• Journal of the Korean Ceramic Society
• /
• v.47 no.5
• /
• pp.461-466
• /
• 2010

In this study, $Al_2O_3/TaAlO_4/SiO_2$ (A/TAlO/S) structures with tantalum aluminate charge trap layer were fabricated for Nand flash memory device. We evaluated the memory window and retention characteristic as the thickness of the tunnel oxide was varied among 3 nm, 4 nm, and 5 nm. All tunnel oxide thicknesses were measured by ellipsometer and TEM (Transmission Electron Microscope). The A/TAlO/S multi-layer film consisted of 5 nm tunnel oxide showed the best result of memory window of 1.57 V and retention characteristics. After annealing the 5 nm tunnel oxide A/TAlO/S multi-layer film at $900^{\circ}C$. The memory window decreased to 1.32 V. Moreover, the TEM images confirmed that the thickness of multi-layer structure decreased 14.3% after annealing and the program conditions of A/TAlO/S multi-layer film decreased from 13 V to 11 V for 100 ms. Retention properties of both as-deposited and annealed films stably maintained until to $10^4$ cycles.

• Bulletin of the Korean Chemical Society
• /
• v.24 no.11
• /
• pp.1659-1663
• /
• 2003

$Al_2O_3$ thin films were grown on H-terminated Si(001) substrates using dimethylaluminum isopropoxide [DMAl: $(CH_3)_2AlOCH(CH_3)_2$], as a new Al precursor, and water by atomic layer deposition (ALD). The selflimiting ALD process by alternate surface reactions of DMAI and $H_2O$ was confirmed from measured thicknesses of the aluminum oxide films as functions of the DMAI pulse time and the number of DMAI-$H_2O$ cycles. Under optimal reaction conditions, a growth rate of ~1.06 ${\AA}$ per ALD cycle was achieved at the substrate temperature of $150\;^{\circ}C$. From a mass spectrometric study of the DMAI-$D_2O$ ALD process, it was determined that the overall binary reaction for the deposition of $Al_2O_3\;[2\;(CH_3)_2AlOCH(CH_3)_2\;+\;3\;H_2O\;{\rightarrow}\;Al_2O_3\;+\;4\;CH_4\;+\;2\;HOCH(CH_3)_2]$can be separated into the following two half-reactions: where the asterisks designate the surface species. Growth of stoichiometric $Al_2O_3$ thin films with carbon incorporation less than 1.5 atomic % was confirmed by depth profiling Auger electron spectroscopy. Atomic force microscopy images show atomically flat and uniform surfaces. X-ray photoelectron spectroscopy and cross-sectional high resolution transmission electron microscopy of an $Al_2O_3$ film indicate that there is no distinguishable interfacial Si oxide layer except that a very thin layer of aluminum silicate may have been formed between the $Al_2O_3$ film and the Si substrate. C-V measurements of an $Al_2O_3$ film showed capacitance values comparable to previously reported values.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.5
• /
• pp.273-277
• /
• 2018

This research introduces the sputtered IZO thin film transistor (TFT) with solution-processed $Al_2O_3$ diffusion layer. IZO is one of the most commonly used amorphous oxide semiconductor (AOS) TFT. However, most AOS TFTs have many defects that degrade performance. Especially oxygen vacancy in the active layer. In previous research, aluminum was used as a carrier suppressor by binding the oxygen vacancy and making a strong bond with oxygen atoms. In this paper, we use a solution-processed $Al_2O_3$ diffusion layer to fabricate stable IZO TFTs. A double-layer solution-processed $Al_2O_3$-sputtered IZO TFT showed better performance and stability, compared to normal sputtered IZO TFT.

• Korean Journal of Materials Research
• /
• v.12 no.7
• /
• pp.540-544
• /
• 2002

Hydration treatments were performed on the pure aluminum substrate at $100^{\circ}C$ followed by anodizing and heat treatments on the layers. The transformation behaviors of the oxide layers according to the hydration treatment were studied using TEM, XRD, RBS etc. Above $90^{\circ}C$ the hydrous oxide film could be formed, which were turned out to be hydrous oxides(AlOOH $nH_2$O). The anodization on the hydrous oxide film was more effective for the transition of amorphous anodic oxides to the crystalline $\Upsilon-Al_2$ $O_3$ comparing with the case for anodizing on the aluminum substrate without hydration treatment And additional heat treatments were also helpful for the acceleration of the transformation of the hydrous oxide to $\Upsilon-Al_2$ $O_3$. During the heat treatment the interface between $\Upsilon-Al_2$ $O_3$and the hydrous oxide layers migrated to the outer side of hydrous layer.

• Korean Journal of Materials Research
• /
• v.9 no.1
• /
• pp.25-29
• /
• 1999

We have developed a laser molecular beam epitaxy system for the layer-by-layer growth of oxide thin films. Using this system, we could grow and control oxide thin films of LaAlO$_3$in a molecular layer epitaxy mode on the atomically flat SrTiO$_3$ substrate with a LaAlO$_3$single crystal target. Very clear RHEED oscillations were observed during to growth of a LaAlO$_3$ film for a long period under the optimized conditions of substrate temperature at $650^{\circ}C$, oxygen pressure at 1$\times$10\ulcorner torr, and an incident laser fluence of 4.6J/$\textrm{cm}^2$. The height of mono-layer-LaAlO$_3$ film grown during one period of RHEED intensity oscillation was 3.8$\AA$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.7
• /
• pp.437-442
• /
• 2018

This work reports the preparation of Al-Ti based oxide thin films and their optical properties. Although the transmittance of a $TiO_2/Al2O_3$ bilayer structure was as high as 90% at wavelengths of 600 nm or larger, the reflectance of the bilayer reached its minimum at wavelengths of around 360 nm. The transmittance of an 89-nm-thick $TiO_2$ thin film rapidly increased and then decreased at a critical wavelength because of destructive interference. The wavelength corresponding to the reflectance minimum increased after an increase in $TiO_2$ film thickness. The smooth surface morphology of the AlTiO thin film was retained up to a film thickness of 65 nm, and the transmittance of the film was inversely proportional to film thickness, in accordance with the general tendency for optical films. The reflectance of the AlTiO film at visible light wavelengths was lower than that of the $TiO_2$ film, which implies that the AlTiO film is suitable for applications as an optical thin film layer in semitransparent solar cells.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.13 no.6
• /
• pp.581-588
• /
• 2013

This paper presents a study of the process temperature dependence of $Al_2O_3$ film grown by thermal atomic layer deposition (ALD) as a passivation layer in the crystalline Si (c-Si) solar cells. The deposition rate of $Al_2O_3$ film maintained almost the same until $250^{\circ}C$, but decreased from $300^{\circ}C$. $Al_2O_3$ film deposited at $250^{\circ}C$ was found to have the highest negative fixed oxide charge density ($Q_f$) due to its O-rich condition and low hydroxyl group (-OH) density. After post-metallization annealing (PMA), $Al_2O_3$ film deposited at $250^{\circ}C$ had the lowest slow and fast interface trap density. Actually, $Al_2O_3$ film deposited at $250^{\circ}C$ showed the best passivation effects, that is, the highest excess carrier lifetime (${\tau}_{PCD}$) and lowest surface recombination velocity ($S_{eff}$) than other conditions. Therefore, $Al_2O_3$ film deposited at $250^{\circ}C$ exhibited excellent chemical and field-effect passivation properties for p-type c-Si solar cells.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.6
• /
• pp.365-370
• /
• 2015

Zinc tin oxide transparent thin film transistors (ZTO TTFTs) were fabricated on oxidized $n^+$ Si wafers. The thickness of ~30 nm $Al_2O_3$ films were deposited on the oxidized Si wafers by atomic layer deposition, which acted as the gate insulators of ZTO TTFTs. The $Al_2O_3$ films were rapid-annealed at $400^{\circ}C$, $600^{\circ}C$, $800^{\circ}C$, and $1,000^{\circ}C$, respectively. Active layers of ZTO films were deposited on the $Al_2O_3/SiO_2$ coated $n^+$ Si wafers by rf magnetron sputtering. Mobility and threshold voltage were measured as a function of the rapid-annealing temperature. X-ray photoelectron spectroscopy (XPS) were carried out to observe the chemical bindings of $Al_2O_3$ films. The annealing effects of gate-insulator on the properties of TTFTs were analyzed based on the results of XPS.

• Applied Science and Convergence Technology
• /
• v.24 no.2
• /
• pp.33-40
• /
• 2015

$ZrO_2$ and Al-Zr composite oxide film was prepared by vacuum assisted sol-gel dip coating method and anodizing. $ZrO_2$ films annealed above $400^{\circ}C$ have tetragonal structure. $ZrO_2$ layers inside etch pits were successfully coated from the $ZrO_2$ sol. The double layer structures of samples were obtained after being anodized at 100 V to 600 V. From the TEM images, it was found that the outer layer was $Al_2O_3$, the inner layer was multi-layer of $ZrO_2$, Al-Zr composite oxide and Al hydrate. The capacitance of $ZrO_2$ coated foil exhibited about 28.3% higher than that of non-coating foil after being anodized at 100 V. The high capacitance of $ZrO_2$ coated foils anodized at 100 V can be attributed to the relatively high percentage of inner layer in total thickness. The electrical properties, such as withstanding voltage and leakage current of coated and non-coated Al foils showed similar values. From the results, $ZrO_2$ and Al-Zr composite oxide is promising to be used as the partial dielectric of high voltage capacitor to increase the capacitance.

• Journal of the Semiconductor & Display Technology
• /
• v.20 no.4
• /
• pp.157-160
• /
• 2021

As an insulator for a thin film transistor(TFT) and an encapsulation material of organic light emitting diode(OLED), aluminum oxide (Al₂O₃) has been widely studied using several technologies. Especially, in spite of low deposition rate, atomic layer deposition (ALD) has been used as a process method of Al₂O₃ because of its low process temperature and self-limiting reaction. In the Al₂O₃ deposition by ALD method, Ar Purge had some crucial effects on the film properties. After reaction gas is injected as a formation of pulse, an inert argon(Ar) purge gas is injected for gas desorption. Therefore, the process parameter of Ar purge gas has an influence on the ALD deposited film quality. In this study, Al₂O₃ was deposited on glass substrate at a different Ar purge time and its structural characteristics were investigated and analyzed. From the results, the growth rate of Al₂O₃ was decreased as the Ar purge time increases. The surface roughness was also reduced with increasing Ar purge time. In order to obtain the high quality Al₂O₃ film, it was known that Ar purge times longer than 15 sec was necessary resulting in the self-limiting reaction.