We have studied the photoluminescence properties of undoped epitaxial layers of GaN on sapphire substrate grown by horizontal low pressure metal organic chemical vapor deposition method in the temperature range of 9-300 K. At 9 K the spectra are dominated by the well resolved interband free excitons A and B as well as bound excitons. Temperature dependence of free exciton transitions was studied and Varshni's coefficients for the temperature variation of bandgap were determined.

We have deposited Mn on Pd(oon) at RT up to 30 ML. LEED pattern changed from p($1{\times}1$) to c($2{\times}2$) order below 0.5 ML Mn deposition. During Mn deposition, we have not found any changes in the peak position and the intensity of LEED I/V curve. Using LEED I/V curve analysis for each coverage, we found atomic structure and surface composition of c($2{\times}2$) ordered Mn alloy on Pd(001) surface. Above 1 Ml Mn, in the first layer the Mn subplane lies above the Pd subplane by 0.32 ${\AA}$. This result is very different from the earlier result of Jona et al., who contended that after annealing at 200 for 2 min, a buckled first layer with the Mn subplane lower than the Pd subplane by 0.2 ${\AA}$.

Single crystal and polycrystalline Si thin films were doped with phosphorus by a 2-zone diffusion method to develop the low-resistivity polycrystalline Si electrode for a hemispherical grain. Solid phosphorus source was used in order to achieve uniformly and highly doped surface region of polycrystalline Si films having rough surface morphology. In case of 2-zone diffusion method, it is proved that the heavy doping near the surface area can be achieved even at a relatively low temperature. SIMS analysis revealed that phosphorus doping concentration in case of using solid P as a doping source was about 50 times as that of phosphine source at 750$^{\circ}C$. Also, ASR analysis revealed that the carrier concentration was about 50 times as that of phosphine. In order to evaluate the electrical characteristics of doped polycrystalline Si films for semiconductor devices, MOS capacitors were fabricated to measure capacitance of polycrystalline Si films. In ${\pm}$2 V measuring condition, Si films, doped with solid source, have 8% higher $C_{min}$ than that of unadditional doped Si films and 3% higher $C_{min}$ than that of Si films doped with $PH_3$ source. The leakage current of these films was a few fA/${\mu}m^2$. As a result, a 2-zone diffusion method is suggested as an effective method to achieve highly doped polycrystalline Si films even at low temperature.

We reprot on the fabrication and characterization of InGaN/GaN multiple quantum well light-emitting diode (LED) with a highly transparent Pt ohmic contact as a current spreading layer. The value of light transmittance of a Pt thin film with a thickness of 8 nm on-GaN was measured to be 85% at 450 nm. The peak wavelength and the full-width at half-maximum (FWHM) of the emission spectrum of the LED at 20 mA were 453 nm and 23 nm, respectively. Pt-contacted LEDs show good electrical properties and high light-output efficiency compared to Ni/Au-contacted ones. These results suggest that a Pt thin film can be used as an effective current spreading layer with high light-transparency.

The effects of $NH_3$ flow rate and reactor pressure on Al composition and the interface of AlGaN/GaN heterostructure were studied. Equilibrium partial pressure of Ga and Al over AiGaN alloy was calculated as a function of growth pressure, $NH_3$flow rate and temperature. It was found equilbrium vapor pressure of Al is significantly lower than that of Ga, thus, the alloy composition mainly controlled by Ga partial pressure. We believe that more decomposition of Ga occur at lower $NH_3$ flow rate and higher growth pressure leads to preferred Al incorporation into AlGaN. The alloy composition gradient became larger at AlGaN/GaN heterointerface at higher reactor pressures, higher Al composition and low $NH_3$ flow rate. This composition gradient lowered sheet carrier concentration and electron mobility as well. We obtained an AlGaN/GaN heterostructure with sheet carrier density of ${\sim}2{\times}10^{13}cm^{-2}$ and mobility of 1250 and 5000 $cm^2$/Vs at 300 K and 100 K, respectively.

ZnO : Al films were prepared through the optimization process of aluminum content and substrate temperature in rf-magnetron sputtering. When hydrogenation was performed on these films using a hot filament method, all films showed improvement in conductivity although more conductive film showed less improvement. When the substrate temperature ($T_H$) was varied from $25^{\circ}C\;to\;300^{\circ}C$ during hydrogenation, the resistivity was reduced more at higher $T_H$ (more than 30% at $T_H=300^{\circ}C$) Thus, two methods were developed to suppress the dehydrogenation in ZnO : Al films : (1) capping with amorphous silicon thin film as a diffusion barrier, and (2) cooling during hydrogenation.