Pd/Si/Pd/Ti/Au Ohmic Contact for Application to AIGaAs/GaAs HBT

AlGaAs/GaAs HBT 응용을 위한 Pd/Si/Pd/Ti/Au 오믹 접촉

  • 김일호 (충주대학교 재료공학과ㆍ나노기술연구소) ;
  • 장경욱 (한서대학교 재료공학과)
  • Published : 2002.12.01

Abstract

Pd/Si/Pd/Ti/Au ohmic contact to n-type InGaAs was investigated with rapid thermal annealing conditions. Minimum specific contact resistivity of $3.9\times10^{-7}\Omega\textrm{cm}^2$ was achieved at $400^{\circ}C$/20sec. This was related to the formation of Pd-Si compounds by rapid thermal annealing and the in-diffusion of Si atoms to InGaAs surface. However, the specific contact resistivity increased slightly to low-$10^{-6}\Omega \textrm{cm}^2$ at $400^{\circ}C$ for longer than 30 seconds, and to high-$10^{-7}$ at 425~$450^{\circ}C$ for 10 seconds. This resulted from the formation of Pd-Ga compounds. Superior ohmic contact and non-spiking planar interface between ohmic materials and InGaAs were maintained after annealing at high temperature. Therefore, this thermally stable ohmic contact system is a promising candidate for compound semiconductor devices.

N형 InGaAs에 대한 Pd/Si/Pd/Ti/Au 오믹 접촉의 급속 열처리 조건에 따른 오믹 특성을 조사하였다. $450^{\circ}C$까지의 열처리 동안에 전반적으로 우수한 오믹 특성을 나타내어 $400^{\circ}C$, 20초의 급속 열처리 조건에서 최저 $3.9\times10^{-7}\Omega\textrm{cm}^2$ 의 접촉 비저항을 나타내었다. 이는 열처리에 의해 생성된 Pd-Si계 화합물의 형성 및 Si의 InGaAs 표면으로의 확산과 관련이 있었다. 그러나 $400^{\circ}C$에서 열처리 시간을 30초 이상으로 연장할 경우 접촉 비저항이 low-$10^{-6}\Omega \textrm{cm}^2$ 으로 약간 증가하였고, 열처리 조건을 425~$450^{\circ}C$/10초로 변화시킬 경우 high-$10^{-7}$~low-$10^{-6}\Omega \textrm{cm}^2$으로 약간 증가하였다. 이는 오믹 재료와 InGaAs의 반응에 의해 Pd-Ga계 화합물이 형성된 것과 관련이 있었다. 고온 열처리 후에도 오믹 재료와 InGaAs의 평활한 계면을 유지하면서 우수한 오믹 특성을 나타내어, 화합물 반도체 소자의 오믹 접촉으로 충분히 응용 가능하다고 판단된다.

Keywords

References

  1. J. Appl. Phys. v.62 Y. C. Shih;M. Murakami;E. L. Wilkie;A. C. Callerari https://doi.org/10.1063/1.339860
  2. J. Appl. Phys. v.72 K. Tanahashi;H. J. Tanaka;A. Otuki;M. Murakami https://doi.org/10.1063/1.352228
  3. J. Appl. Phys. v.65 L. S. Yu;L. C. Wang;E. D. Marshall;S. S. Lau;T. F. Kuech https://doi.org/10.1063/1.342954
  4. Thin Solid Film v.187 A. Paccagnella;L. C. Wang;C. Canali;G. Castellaneta;M. Dapor;G. Donzelli;E. Zanoni;S. S. Lau https://doi.org/10.1016/0040-6090(90)90105-M
  5. J. Appl. Phys. v.62 E. D. Marshall;B. Zhang;L. C. Wang;P. F. Jiao;W. X. Chen;T. Sawada;S. S. Lau;K. L. Kavangh;T. F. Kuech https://doi.org/10.1063/1.339705
  6. Appl. Phys. Lett. v.54 L. C. Wang;S. S. Lau;E. K. Hsieh;J. R. Velebir https://doi.org/10.1063/1.101032
  7. 한국진공학회지 v.7 김일호;박성호;김좌연;이종민;이태우;박문평
  8. Jpn. J. Appl. Phys. v.37 I.-H. Kim;S. H. Park;J.-W. Kim;J.-M. Lee;T.-W. Lee;M.-P. Park
  9. J. Appl. Phys. v.74 W. Y. Han;Y. Lu;H. S. Lee;M. W. Cole;L. M. Casas;A. DeAnni;K. A. Jones;L. W. Yang https://doi.org/10.1063/1.355248
  10. Appl. Phys. Lett. v.71 I.-H. Kim;S. H. Park;T.-W. Lee;M.-P. Park https://doi.org/10.1063/1.119421
  11. J. Vac. Sci.& Tech. v.B10 T. C. Shen;G. B. Gao;H. Morkoc
  12. J. Appl. Phys. v.69 A. Katz;C. R. Abermathy;S. J. Pearton;B. E. Weir;W. Savin https://doi.org/10.1063/1.348707
  13. Appl. Phys. Lett. v.23 K. Kajiyama;Y. Mizushima;S. Sakata https://doi.org/10.1063/1.1654957
  14. J. Appl. Phys. v.76 P. W. Leech;G. K. Reeves;M. H. Kibel https://doi.org/10.1063/1.357264
  15. Mater. Sci. Eng. v.B29 T. Pirling;K. Fricke;M. Schussler;W. Y. Lee;H. Fuess;H. L. Hartagel
  16. Electron. Lett. v.32 L. C. Wang;M.-H. Park;H. A. Jorge;I. H. Han;F. Kish https://doi.org/10.1049/el:19960224
  17. IEEE Device Lett. v.7 W. X. Chen;S. C. Hsueh;P. K. L. Yu;S. S. Lau https://doi.org/10.1109/EDL.1986.26443