The phenotyping of the sixth complement component (C6) was performed on plasma or serum samples from 383 unrelated Korean, by IEF and immunoblotting using anti-human C6 serum. Three common allotypes, C6 A, C6 B and C6 B2 and two rare allotypes, C6 Ml and C6 Mu were observed. The allele frequencies of C6*A, C6*B and C6*B2 were estimated to be 0.4399, 0.5144, 0.0392, respectively. These frequencies are similar to those of the Eastasian populations.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.2 s.257
• /
• pp.205-210
• /
• 2007

SiC/SiC composites and monolithic SiC materials have been fabricated by the melt infiltration process, through the creation of crystallized SiC phase by the chemical reaction of C and Si. The reinforcing material used in this system was a braided Hi-Nicalon SiC fiber with double interphases of BN and SiC. The microstructures and the mechanical properties of RS-SiC based materials were investigated through means of SEM, TEM, EDS and three point bending test. The matrix morphology of RS-SiS/SiC composites was greatly composed of the SiC phases that the chemical composition of Si and C is different. The TEM analysis showed that the crystallized SiC phases were finely distributed in the matrix region of RS-SiC/SiC composites. RS-SiC/SiC composites also represented a good flexural strength and a high density, accompanying a pseudo failure behavior.

• IEIE Transactions on Smart Processing and Computing
• /
• v.5 no.1
• /
• pp.55-62
• /
• 2016

In this paper, we propose a hybrid multi.system-on-chip (H-MSoC) architecture that provides a high-flexibility system in a rapid development time. The H-MSoC approach provides a flexible system-on-chip (SoC) architecture that is easy to configure for physical- and application-layer development. The physical- and application-layer aspects are dynamically designed and modified; hence, it is important to consider a design methodology that supports rapid SoC development. Physical layer development refers to intellectual property cores or other modular hardware (HW) development, while application layer development refers to user interface or application software (SW) development. H-MSoC is built from multi-SoC architectures in which each SoC is localized and specified based on its development focus, either physical or application (hybrid). Physical HW development SoC is referred to as physical-SoC (Phy-SoC) and application SW development SoC is referred to as application-SoC (App-SoC). Phy-SoC and App-SoC are connected to each other via Ethernet. Ethernet was chosen because of its flexibility, high speed, and easy configuration. For prototyping, we used a LEON3 SoC as the Phy-SoC and a ZYNQ-7000 SoC as the App-SoC. The proposed design was proven in real-time tests and achieved good performance.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.429-434
• /
• 2015

This study investigates the macroscopic wear behaviors of C/C and C/C-SiC composites coated with hafnium carbide (HfC). To improve the wear resistance of C/C composites, low-pressure chemical vapor deposition (LPCVD) was used to obtain HfC coating. The CVD coatings were deposited at various deposition temperatures of 1300, 1400, and $1500^{\circ}C$. The effect of the substrate material (the C/C substrate, the C/C-CVR substrate, or the C/C-SiC substrate deposited by LSI) was also studied to improve the wear resistance. The experiment used the ball-on-disk method, with a tungsten carbide (WC) ball utilized as an indenter to evaluate the wear behavior. The HfC coatings were found to effectively improve the wear resistance of C/C and C/C-SiC composites, compared with the case of a non-coated C/C composite. The former showed lower friction coefficients and almost no wear loss during the wear test because of the presence of hard coatings. The wear scar width was relatively narrower for the C/C and C/C-SiC composites with hafnium coatings. Wear behavior was found to critically depend on the deposition temperature and the material. Thus, the HfC-coated C/C-SiC composites fabricated at deposition temperatures of $1500^{\circ}C$ showed the best wear resistance, a lower friction coefficient, and almost no loss during the wear test.

• Journal of the Korean Ceramic Society
• /
• v.26 no.4
• /
• pp.514-520
• /
• 1989

The early hydration characteristics according to the C3S/C3A ratio and presence of gypsum, in order to establish the hydration mechanism of the system C3S-C3A, have been studied. The rate of C3S dissolution in the system C3S-Gypsum was higher than that in the system C3S. Consequently, the induction period was reduced and the rate of Ca(OH)2 formation in the accleration period was increased. The hydration of C3S in the system C3S-C3A was retarded because Al3+ in the liquid phase originating from the hydration of C3A was incorporated into calcium hydrosilicates formed. The retardation phenomenon of C3S hydration was not appeared in the system C3S-C3A-gypsum because the reaction of monosulfate formation became the rate-determining step.

• Proceedings of the Korean Geotechical Society Conference
• /
• 1999.02a
• /
• pp.70-77
• /
• 1999

Consolidation settlements on soft clay are often large and potentially damaging to structures. Currently, large-scale projects are in progress in Korea. These structures will be constructed on both thick and soft clay layers, and so the accurate evaluation of magnitude of settlement is required at every step in design and construction. Especially, secondary compression play an important role in consolidation settlements on soft clay. Generally, the magnitudes of secondary compression are evaluated by laboratory and in-situ consolidation tests or by empirical $C_{a/}$ $C_{c}$ relationships. The empirical $C_{a/}$ $C_{c}$ may not be only economical, but a fast and powerful tool in estimating secondary consolidation settlement. However, databases of the $C_{a/}$ $C_{c}$ relationship for sites in Korea are currently insufficient. The purpose of this study is to investigate the relationship of $C_{a/}$ $C_{c}$, on marine clay near the southern sea in Korea. In this study a series of incremental loading consolidation tests (measuring base pore water pressure) are performed. It was found that the $C_{a/}$ $C_{c}$ on undisturbed marine clay equaled 0.0397. This value is similar to the value proposed by Mesri and Castro(1987) for inorganic clay and silt. and silt. and silt.

• Journal of the Korean Ceramic Society
• /
• v.38 no.4
• /
• pp.314-318
• /
• 2001

SiC-TiC composites have been fabricated by using a mechanochemical processing of a mixture of Si, Ti, and C at room temperature and subsequent hot pressing. TiC powders have been obtained by the mechanochemical processing of a mixture of Ti and C whereas SiC powders has not been obtained from a mixture of Si and C. By using the exothermic reaction between Ti and C, SiC-TiC powder could be obtained from the mixture of Si, Ti, and C using the mechanochemical processing for more than 12h. The X-ray diffraction analysis has shown that the powder subjected to the mechanochemical processing consisted of the particles having crystallite size below 10nm. Fully densified SiC-TiC composites have been obtained by hot-pressing of the powder at 1850$\^{C}$ for 3h and it has shown comparable mechanical properties to those of the SiC-TiC composites prepared from the commercially available SiC and TiC powders. Flexural strength of 560 MPa and fracture toughness of 4.8 MP$.$am$\_$1/2/ have been shown for the SiC-TiC composites with composition corresponding to 0.75:0.25:1 mole ratio of Si:Ti:C.

• Proceedings of the Korean Geotechical Society Conference
• /
• 1999.03a
• /
• pp.373-380
• /
• 1999

Consolidation settlements of soft clay are often large and potentially damaging to the structures. Currently, large-scale construction projects for airport and harbor etc. are in progress in Korea and many of these structures will be constructed on thick and soft clay layers. For this kind of ground condition, evaluation of consolidation settlement is required at every design and construction stages, and the magnitude of secondary compression appears to be larger than expected. Generally, the magnitude of secondary compression is evaluated by laboratory and in-situ consolidation tests or by empirical $C_{a/}$ $C_{c}$, relationship. The use of empirical value $C_{a/}$ $C_{c}$ may be economical, fast and powerful tool in estimating secondary consolidation settlement. However, the databases of the $C_{a/}$ $C_{c}$, for typical soft clays in Korea are insufficient. The purpose of this study is to investigate the relationship of $C_{a/}$ $C_{c}$ on marine clay near the southern sea in Korea. A series of incremental loading consolidation tests with measurement of pore water pressure were performed. It was found that the $C_{a/}$ $C_{c}$ of undisturbed marine clay is 0.0397. This value is similar to that proposed by Mesri and Castro(1987) on inorganic clay and silt. and silt. and silt.

• Journal of the Korean Geotechnical Society
• /
• v.15 no.6
• /
• pp.87-98
• /
• 1999

Consolidation settlements on soft clay are often greatly and potentially damaging to structures. Currently, large-scale projects are in planning or progressing in Korea. These structures will be constructed on both thick and soft clay layers, and so the accurate evaluation of magnitude of settlement is required at every step in design and construction. Especially, secondary compression may play an important role in consolidation settlements of soft clay. Generally, the magnitudes of secondary compression are evaluated by laboratory and in-situ consolidation tests. The empirical $C_a/C_c$ may be economical, fast and powerful tool in estimating secondary consolidation settlement. However, the databases of the $C_a/C_c$ at construction site in Korea are insufficient. The purpose of this study is to investigate the relationship of $C_a/C_c$ on marine clay near the southern sea in Korea. A series of incremental loading consolidation tests (measuring base pore water pressure) is peformed. It was found that the $C_a/C_c$ on undisturbed marine clay is 0.0397.

• The Journal of Internal Korean Medicine
• /
• v.34 no.1
• /
• pp.71-85
• /
• 2013

Objectives : The aim of this study was to evaluate the distribution of tongue color and the correlation of the tongue colors with clinical laboratory parameters. Methods : Statistical analysis on the frequency of each tongue color and the results of the clinical laboratory parameters in each tongue color group. Results : Tongue colors that appeared most frequently were 702c, 695c, 493c, 694c, 701c, 500c, 7432c, 7431c, 7634c, 7419c in that order. Following them, 494c and 507c were rarer colors, and 501c, 673c, 687c, 693c, 696c, 703c, 7418c were equally rarest colors. Among each tongue color group, a significant difference was found in the result of complete blood cell count (CBC). The level of red blood cell (RBC) of 7432c group was significantly higher than that of the other groups except 694c group. The level of hemoglobin (Hb), hematocrit (Hct) of 7432c group were significantly higher than those of all the other groups. The level of RBC of 7431c group was lowest and significantly different from 694c, 7432c group. In results of the other tests were not significantly different. However the level of total cholesterol was higher in 695c, 694c, 500c group, and the level of triglyceride was higher in 500c, 7431c, 694c group. Those four colors have a low chroma and 7431c, 695c take blue violet color. Conclusions : The tongue color is distributed throughout following colors by order of frequency: 702c, 695c, 493c, 694c, 701c, 500c, 7432c, 7431c, 7634c, 7419c, 708c, 494c, 507c, 501c, 673c, 687c, 693c, 696c, 703c, 7418c. Some parameters of CBC has a significant correlation with some tongue colors. Other results including lipid profile, renal function test, and liver function test had no significant difference according to tongue color. However, the colors which have low chroma or take blue violet color tented to be higher in the levels of total cholesterol and triglyceride.