• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.2
• /
• pp.137-143
• /
• 2017

In the present study, Ni and $TaF_5$ were chosen as additives to enhance the hydriding and dehydriding rates of Mg. A sample with a composition of 80 wt% Mg + 14 wt% Ni + 6 wt% $TaF_5$ (named $80Mg+14Ni+6TaF_5$) was prepared by high-energy ball milling in hydrogen. Its hydriding and dehydriding properties were then examined. At the fourth cycle, the activated sample absorbed 3.88 wt% H for 2.5 min, 4.74 wt% H for 5 min, and 5.75 wt% H for 60 min at 593 K under 12 bar $H_2$. $80Mg+14Ni+6TaF_5$ had an effective hydrogen-storage capacity (the quantity of hydrogen absorbed for 60 min) of about 5.8 wt%. The sample desorbed 1.42 wt% H for 5 min, 3.42 wt% H for 15 min, and 5.09 wt% H for 60 min at 593 K under 1.0 bar $H_2$. Line scanning results by EDS for $80Mg+14Ni+6TaF_5$ before and after cycling showed that the peaks of Ta and F appeared at different positions, indicating that the $TaF_5$ in $80Mg+14Ni+6TaF_5$ was decomposed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.6
• /
• pp.629-636
• /
• 2014

For surface modification, bulk metallic glass coatings were fabricated using metallic glass powder and a mixture of a self-fluxing alloy or/and hard metal alloys with a heat-resisting property using a high velocity oxy-fuel coating thermal spraying process. Microstructural analyses and mechanical tests were carried out using X-ray diffraction, a scanning electron microscope, an atomic force microscope, a three-dimensional optical profiler, and nanoindenation. As a result, the monolithic metallic glass coating was found to consist of solid particle and lamellae regions that included many pores. Second phase-reinforced composite coatings with a self-fluxing alloy or/and hard metal alloy additives were employed with in-situ $Cr_2Ni_3$ precipitate or/and ex-situ WC particles in an amorphous matrix. The mechanical behaviors of the solid particles and lamella regions showed large hardness and elastic modulus differences. The mechanical properties of the particle regions in the metallic glass composite coatings were superior to those of the lamellae regions in the monolithic metallic glass coatings, but indicated similar trends in matrix region of all the coating layers.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.2 no.2
• /
• pp.145-153
• /
• 2004

H$_2$SO$_4$ and citric acid were used as additives for the electrokinetic remediation experiment to increase removal efficiency of $^{137}$ Cs and $^{60}$ Co from the radioactive soil waste stored for more than 10 years. The average effluent velocity discharged from the elctrokinectic remediation experimental column was 2.0${\times}$10$^{-2}$ cm/min and the discharged soil wastewater volume for 10 days is 3.6 pore volume of the column. 97% of $^{60}$ Co in the column was decontaminated for 10 days of operation, while only 54% of $^{137}$ Cs was decontaminated. These results are considered that the absorption equilibrium coefficient of $^{137}$ Cs is higher than that of $^{60}$ Co. The predicted values of the residual concentration by the proposed mathematical model were well coincided with the experimental results within the experimental error range

• Journal of the Korean Electrochemical Society
• /
• v.10 no.2
• /
• pp.94-103
• /
• 2007

The transition of interconnection metal from aluminum alloy to copper has been introduced to meet the requirements of high speed, ultra-large scale integration, and high reliability of the semiconductor device. Since copper, which has low electrical resistivity and high resistance to degradation, has different electrical and material characteristics compared to aluminum alloy, new related materials and processes are needed to successfully fabricate the copper interconnection. In this review, some important factors of multilevel copper damascene process have been surveyed such as diffusion barrier, seed layer, organic additives for bottom-up electro/electroless deposition, chemical mechanical polishing, and capping layer to introduce the related issues and recent research trends on them.

• Particle and aerosol research
• /
• v.15 no.1
• /
• pp.1-13
• /
• 2019

Current desulfurization and denitrification technologies have reached a considerable level in terms of reduction efficiency. However, when compared with the simultaneous reduction technology, the individual reduction technologies have issues such as economic disadvantages due to the difficulty to scale-up apparatus, secondary pollution from wastewater/waste during the treatment process, requirement of large facilities for post-treatment, and increased installation costs. Therefore, it is necessary to enable practical application of simultaneous SOx and NOx treatment technologies to remove two or more contaminants in one process. The present study analyzes a technology capable of maintaining simultaneous treatment of SOx and NOx even at low temperatures due to the electrochemically generated strong oxidation of the wet-pulse complex system. This system also reduces unreacted residual gas and secondary products through the wet scrubbing process. It addresses common problems of the existing fuel gas treatment methods such as SDR, SCR, and activated carbon adsorption (i.e., low treatment efficiency, expensive maintenance cost, large installation area, and energy loss). Experiments were performed with varying variables such as pulse voltage, reaction temperature, chemicals and additives ratios, liquid/gas ratio, structure of the aeration cleaning nozzle, and gas inlet concentration. The performance of individual and complex processes using the wet-pulse discharge reaction were analyzed and compared.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.16 no.4
• /
• pp.479-490
• /
• 2018

The granite melting concept, which was suggested by Gibb's group for the closing of a deep borehole, was experimentally checked for KURT granite. The granite melting experiments were performed in two pressure conditions of atmospheric melting with certain inorganic additives and high pressure melting formed by water vaporization. The results of atmospheric tests showed that KURT granite started to melt at a lower temperature of $1,000^{\circ}C$ with NaOH addition and that needle shaped crystals were formed around partially melted crystals. In high pressure tests, vapor pressure was increased by adding water with maximum pressure of about 400 bars. KURT granite was partially melted at $1,000^{\circ}C$ when vapor pressure was low. However, it was not melted at vapor pressures higher than 200 bars. Therefore, it was determined that high pressure with a small amount of water vapor more effectively decreased the melting point of granite. Meanwhile, high temperature and high pressure vapor caused severe corrosion of the reactor wall.

• New & Renewable Energy
• /
• v.18 no.3
• /
• pp.23-31
• /
• 2022

This study evaluated the potential of coffee waste (CW) and used frying oil (UFO) as an additive in the production of pitch pine (PIP) and Mongolian oak (MOK) pellets. Ash contents obtained from CW and UFO were 0.5% and <0.1%, respectively. The calorific values of UFO (31.4 MJ/kg) and CW (26.3 MJ/kg) are higher than PIP (20.6 MJ/kg) and MOK (19.1 MJ/kg). For pellets fabricated using a pilot-scale flat-die pellet mill, regardless of fabricating conditions, moisture content (MC) and bulk density of PIP and MOK pellets satisfied the A1 wood pellet standard for residential and small-scale commercial uses, as designated by the National Institute of Forest Science (NIFOS) of the Republic of Korea. When CW was used as an additive, durability of PIP pellets made with 12%-MC sawdust and MOK pellets increased. The optimal conditions for producing PIP and MOK pellets could be by adding 20 mesh CW as an additive and the using of 12%-MC sawdust. However, durability of PIP pellets and ash content MOK pellets did not satisfy the A1 wood pellet standard of NIFOS. Thus, further research is needed to improve the properties of wood pellets with additives.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.11 no.1
• /
• pp.11-21
• /
• 2013

The Geyoungju Ca-bentonite with dry density of 1.6 g/$cm^3$ has been considered as a standard buffer material for the disposal of high level waste in KAERI disposal system design. But it had relatively lower thermal conductivity compared with other surrounding materials, that was one of key parameters to limit the increase of the disposal density in the disposal system. In this study, various additives were selected and mixed with the Ca-bentonite in different mixing methods in order to increase the thermal conductivity from 0.8 W/mK to 1.0 W/mK. As an additive, CNT (Cabon Nano Tube), graphite, alumina, CuO, and $Fe_2O_3$ were selected, which are chemically stable and have good thermal conductivity. As mixing methods, dry hand-mixer mixing, wet milling and dry ball mill mixing were applied for the mixing. Above all, the ball mill mixing was proved to be most effective since the produced mixture was most homogeneous and showed higher increase in the thermal conductivity. From this study, it was confirmed that the thermal conductivity for the Geyoungju Ca-bentonite could be improved by adding small amount of highly thermal conductive material to 1.0 W/mk. In conclusion, it was believed that the experimental results will be valuable in the disposal system design if the additive effects on the swelling and permeability on the compact bentonite are also approved in further studies.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.3 no.3
• /
• pp.249-256
• /
• 2005

Thermal decomposition and stabilization characteristics of the solid cake after the dissolution of nitrate of the lagoon sludge was investigated. Most of the nitrates were dissolved in the water and removed to the filtrate, but small amount of nitrates, calcium carbonate and uranium were remained in the solid cake. The solid cake was thermally decomposed in the muffle furnace at $900^{\circ}C$ for 5 hours. Uranium, which is in the lagoon 1, was stabilized with $NaNO_3$ decomposition to $Na_{2}O{\cdot}2UO_3$ form. For the lagoon 2, it is confirmed that CaO, which was created by thermal decomposition of the $Ca(NO_3)_2$ and $CaCO_3$, was transferred to $Ca(OH)_2$ in the air with water. Because it is known that $Ca(OH)_2$ is stable material, further additives did not need to the stabilization of the thermal decomposition of the lagoons.

• Korean Chemical Engineering Research
• /
• v.54 no.6
• /
• pp.854-862
• /
• 2016

As the demand for a clean energy to replace fossil fuel being depleted increases, hydrogen energy is considered as a promising candidate for future energy source. Water electrolysis which produces hydrogen has high energy efficiency and stability but still has a large overpotential for oxygen evolution reaction (OER). In this study, $Co_3O_4$ catalysts with different morphology were prepared by spray pyrolysis from solutions which contain Co precursor and various organic additives (urea, sucrose, and citric acid), followed by post heat treatment. For the catalysts synthesized, X-ray diffraction (XRD) measurements were performed to identify their crystal structure. Morphology and surface shape of the catalysts were observed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Surface area and pore volume were examined by nitrogen adsortpion & desorption tests and X-ray photoelectron spectroscopy (XPS) was conducted to confirm nitrogen doping. Linear sweep voltammetry (LSV) was carried out to investigate OER activity of $Co_3O_4$ catalysts. As a result, bare-$Co_3O_4$ which has high surface area and small particle size determined by spray pyrolysis showed high activity toward OER.