Kim, Ki-Joo;Kim, Jong-Seok;Ahn, Byung-Kook;Suh, Soo-Kyo;Chang, Young-Jae;Kang, Kyoung-Ho
276
This study deals with both effects of inorganic fillers to vulcanized rubbers such as NR, CR, EPDM, NBR & SBR and inorganic characteristics of domestic fillers in comparision with hard clay produced in the USA. The results were as follows. 1. Main ingredient of domestic clay "Ha-dong clay" was Halloysite, "No-ha Island" was Pyrophyllite with $\alpha$-Quartz, and both of "Hard clay" & "Hwa-soon clay" were proved to be Kaolinite by XRD, DT-TGA and chemical analysis by XRF. 2. Tensile strength value of SBR compounded with these fillers, was Hard clay $146kg\;f/cm^2$, Kaolinite $123kg\;f/cm^2$, Pyrophyllite $82kg\;f/cm^2$, Halloysite $80kg\;f/cm^2$, precipitated $CaCO_3\;27kg\;f/cm^2$, and ground $CaCO_3$ was $21kg\;f/cm^2$. These results showed the increase of seven times according to filler species. 3. The physical properties of non-crystalline rubbers, such as SBR, NBR & EPDM, compared with NR & CR, have been considerably changed according to crystalline phase, particle size, shape and surface structure of fillers. Especially, tensile strength value in case of SBR & EPDM, was differentiated about 1.5 times by the particle size of fillers. 4. In SBR, physical properties of rubber compounded with Kaolinite which was surface treated with fatty acid and silane, almost approach to the value of hard clay. 5. Delayed cure time of Kaolinite and decrease of rubber properties by $CaCO_3$ can be improved by blending kaolinite & $CaCO_3$ in the ratio of 2:1.