or 25 nm Pd/15 nm Au. After heat treatment in $O_2$ + $N_2$ at various temperatures, the contacts were subsequently cooled in liquid nitrogen. Cryogenic cooling following heat treatment at $600^{\circ}C$ decreased the specific contact resistance from $9.84{\times}10^{-4}$ ${\Omega}cm^2$ to $2.65{\times}10^{-4}$ ${\Omega}cm^2$ for the Ni/Au contacts, while this increased it from $1.80{\times}10^{-4}$ ${\Omega}cm^2$ to $3.34{\times}10^{-4}$ ${\Omega}cm^2$ for the Pd/Au contacts. The Ni/Au contacts showed slightly higher specific contact resistance than the Pd/Au contacts, although they were more stable than the Pd contacts. X-ray photoelectron spectroscopy depth profiling showed the Ni contacts to be NiO followed by Au at the interface for the Ni/Au contacts, whereas the Pd/Au contacts exhibited a Pd:Au solid solution. The contacts quenched in liquid nitrogen following sintering were much more uniform under atomic force microscopy examination and gave a 3 times lower contact resistance with the Ni/Au design. Current-voltage-temperature analysis revealed that conduction was predominantly by thermionic field emission.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.2
• /
• pp.94-103
• /
• 2007

The transition of interconnection metal from aluminum alloy to copper has been introduced to meet the requirements of high speed, ultra-large scale integration, and high reliability of the semiconductor device. Since copper, which has low electrical resistivity and high resistance to degradation, has different electrical and material characteristics compared to aluminum alloy, new related materials and processes are needed to successfully fabricate the copper interconnection. In this review, some important factors of multilevel copper damascene process have been surveyed such as diffusion barrier, seed layer, organic additives for bottom-up electro/electroless deposition, chemical mechanical polishing, and capping layer to introduce the related issues and recent research trends on them.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.13 no.6
• /
• pp.581-588
• /
• 2013

This paper presents a study of the process temperature dependence of $Al_2O_3$ film grown by thermal atomic layer deposition (ALD) as a passivation layer in the crystalline Si (c-Si) solar cells. The deposition rate of $Al_2O_3$ film maintained almost the same until $250^{\circ}C$, but decreased from $300^{\circ}C$. $Al_2O_3$ film deposited at $250^{\circ}C$ was found to have the highest negative fixed oxide charge density ($Q_f$) due to its O-rich condition and low hydroxyl group (-OH) density. After post-metallization annealing (PMA), $Al_2O_3$ film deposited at $250^{\circ}C$ had the lowest slow and fast interface trap density. Actually, $Al_2O_3$ film deposited at $250^{\circ}C$ showed the best passivation effects, that is, the highest excess carrier lifetime (${\tau}_{PCD}$) and lowest surface recombination velocity ($S_{eff}$) than other conditions. Therefore, $Al_2O_3$ film deposited at $250^{\circ}C$ exhibited excellent chemical and field-effect passivation properties for p-type c-Si solar cells.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.1-7
• /
• 2008

We studied a growth behavior of Intermetallic compounds(IMCs) during solder bumping with two reflow methods. Ti(50 nm), Cu($1{\mu}m$), Au(50 nm) and Ti(50 nm) thin films were deposited on $SiO_2$/Si wafer using the DC magnetron sputtering system as the under bump metallization(UBM). And the $5{\mu}m$ thick Cu bumps and $20{\mu}m$ thick Sn bumps were fabricated on UBM by electroplating. Sn bumps were reflowed in RTA(Rapid Thermal Annealing) system and convection reflow oven. When RTA system was used, reflow was possible without using flux and IMC thickness formed in the solder interface was thinner than that of a convectional method.

• The Journal of The Korea Institute of Intelligent Transport Systems
• /
• v.4 no.2 s.7
• /
• pp.81-87
• /
• 2005

In this paper, a VCDRO(Voltage Control Dielectirc Resonator Oscillator) for signal source of doppler radar system is designed and fabricated. The proposed VCDRO is made with new tuning mechanism using CPW line. The coplanar waveguide of $\lambda_{g}$/2 in length with varactor diode is placed on the metallization side under the dielectric resonator and coupled to it. Tuning varactor diode is mounted at one end of the CPW. The proposed circuit tuned by a CPW allows one more varactor diode to be mounted on the optimized CPW, where a greater sensitivity of frequency tuning is needed. With varying the biasing voltage for the varactor diode from 0 V to 15 V, output frequency tuning of 12 MHz is obtained. The PLDRO exhibits output power of 16.5 dBm with phase noise in the phase locked state characteristic of -115 dBc/Hz at 100 Hz, -105 dBc/Hz at the 10 kHz, and -102 dBc/Hz at 1 Hz offset from 10.525 GHz , respectively.

• Korean Journal of Materials Research
• /
• v.8 no.11
• /
• pp.977-981
• /
• 1998

Controlling the wafer temperatures from 200 to$500^{\circ}C$, low resistive tungsten thin films used for VLSI metallization are deposited by PECVD method. Resistivities of plasma deposited tungsten thin films are very sensitive to the $H_2/WF_6 $ partial pressure ratios. Residual stress behaviors of the films as a function of plasma power density were also studied. At the power density under the $0.7W/\textrm{cm}^2$, residual stress of W film is about $2.4\times10^9dyne/\textrm{cm}^2$. When the power density is. however, increased from 1.8 to $2.7W/\textrm{cm}^2$, residual stress is suddenly increased from $8.1\times10^9$ to $1.24\times10^{10}dyne/\textrm{cm}^2$ ue to the ion or radical bombardment at high power density.

• Current Photovoltaic Research
• /
• v.4 no.4
• /
• pp.145-149
• /
• 2016

Characteristic of aluminum-silicon alloy paste which is applied on the rear side of PERC cell was investigated. The paste was made by aluminum-silicon alloy with eutectic composition to avoid the formation of void which is responsible for the degradation of the open-circuit voltage. Also, the glass frit component of the paste was changed to improve the adhesion of aluminum-silicon paste. We observed the formation of void and local back surface field between aluminum electrode and silicon base by SEM. The light IV, quantum efficiency and reflectance of the solar cells were characterized and compared for each paste.

• Journal of the Korean Vacuum Society
• /
• v.12 no.2
• /
• pp.136-143
• /
• 2003

In this paper, high purity RF sputter-type ion source for non-mass separated ion beam deposition was evaluated. The fundamental characteristics of the ion source which is composed of an RF Cu coil and a high purity Cu target (99.9999 %) was studied, and the practical application of Cu thin films for ULSI metallization was discussed. The relationship between the DC target current and the DC target voltage at various RF power and Ar gas pressures was measured, and then preparation conditions for Cu thin films was described. As a result, it was found that the deposition conditions of the target voltage, the target current and the Ar pressure were optimized at -300 V, 240 W and 9 Pa, respectively. The resistivity of Cu films deposited at a bias voltage of -50 V showed a minimum value of 1.8 $\pm$ 0.1 $mu\Omega$cm, which is close to that of Cu bulk (1.67 $mu\Omega$cm).