• 한국재료학회지
• /
• 제17권2호
• /
• pp.96-99
• /
• 2007

The effects of post-annealing of high-k $HfO_2$ thin films grown by atomic layer deposition method were investigated by the annealing treatments of $400-600^{\circ}C$. $Pt/HfO_2/p-Si\;MOS$ capacitor structures were fabricated, and then the capacitance-voltage and current-voltage characteristics were measured to analyze the electrical characteristics of dielectric layers. The X-ray diffraction analyses revealed that the $500^{\circ}C-annealed\;HfO_2$ film remained to be amorphous, and the $600^{\circ}C-annealed\;HfO_2$ film was crystallized. The annealing treatment at $500^{\circ}C$ resulted in the highest capacitance and the lowest leakage current due to the reduction of defects in the $HfO_2$ films and non-crystallization. Our results suggest that post-annealing treatments are a critical factor in improving the characteristics of gate dielectric layer.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2001년도 창립10주년 제20회 학술발표회
• /
• pp.150-150
• /
• 2001

• 한국표면공학회지
• /
• 제41권1호
• /
• pp.1-5
• /
• 2008

In this work, improvement of mechanical and electrical properties of gate dielectric layer for flexible organic thin film transistor (OTFT) devices was investigated. In order to increase the mechanical flexibility of PVP (poly(4-vinyl phenol) organic gate dielectric, a very thin inorganic $HfO_2$ layers with the thickness of $5{\sim}20nm$ was inserted in between the spin-coated PVP layers. Insertion of the inorganic $HfO_2$ in the laminated organic/inorganic structure of PVP/$HfO_2$/PVP layer led to a dramatic reduction in the leakage current compared to the pure PVP layer. Under repetitive cyclic bending, the leakage current density of the laminated PVP/$HfO_2$/PVP layer with the thickness of 20-nm $HfO_2$ layer was not changed, while that of the single PVP layer was increased significantly. Mechanical flexibility tests of the OTFT devices by cyclic bending with 5 mm bending radius indicated that the leakage current of the laminated PVP/$HfO_2$(20 nm)/PVP gate dielectric in the device structure was also much smaller than that of the single PVP layer.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2008년도 제34회 동계학술대회 초록집
• /
• pp.335-335
• /
• 2008

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2005년도 춘계학술발표대회 및 제8회 신소재 심포지엄 논문개요집
• /
• pp.147-147
• /
• 2005

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2011년도 춘계학술대회 초록집
• /
• pp.130.2-130.2
• /
• 2011

본 연구에서는 RF magnetron sputtering을 이용하여 실리콘 박막 태양전지용 ZnO:Al 전면전극을 제작하고 다양한 식각조건에 따른 ZnO:Al 박막의 표면형상 변화와 함께 전기적 및 광학적 특성 변화를 조사하였다. pin 구조를 갖는 실리콘 박막 태양전지의 효율 향상을 위해서는 입사광의 산란효과에 따른 광포획 증가가 필수적이며 이를 위하여 ZnO:Al 전면전극의 표면텍스처링 형성이 필요하다. 식각용액으로는 HCl과 HF 등을 사용하였으며 식각용액 농도 및 식각시간을 변화시켰다. 식각 후의 ZnO:Al 박막의 표면형상은 SEM(Scanning Electron Microscope)과 AFM(Atomic Force Microscope)을 이용하여 분석을 하였고, UV-visible-nIR spectrometer를 이용하여 총 투과도 및 산란 투과도를 측정하였다. 이 외에도 four-point probe 및 Hall measurement를 이용하여 전기적 특성 변화를 조사하였다. 다양한 식각조건에 따라 제조된 ZnO:Al 박막 위에 실리콘 박막 태양전지를 제작하여 전면전극의 표면형상에 따른 태양전지 성능변화를 비교 분석하였다.

• 한국전기전자재료학회논문지
• /
• 제24권9호
• /
• pp.710-712
• /
• 2011

In this study, we fabricate resistive switching random access memory (ReRAM) devices constructed with a Al/$HfO_2$/ITO structure on glass substrates and investigate their memory characteristics. The hafnium oxide thin film used as a resistive switching layer is sputtered at room temperature in a sputtering system with a cooling unit. The Al/$HfO_2$/ITO device exhibits bipolar resistive switching characteristics, and the ratio of the high resistance (HRS) to low resistance states (LRS) is more than 60. In addition, the resistance ratio maintains even after $10^4$ seconds.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제38회 동계학술대회 초록집
• /
• pp.199-199
• /
• 2010

XRR(X-ray reflectometry)은 나노 스케일 박막의 두께를 측정하는 유망한 도구로 인식되고 있고, XRR측정 결과의 신뢰성을 향상시키기 위하여 많은 연구가 이루어지고 있다. 본 연구에서는 나노 스케일 박막 두께의 정확한 측정을 위해 Si기판 위에 성장시킨 $HfO_2$, $Al_2O_3$, $Ta_2O_5$의 산화물 박막에 대하여 여러 가지 전처리 조건을 변화시켜 조건에 따른 반사율 곡선의 변화와 분석 결과를 살펴보았다. 샘플의 전처리에는 acetone, sulfuric acid, methanol, 초음파세척기를 이용하였고, 전처리가 끝난 후 샘플에 남아있는 수분기를 제거하기 위하여 약 $150^{\circ}C$의 온도로 가열 후 측정비교 분석하였다. 전처리 시 solution과 시간 등의 전처리 조건이 변화함에 따라 X-선 반사율 곡선의 변화가 있음을 알 수 있었고, 이에 따라 XRR 측정 분석 시 두께에 영향을 받았으며, TEM과 XPS를 이용하여 전처리 영향에 대하여 비교 분석 하였다. 이번 연구를 통하여 전처리 방법에 따라 XRR 측정에 정확성을 향상 시킬 수 있는 있는 것으로 보여진다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2000년도 제18회 학술발표회 논문개요집
• /
• pp.106-106
• /
• 2000

반도체 소자가 미세화 됨에 따라 게이트 유전막으로 사용되는 SiO2의 박막화가 요구되나, boron penetration에 의한 Vt shift, 게이트 누설전류, 다결정 실리콘 게이트의 depletion effect 그리고 quantum mechanical effect 때문에 ~20 급에서 한계를 나타내고 있다. 이에 0.1$\mu\textrm{m}$이상의 design rule을 갖는 logic이나 memory 소자에서 요구되어지는 ~10 급 게이트 산화막은 SiO2(K=3.9)를 대신하여 고유전율을 갖는 재료의 채택이 필수 불가결하게 되었다. 고유전 박막 재료를 사용하면, 두께를 두껍게 해도 동일한 inversion 특성이 유지되고 carrier tunneling 이 덜하여 등가 산화막의 두께를 줄일 수 있다. 이러한 고유전박막 재료중 가장 활발히 연구되고 있는 재료는 Ta2O5, Al2O3, STO 그리고 BST 등이 있으나 Ta2O5, STO, BST 등은 실리콘 기판과 직접 반응을 한다는 문제를 가지고 있으며, Al2O3는 유전율이 낮의 재료가 최근 주목받고 있다. 본 실험에서는 ZrO2, HfO2 또는 그 silicates 등의 재료가 최근 주목 받고 있다. 본 실험에서는 ZrO2 박막의 증착조건에 따른 물리적, 전기적 특성 변화에 대하여 연구하였다. RCA 방식으로 세정한 P-type (100) 실리콘 기판위에 reactive DC sputtering 방법으로 압력 5mtorr, power 100~400W, 기판온도는 100-50$0^{\circ}C$로 변화시켜 ZrO2 박막을 증착한 후 산소와 아르곤 분위기에서 400-80$0^{\circ}C$, 10-120min으로 열처리하였다. 증착직후의 시편들과 열처리한 ZrO2 박막의 미세구조와 전기적 특성 변화를 관찰하였다. 우선 굴절율(RI)를 이용해 ZrO2 박막의 밀도를 예측하여 power와 기판온도에 따라 이론값 2.0-2.2 에 근접한 구조를 얻은 후 XRD, XPS, AFM, 그리고 TEM을 사용하여 ZrO2 박막의 chemical bonding, surface roughness 그리고 interfacial layer의 특성을 관찰하였다. 그리고 C-V, I-V measurement를 이용해 capacitance, 유전율, 누설전류 등의 전기적 특성을 관찰해 최적 조건을 설정하였다.

• 한국진공학회지
• /
• 제19권2호
• /
• pp.141-147
• /
• 2010

$Al_2O_3$, $TiO_2$, $HfO_2$와 같은 high-k (고 유전상수) 산화물 박막을 Si, $SiO_2$/Si, GaAs 기판에 각각 입혀서 주기적인 온도변화에 의해 발생되는 박막 표면에서의 반사율 변화를 이용한 열-반사율법을 이용하여 열전도도를 측정하였다. 그 결과, 약 50nm 두께에서 0.80~1.29 W/(mK)와 같은 높은 열전도도를 가지고 있어 CMOS와 메모리 디바이스와 같은 전자 회로에서 발생되는 열을 효과적으로 방산할 수 있고, 또 미세 입자의 크기에 따라 열전달이 변화하는 것을 확인하였다.