• Korean Journal of Materials Research
• /
• v.13 no.11
• /
• pp.711-716
• /
• 2003

Gate length, height, and silicide thickness have all been shrinking linearly as device density has progressively increased over the years. We investigated the effect of the cobalt diffusion during the silicide formation process on the 60$\AA$-thick gate oxide lying underneath the Ti/Co and Co/Ti bilayers. We prepared four different cobalt silicides, which have similar sheet resistance, made from the film structure of Co/Ti(interlayer), and Ti(capping layer)/Co, and peformed the current-voltage, time-to-break down, and capacitance-voltage measurements. Our result revealed that the cobalt silicide process without the Ti capping layer allowed cobalt atoms to diffuse into the upper interface of gate oxides. We propose that 100$\AA$-thick titanium interlayer may lessen the diffusion of cobalt to gate oxides in 1500-$\AA$ height polysilicon gates.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.9
• /
• pp.729-734
• /
• 2000

Recently, Very Large Scale Integrated (VLSI) circuit & deep-submicron bulk Complementary Metal Oxide Semiconductor(CMOS) devices require gate electrode materials such as metal-silicide, Titanium-silicide for gate oxides. Many previous authors have researched the improvement sub-micron gate oxide quality. However, few have reported on the electrical quality and reliability on the ultra thin gate oxide. In this paper, at first, I recommand a novel shallow trench isolation structure to suppress the corner metal-oxide semiconductor field-effect transistor(MOSFET) inherent to shallow trench isolation for sub 0.1${\mu}{\textrm}{m}$ gate oxide. Different from using normal LOCOS technology deep-submicron CMOS devices using novel Shallow Trench Isolation(STI) technology have a unique"inverse narrow-channel effects"-when the channel width of the devices is scaled down, their threshold voltage is shrunk instead of increased as for the contribution of the channel edge current to the total channel current as the channel width is reduced. Secondly, Titanium silicide process clarified that fluorine contamination caused by the gate sidewall etching inhibits the silicidation reaction and accelerates agglomeration. To overcome these problems, a novel Two-step Deposited silicide(TDS) process has been developed. The key point of this process is the deposition and subsequent removal of titanium before silicidation. Based on the research, It is found that novel STI structure by the SEM, in addition to thermally stable silicide process was achieved. We also obtained the decrease threshold voltage value of the channel edge. resulting in the better improvement of the narrow channel effect. low sheet resistance and stress, and high threshold voltage. Besides, sheet resistance and stress value, rms(root mean square) by AFM were observed. On the electrical characteristics, low leakage current and trap density at the Si/SiO$_2$were confirmed by the high threshold voltage sub 0.1${\mu}{\textrm}{m}$ gate oxide.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.39 no.5
• /
• pp.1-7
• /
• 2002

Deep sub-micron bulk CMOS circuits require gate electrode materials such as metal silicide and titanium silicide for gate oxides. Many authors have conducted research to improve the quality of the sub-micron gate oxide. However, few have reported on the electrical quality and reliability of an ultra-thin gate. In this paper, we will recommend a novel shallow trench isolation structure and a two-step TiS $i_2$ formation process to improve the corner metal oxide semiconductor field-effect transistor (MOSFET) for sub-0.1${\mu}{\textrm}{m}$ VLSI devices. Differently from using normal LOCOS technology, deep sub-micron CMOS devices using the novel shallow trench isolation (STI) technology have unique "inverse narrow-channel effects" when the channel width of the device is scaled down. The titanium silicide process has problems because fluorine contamination caused by the gate sidewall etching inhibits the silicide reaction and accelerates agglomeration. To resolve these Problems, we developed a novel two-step deposited silicide process. The key point of this process is the deposition and subsequent removal of titanium before the titanium silicide process. It was found by using focused ion beam transmission electron microscopy that the STI structure improved the narrow channel effect and reduced the junction leakage current and threshold voltage at the edge of the channel. In terms of transistor characteristics, we also obtained a low gate voltage variation and a low trap density, saturation current, some more to be large transconductance at the channel for sub-0.1${\mu}{\textrm}{m}$ VLSI devices.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.7
• /
• pp.521-524
• /
• 1999

Nb silicide was formed on the Si micro-tip arrays in order to improve field emission properties of Si-tip field emitter array. After silicidization of the tips, the etch-back process, by which gate insulator, gate electrode and photoresist were deposited sequentially and gate holes were defined by removing gradually the photoresist by $O_2$ plasma from the surface, was applied. Si nitride film was used as a protective layer in order to prevent oxygen from diffusion into Nb silicide layer and it was identified that the NbSi2 was formed through annealing in $N_2$ ambient at $1100^{\circ}C$ for 1 hour. By the Nb silicide coating on Si tips, the turn-on voltage was decreased from 52.1 V to 32.3 V and average current fluctuation for 1 hour was also reduced from 5% to 2%. Also, the fabricated Nb silicide-coated Si tip FEA emitted electrons toward the phosphor and light emission was obtained at the gate voltage of 40~50 V.

• Journal of the Korean Vacuum Society
• /
• v.1 no.3
• /
• pp.376-381
• /
• 1992

Tungsten silicide films were deposited on the highly phosphorus-doped poly Si/SiO2/Si substrates by Low Pressure Chemical Vapor Deposition. They were heat treated in different conditions. XTEM, SIMS and high frequency C-V analysis were conducted for characterization. It can be concluded that outdiffusion of phosphours impurity throught the silicide films lead to its depletion in the poly-Si gate region near the gate oxide, resulting in loss of capacitance and increase of effective gate oxide thickness.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.12 no.1
• /
• pp.41-45
• /
• 2012

We observed that in chemical vapor deposition (CVD) tungsten silicide (WSix) poly gate scheme, the gate oxide thickness decreases as gate length is reduced, and it intensifies the roll-off properties of transistor. This is because the fluorine diffuses laterally from WSix to the gate sidewall oxide in addition to its vertical diffusion to the gate oxide during gate re-oxidation process. When the channel length is very small, the gate oxide thickness is further reduced due to a relative increase of the lateral diffusion than the vertical diffusion. In DRAM cells where the channel length is extremely small, we found the thinned gate oxide is a main cause of poor retention time.

• Proceedings of the IEEK Conference
• /
• 2000.06b
• /
• pp.64-67
• /
• 2000

Tungsten silicide(WSi$_2$) is proposed for the alternate gate electrode of ULSI MOS devices. Good structural property and low resistivity of WSi$_2$ deposited by a low pressure chemical vapor deposition(LPCVD) method directly on SiO$_2$ is obtained after annealing. Especially, WSi$_2$-SiO2 interface remains flat after annealing tungsten silicide at high temperature. Electrical characteristics of annealed WSi$_2$-SiO$_2$-Si(MOS) capacitors were improved in view of charge trapping.

• Korean Journal of Materials Research
• /
• v.15 no.5
• /
• pp.301-305
• /
• 2005

We fabricated nickel silicide layers on whole non-patterned wafers from $p-Si(100)SiO_2(200nm)$/poly-Si(70 nm)mn(40 nm) structure by 40 sec rapid thermal annealing of $500\~900^{\circ}C$. The sheet resistance, cross-sectional microstructure, surface roughness, and phase analysis were investigated by a four point probe, a field emission scanning electron microscope, a scanning probe microscope, and an X-ray diffractometer, respectively. Sheet resistance was as small as $7\Omega/sq$. even at the elevated temperature of $900^{\circ}C$. The silicide thickness and surface roughness increased as silicidation temperature increased. We confirmed the nickel silicides iron thin nickel/poly-silicon structures would be a mixture of NiSi and $NiSi_2$ even at the $NiSi_2$ stable temperature region.

• Proceedings of the KIEE Conference
• /
• 1989.11a
• /
• pp.122-126
• /
• 1989

A composite polycide struoture consisting of refractory metal and noble metal silicide film on top of polysilicon bas been considered as a replacement for polysilicon as a gate electrode and Interconnect line in MOSFET integrated circuits. In this paper presents divice characteristics of NOS with $TiSi_2/n^+$polyoide and $CoSi_2/n^+$polycide gate. Also, evaporated Ti,Co films on polysilicon has been annealed by RTA and furnace annealing in $N_2$ abient at temperature of $400^{\circ}C-1000^{\circ}C$. The Ti-,Co-silioide formation is characterized by 4-point probe, silicide growth rate and Its reproductivity bas been examined by SEM.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.685-688
• /
• 2002

In this paper, it is reported that the anode current changes at the constantly applied gate voltages and the current-voltage (I-V) characteristics of Si, Co silicide and Mo silicide field emitter arrays (FEAs) depending on vacuum level from a $10^{-9}$ torr to a $10^{-6}$ torr. The mechanism of the robustness of anode current degradation of Mo silicide FEAs under poor vacuum conditions can be explained by the model of tolerance for the oxygen adsorption and oxidation at the silicide surface. Also, we present the changes of emitting area and work function of the emitters according to vacuum level.