The purpose of this dissertation is to study some of the vulcanization characteristics of rubber-bound antioxidants such as G-1, [N-(3-methacryloyloxy-2-hydroxypropyl)-N'-phenyl-p-phenylene diamine] and acryl, acrylamide & acrylester substituted hindered phenols. The influence of these antioxidants upon vulcanization characteristics in NR and SBR compounds in the presence of vulcanizing accelerators such as MSA, TT, DM, M & D was evaluated by means of Oscillationg Disk Cure Meter. The comparison was also made between the influence of rubber-bound antioxidants and that of conventional non-reactive antioxidants such as N-alkyl substituted PADA series. Regarding the influence of reactive type antioxidant G-1 mixed with accelerator TT upon vulcanization characteristics, rapid onset of vulcanization and higher degree of cross-linking were discovered, whereas in the case of accelerator M and DM, the result was slow onset of vulcanization and lesser degree of cross-linking. The comparison of vulcanizing characteristics among acrylic substituted hindered phenols as antioxidants was made under several vulcanization accelerator systems. Under such systems, MSA-S combined accelerator caused the onset of vulcanization to slow down and lowered the degree of cross-linking. Finally in the case of hindered phenol derivatives containing longer substituent, the delayed onset of vulcanization and the lowered degree of cross-linking could be discerned.