Abstract
This study was to measure the minuteness structure, piezoelectric properties of (0.3-x)PMN- xPSS -0.7PZT+0.5[wt%]NiO+0.5(wt%)$MnO_2$ (x=0.05, 0.10, 0.15, 0.20, 0.25)ceramics according to sintering temp- erature and PSS(mol%) after manufacturing the specimens with a general method. the results of this study were gotten such as follows. The crystal structure of ceramic has the rombohedral structure in XRD. It appeared that addition of Ni, Mn additive was helpful to the formation of stable structure. The electrome- chanical coupling coefficient(kp) showed good properites on the whole, showed its maximum value 25.94[%] in specimens sintered at 1100[$^{\circ}C$], x=0.25mol. The mechanical quality coefficient(Qm) showed its maximum value 272.42 in specimens sintered at 1150[$^{\circ}C$], x=0.05mol. and was decreased by increasing PSS[mol%] The temperature coefficient of the resonant frequency(TCFr) showed stable properties in all sintering temperature with x=0.05mol. Especially good stability of 0.0054[%/$^{\circ}C$] showed in specimens sintered at 1100$^{\circ}C$, x=0.05mol.