In order to look into the internal structure and the properties in the silicone rubbers added reinforcing fillers; silica $additives(O{\sim}140phr)$, and to examine the behavior of charged particles, the properties of thermally stimulated current(TSC) and X-Ray diffraction are investigated, respectively. And then, from the TSC which are formed by applying the electric field of $2{\sim}5kV/mm$ to specimen at the temperature range from -150 to $260^{\circ}C$, the results are as follwing: In the case of non-filled specimen, four peaks of ${\delta},\;{\gamma},\;{\beta}\;and\;{\alpha}$ are obtained at the temperature of $-120^{\circ}C,\;-60^{\circ}C,\;20^{\circ}C\;and\;130^{\circ}C$, respectively and the case of filled specimen, three peaks of ${\delta},\;{\alpha}_2\;and\;{\alpha}_1$ are observed at the temperature of $-120^{\circ}C,\;80^{\circ}C\;and\;130^{\circ}C$, respectively. The origins of these peaks are that, the ${\delta}$ peak seems to the result from the contribution of side chain methyl radical, and the ${\gamma}$ peak from the depolarization of space charge polarization owing to be added impurity during manufacturing specimens, and the ${\beta}$ peak from the orientation of $Si-CH_3$ dipole, and the ${\alpha}_2$ near the temperature of $80^{\circ}C$ from hydroxyl in carboxylic radical, and finally, the ${\alpha}_1$ peak near the temperature of $130^{\circ}C$ from carboxyl acid that is formed by the thermal oxidation of high temperature.