• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.6
• /
• pp.462-465
• /
• 2009

Schottky barrier thin film transistors (SB-TFT) on polycrystalline silicon(poly-Si) are fabricated by platinum silicided source/drain for p-type SB-TFT. High quality poly-Si film were obtained by crystallizing the amorphous Si film with excimer laser annealing (ELA) or solid phase crystallization (SPC) method, The fabricated poly-Si SB-TFTs showed low leakage current level and a large on/off current ratio larger than 10), Significant improvement of electrical characteristics were obtained by the additional forming gas annealing in 2% $H_2/N_2$ ambient, which is attributed to the termination of dangling bond at the poly-Si grain boundaries as well as the reduction of interface trap states at gate oxide/poly-Si channel.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.10
• /
• pp.918-923
• /
• 1998

Poly-silicon thin film transistors were fabricated on quartz substrates by high temperature processes. Electrical characteristics were measured and compared for 3 transistor structures of Standard Inverted Gate(SIG), Lightly Doped Drain(LDD), and Dual Gate(DG). Leakage currents of DG and LDD TFT's were smaller that od SIG transistor, while ON-current of LDD transistor is much smaller than that of SIG and DG transistors. Temperature dependence of the leakage currents showed that SIG and DG TFT's had thermal generation current at small drian bias and Frenkel-Poole emission current at hight gate and drain biases, respectively. In case of LDD transistor, thermal generation was the dominant mechanism of leakage current at all bias conditions. It was found that the leakage current was closely related to the reduction of the electric field in the drain depletion region.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.523-525
• /
• 2002

The poly-Si thin film can be used in high mobility active matrix liquid-crystal display (AMLCD) and system on panel (SOP). In this paper, poly-Si thin films were grown by novel high temperature process on the molybdenum (Mo) substrate. By applying a high current above 48A on a Mo substrate. We obtained an improved crystalline Si films with the crystallinity over 80%. We exhibit the properties of structural and electrical properties of high temperature poly-Si thin film transistor on the Mo substrates.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.7
• /
• pp.522-526
• /
• 1998

We have fabricated a LDD structured polysilicon thin film transistor with low leakge current and the optimized LDD length has been obtained. The device performance is improved is improved by hydrogen passivation process. The on.off current ratio of poly0Si TFT s with $0.5{\mu}m$ and $1.0{\mu}m$ LDD length is much higher than that of conventional structured device due to the decrease of leakege current. The optimized LDD length may be $0.5{\mu}$ from the experimental data such as on/off current ratio, threshold voltage and hydrogenation effect.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2006.08a
• /
• pp.1182-1184
• /
• 2006

A mica has been introduced as a new substrate material for the fabrication of the poly-Si TFTs. A poly-Si film is produced on the mica substrate at $550^{\circ}C$ by the nickel-induced crystallization and the poly-Si TFTs on the mica substrate are successfully fabricated for the first time.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.87-88
• /
• 2006

Recently, poly-Si TFT-LCD starts to be mass produced using excimer laser annealing (ELA) poly-Si. The main reason for this is the good quality poly-Si and large area uniformity. We report the influence of channel length and width on poly-Si TFTs performance. Transfer characteristics of p-channel poly-Si thin film transistors fabricated on polycrystalline silicon (poly-Si) thin film transistors (TFTs) with various channel lengths and widths of 2-30 ${\mu}m$ has been investigated. In this paper, we analyzed the data of p-type TFTs. We studied threshold voltage ($V_{TH}$), on/off current ratio ($I_{ON}/I_{OFF}$), saturation current ($I_{DSAT}$), and transconductance ($g_m$) of p-channel poly-Si thin film transistors with various channel lengths and widths.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.7
• /
• pp.525-531
• /
• 2011

In this paper, experimental analyses have been performed to compare the electrical characteristics of n channel LT(low temperature) and HT(high temperature) poly-Si TFTs(polycrystalline silicon thin film transistors) on quartz substrate according to activated step annealing. The size of the particles step annealed at low temperature are bigger than high temperature poly-Si TFTs and measurements show that the electric characteristics those are transconductance, threshold voltage, electric effective mobility, on and off current of step annealed at LT poly-Si TFTs are high more than HT poly-Si TFT's. Especially we can estimated the defect in the activated grade poly crystalline silicon and the grain boundary of LT poly-Si TFT have more high than HT poly-Si TFT's due to high off electric current. Even though the size of particles of step annealed at low temperature, the electrical characteristics of LT poly-Si TFTs were investigated deterioration phenomena that is decrease on/off current ratio depend on high off current due to defects in active silicon layer.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.957-961
• /
• 2004

In order to realize high performance thin film transistor (TFT) on plastic substrate, Si film was deposited on plastic substrate at 170$^{\circ}C$ by using inductivity coupled plasma chemical vapor deposition (ICPCVD). Hydrogen concentration in as-deposited Si film was 3.8% which is much lower than that in film prepared by using conventional plasma enhanced chemical vapor deposition (PECVD). Si film was deposited as micro crystalline phase rather than amorphous phase even at 170$^{\circ}C$ because of high density plasma. By step-by-step Excimer laser annealing, dehydrogenation and recrystallization of Si film were carried out simultaneously. With step-by-step annealing and optimization of underlayer structure, it has succeeded to achieve large grain size of 300nm by using ICPCVD. Base on these results, poly-Si TFT was fabricated on plastic substrate successfully, and it is sufficient to drive pixels of OLEDs, as well as LCDs.

• Electrical & Electronic Materials
• /
• v.11 no.11
• /
• pp.22-27
• /
• 1998

We have investigated the effect of an ion shower doping of the laser annealed poly-Si films at an elevated substrate temperatures. The substrate temperature was varied from room temperature to 300$^{\circ}C$ when the poly-Si film was doped with phosphorus by a non-mass-separated ion shower. Optical, structural, and electrical characterizations have been performed in order to study the effect of the ion showering doping. The sheet resistance of the doped poly-Si films was decreased from7${\times}$106 $\Omega$/$\square$ to 700 $\Omega$/$\square$ when the substrate temperature was increased from room temperature to 300$^{\circ}C$. This low sheet resistance is due to the fact that the doped film doesn't become amorphous but remains in the polycrystalline phase. The mildly elevated substrate temperature appears to reduce ion damages incurred in poly-Si films during ion-shower doping. Using the ion-shower doping at 250$^{\circ}C$, the field effect mobility of 120 $\textrm{cm}^2$/(v$.$s) has been obtained for the n-channel poly-Si TFTs.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.6
• /
• pp.229-235
• /
• 2002

This paper presents the fabrication of polycrystalline thin film transistor(TFT) using sequential lateral solidification(SLS) of amorphous silicon. The fabricated SLS TFT showed high Performance suitable for active matrix liquid crystal display(AMLCD). The SLS process involves (1) a complete melting of selected area via irradiation through a patterned mask, and (2) a precisely controlled pulse translation of the sample with respect to the mask over a distance shorter than the super lateral growth(SLG) distance so that lateral growth extended over a number of iterative steps. The SLS experiment was performed with 550$\AA$ a-Si using 308nm XeCl laser having $2\mu\textrm{m}$ width. Irradiated laser energy density is 310mJ/$\textrm{cm}^2$ and pulse duration time was 25ns. The translation distance was 0.6$\mu$m/pulse, 0.8$\mu$m/pulse respectively. As a result, a directly solidified grain was obtained. Thin film transistors (TFTs) were fabricated on the poly-Si film made by SLS process. The characteristics of fabricated SLS p -type poly-Si TFT device with 2$\mu\textrm{m}$ channel width and 2$\mu\textrm{m}$ channel length showed the mobility of 115.5$\textrm{cm}^2$/V.s, the threshold voltage of -1.78V, subthreshold slope of 0.29V/dec, $I_{off}$ current of 7$\times$10$^{-l4}$A at $V_{DS}$ =-0.1V and $I_{on}$ / $I_{off}$ ratio of 2.4$\times$10$^{7}$ at $V_{DS}$ =-0.1V. As a result, SLS TFT showed superior characteristics to conventional poly-Si TFTs with identical geometry.y.y.y.