• Journal of the Korean Vacuum Society
• /
• v.12 no.4
• /
• pp.218-227
• /
• 2003

Pd/Si/Ti/Pt and Pd/Si/Pd/Ti/Au ohmic contacts to n-type InCaAs were investigated for applications to AlGaAs/GaAs HBT emitter ohmic contacts. In the Pd/Si/Ti/Pt ohmic contact, as-deposited contact showed non-ohmic behavior, and high specific contact resistivity of $5\times10^{-3}\Omega\textrm{cm}^2$ was achieved by rapid thermal annealing at $375^{\circ}C$/10 sec. However, the specific contact resistivity decreased remarkably to $2\times10^{-6}\Omega\textrm{cm}^2$ by annealing at $425^{\circ}C$/10sec. In the Pd/Si/Pd/Ti/Au ohmic contact, minimum specific contact resistivity of $3.9\times10^{-7}\Omega\textrm{cm}^2$ was achieved by annealing at $400^{\circ}C$/20sec. In both ohmic contacts, low contact resistivity and non-spiking planar interface between ohmic materials and InGaAs were maintained. Therefore, these thermally stable ohmic contact systems are promising candidates for compound semiconductor devices. RF performance of the AlGaAs/GaAs HBT was also examined by employing the Pd/Si/Ti/Pt and Pd/Si/Pd/Ti/Au systems as emitter ohmic contacts. Cutoff frequencies were 63.9 ㎓ and 74.4 ㎓, respectively, and maximum oscillation frequencies were 50.1 ㎓ and 52.5 ㎓, respectively. It shows very successful high frequency operations.

• Journal of the Korean Vacuum Society
• /
• v.11 no.1
• /
• pp.35-42
• /
• 2002

We fabricate thermally stable and low resistance Ru ohmic contacts to $n-ZnO:Al(3\times10^{18}\textrm{cm}^{-3})$, grown by specially designed dual target sputtering system. It is shown that the as-deposited Ru contact produces a specific contact resistance of $2.1{\times}10^{-3}{\Omega}\textrm{cm}^2$. Annealing of the Ru contacts leads to the improvement of current-voltage characteristics. For example, annealing of the contact at $700^{\circ}C$ for 1 min produces a contact resistance of $3.2{\times}10^{-5}}{\Omega}\textrm{cm}^2$. furthermore, the metallisation scheme is found to be thermally stable: the surface of the contact is fairly smooth with a rms roughness of 1.4 nm upon annealing at $700^{\circ}C$. These results strongly indicate that the Ru contact represents a suitable metallisation scheme for fabrication of high-performance ZnO-based optical devices and high-temperature devices. In addition, possible mechanisms are suggested to describe the annealing temperature dependence of the specific contact resistance.

• Journal of the Korean Vacuum Society
• /
• v.10 no.2
• /
• pp.219-224
• /
• 2001

Pd/Ge/Ti/Pt ohmic contact to n-type InCaAs was investigated. Minimum specific contact resistivity of $3.7\times10^{-6}\; \Omega\textrm{cm}^2$ was achieved by rapid thermal annealing at $400^{\circ}C$ for 10 seconds. This was related to the formation of Pd-Ge compounds and the in-diffusion of Ge atoms to InGaAs surface. However, the specific contact resistivity increased slightly to $low-10^5\; \Omega\textrm{cm}^2$ in the case of longer annealing time. Superior ohmic contact and non-spiking planar interface between ohmic materials and InGaAs were maintained after annealing at high temperature. Therefore, this thermally stable ohmic contact system is a promising candidate for compound semiconductor devices.

• Journal of the Korean Vacuum Society
• /
• v.11 no.1
• /
• pp.43-49
• /
• 2002

Pd/Ge/Pd/Ti/Au ohmic contact to n-type InGaAs was investigated with rapid thermal annealing conditions. Minimum specific contact resistivity of $1.1\times10^{-6}\Omega\textrm{cm}^2$ was achieved after annealing at $400^{\circ}C$/10sec, and a ohmic performance was degraded at higher annealing temperature due to the chemical reaction between the ohmic contact materials and the InGaAs substrate. However, non-spiking planar interface and relatively good ohmic contact($high-10^{-6};{\Omega}\textrm{cm}^2$) were maintained. This ohmic contact system is expected to be a promising candidate for compound semiconductor devices.

• Journal of the Korean Vacuum Society
• /
• v.11 no.4
• /
• pp.201-206
• /
• 2002

Pd/Si/Pd/Ti/Au ohmic contact to n-type InGaAs was investigated with rapid thermal annealing conditions. Minimum specific contact resistivity of $3.9\times10^{-7}\Omega\textrm{cm}^2$ was achieved at $400^{\circ}C$/20sec. This was related to the formation of Pd-Si compounds by rapid thermal annealing and the in-diffusion of Si atoms to InGaAs surface. However, the specific contact resistivity increased slightly to low-$10^{-6}\Omega \textrm{cm}^2$ at $400^{\circ}C$ for longer than 30 seconds, and to high-$10^{-7}$ at 425~$450^{\circ}C$ for 10 seconds. This resulted from the formation of Pd-Ga compounds. Superior ohmic contact and non-spiking planar interface between ohmic materials and InGaAs were maintained after annealing at high temperature. Therefore, this thermally stable ohmic contact system is a promising candidate for compound semiconductor devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.33-36
• /
• 2004

탄소 도핑$(5{\times}10^{19}\;cm^{-3})$된 p-type GaAsSb 에피층 위에, Ti/Pt/Au, Pd/Au, Pd/Ir/Au를 이용한 다층 오믹 접촉을 제작하였다. MOCVD(metal-organic chemical vapor deposition)를 이용하여 성장시킨 이 p-GaAsSb의 정공 이동도는 탄소의 도핑 농도가 매우 높음에도 불구하고, $50\;cm^2/Vs$로 측정되었다. 오믹 접촉의 전기적 특성을 측정하기 위하여 TLM(Transfer length method)를 이용하였다. Pd/Ir/Au을 이용한 오믹접촉의 specific contact resistivity는 $10^{-8}\;ohm-cm^2$ 보다 작은 수치를, transfer length는 100 nm보다 작은 수치를 보였으며, Ti/Pt/Au을 이용한 ohmic contact의 specific contact resistivity는 $10^{-7|\;ohm-cm^2$ 보다 작은 수치를, transfer length는 400 nm보다 작은 수치를 나타내었다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.47.2-47.2
• /
• 2007

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.25-25
• /
• 2007

• Journal of the Korean Vacuum Society
• /
• v.10 no.3
• /
• pp.368-373
• /
• 2001

Pd/Si/Ti/Pt ohmic contact to n-type InGaAs was investigated. As-deposited contact showed non-ohmic behavior, and high specific contact resistivity of $5\times10^{-3}\Omega\textrm{cm}^2$ was achieved by rapid thermal annealing at $375^{\circ}C$ for 10 seconds. However, the specific contact resistivity decreased remarkably to $1.7\times10^{-6}\Omega\textrm{cm}^2$ and $2\times10^{-6}\Omega\textrm{cm}^2$ at $375^{\circ}C$/60sec and $425^{\circ}C$/10sec, respectively. Superior ohmic contact and non-spiking planar interface between ohmic materials and InGaAs were maintained even at $450^{\circ}C$, therefore, this thermally stable ohmic contact system is a promising candidate for compound semiconductor devices.

• Journal of the Korean Vacuum Society
• /
• v.7 no.1
• /
• pp.24-28
• /
• 1998

Pd/Ge ohmic contact system on n-type InGaAs was studied. A good ohmic begavior by rapid thermal annealing was shown up to $400^{\circ}C$, and the specific contact resistance was reduced to low-$10^-6\Omega\textrm{cm}^2$EX>. However, above $425^{\circ}C$ it was deteriorated by intermixing and phase reaction of ohmic metals and InGaAs substrate. No remarkable phase change was observed below $350^{\circ}C$, but the reaction was initiated at ~$375^{\circ}C$ and considerable phase change was found above $425^{\circ}C$. Non-spiking and planar interfaces were observed even when annealed at $425^{\circ}C$, and smooth and shiny surface was kept up to $400^{\circ}C$.