• The Journal of the Korean dental association
• /
• v.51 no.1
• /
• pp.6-11
• /
• 2013

Dental ceramics is well known to have excellent esthetics, biocompatibility as well as high compressive strength. However, the fragility of ceramics against tensile and shear loads leading to the delayed fracture of micro crack on ceramic surface and the backwardness of ceramic fabrication technique limit the usage of ceramic materials in dentistry. Among all ceramic materials, zirconia has been introduced to overcome the drawback of conventional dental ceramics in the field of dentistry due to the nature of zirconia featuring proper opalescence and high fracture toughness. Also, novel manufacturing techniques enable ceramic materials to prepare high esthetic anterior and posterior all ceramic system. In this paper, it is introduced and discussed that novel techniques characterizing the bond strength between zirconia core and veneering ceramics and analyzing the fluorescence of dental ceramics in order to overcome the gap between the results of basic research and the feasibility of the results in the field of dental clinics.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.3
• /
• pp.319-325
• /
• 2013

PURPOSE. The objective of this study was to determine the effect of the color of a background substructure on the overall color of a zirconia-based all-ceramic crown. MATERIALS AND METHODS. Twenty one posterior zirconia crowns were made for twenty subjects. Seven premolar crowns and six molar crowns were cemented onto abutments with metal post and core in the first and second group. In the third group, eight molar crowns were cemented onto abutments with a prefabricated post and composite core build-up. The color measurements of all-ceramic crowns were made before try-in, before and after cementation. A repeated measure ANOVA was used for a statistical analysis of a color change of all-ceramic crowns at ${\alpha}$=.05. Twenty four zirconia specimens, with different core thicknesses (0.4-1 mm) were also prepared to obtain the contrast ratio of zirconia materials after veneering. RESULTS. $L^*$, $a^*$, and $b^*$ values of all-ceramic crowns cemented either on a metal cast post and core or on a prefabricated post did not show significant changes (P>.05). However, the slight color changes of zirconia crowns were detected and represented by ${\Delta}E{^*}_{ab}$ values, ranging from 1.2 to 3.1. The contrast ratios of zirconia specimens were 0.92-0.95 after veneering. CONCLUSION. No significant differences were observed between the $L^*$, $a^*$, and $b^*$ values of zirconia crowns cemented either on a metal cast post and core or a prefabricated post and composite core. However, the color of a background substructure could affect the overall color of posterior zirconia restorations with clinically recommended core thickness according to ${\Delta}E{^*}_{ab}$ values.

• Journal of Technologic Dentistry
• /
• v.43 no.2
• /
• pp.70-70
• /
• 2021

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.3
• /
• pp.312-319
• /
• 2009

Statement of problem: Delamination of veneering porcelain from underlying ceramic substructures has been reported for zirconia-ceramic restorations. Colored zirconia cores for esthetics have been reported that their bond strength with veneered porcelain is weaker compared to white zirconia cores. Purpose: This study aimed to investigate the shear bond strength by manufacturing the veneering porcelain on the colored zirconia core, using the layering technique and heat-pressing technique, and to evaluate the clinical stability by comparing the result of this with that of conventional metal ceramic system. Material and methods: A Metal ceramic (MC) system was tested as a control group. The tested systems were Katana zirconia with CZR (ZB) and Katana Zirconia with NobelRondo Press (ZP). Thirty specimens, 10 for each system and control, were fabricated. Specimen disks, 3 mm high and 12 mm diameter, were fabricated with the lost-wax technique (MC) and the CAD-CAM (ZB and ZP). MC and ZB specimens were prepared using opaque and dentin veneering ceramics, veneered, 3 mm high and 2.8 mm in diameter, over the cores. ZP specimens were prepared using heat pressing ingots, 3 mm high and 2.8mm in diameter. The shear bond strength test was performed in a Shear bond test machine. Load was applied at a cross-head speed of 0.50 mm/min until failure. Mean shear bond strengths (MPa) were analyzed with the One-way ANOVA. After the shear bond test, fracture surfaces were examined by SEM. Results: The mean shear bond strengths (SD) in MPa were MC control 29.14 (2.26); ZB 29.48 (2.30); and ZP 29.51 (2.32). The shear bond strengths of the tested systems were not significantly different (P > .05). All groups presented cohesive and adhesive failures, and showed predominance of cohesive failures in ceramic veneers. Conclusion: 1. The shear bond strengths of the tested groups were not significantly different from the control group (P >.05). 2. There was no significant different between the layering technique and the heat pressing technique in the veneering methods on the colored zirconia core. 3. All groups presented cohesive and adhesive failures, and showed predominance of cohesive failures in ceramic veneers.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.2
• /
• pp.199-205
• /
• 2009

Purpose: The purpose of this research was to evaluate the shear bond strength between zirconia core and veneer ceramic after surface treatment. Material and methods: Zirconia cores(N=40, n=10, $10mm{\times}10mm{\times}3mm$) were fabricated according to the manufacturers' instructions and ultrasonically cleaned. The veneering ceramics(thickness 3 mm) were built and fired onto the zirconia core materials. Four groups of specimens with different surface treatment were prepared. Group I: without any pre-treatment, Group II: treated with sandblasting, Group III: treated with liner, Group IV: treated with sandblasting and liner. The shear bond strength was tested in a universal testing machine. Data were compared with an ANOVA and $Scheff{\acute{e}}$ post hoc test(P=.05). Results: The shear bond strength of group VI was significantly higher than the other groups. Conclusion: Both mechanically and chemically treated simultaneously on zirconia core surface influenced the shear bond strength between the core and veneering ceramic in all-ceramic systems.

• The Journal of Advanced Prosthodontics
• /
• v.11 no.1
• /
• pp.65-74
• /
• 2019

PURPOSE. To evaluate and compare the effect of different materials and techniques on the shear bond strength of veneering ceramic materials to zirconia. MATERIALS AND METHODS. 136 sintered zirconia cubes were prepared and randomly divided into four study groups according to corresponding methods of surface treatment and materials: GLN (grinding followed by laser scanning using Noritake Cerabien ZR), SLN (sandblasting followed by laser scanning using Noritake Cerabien ZR), GLV (grinding followed by laser scanning using VITA VM 9), and SLV (sandblasting followed by laser scanning using VITA VM 9). Spraying technique was performed to coat the core. Profilometer, SEM, XRD, EDS, universal testing machine, and stereomicroscope were used to record surface roughness Ra, surface morphology, phase transformation, elemental compositions, shear bond strength SBS values, and failure types, respectively. Specimens were investigated in unaged (not immersed in artificial saliva) and aged (stored in artificial saliva for a month) conditions to evaluate SBS values. RESULTS. Grinding and GLN as first and second surface treatments provided satisfactory Ra values in both conditions ($1.05{\pm}0.24{\mu}m$, $1.30{\pm}0.21{\mu}m$) compared to sandblasting and other groups (P<.05). The group GLN showed the highest SBS values in both conditions ($30.97{\pm}3.12MPa$, $29.09{\pm}4.17MPa$), while group SLV recorded the lowest ($23.96{\pm}3.60MPa$, $22.95{\pm}3.68Mpa$) (P<.05). Sandblasting showed phase transformation from t-m. Mixed failure type was the commonest among all groups. CONCLUSION. GLN showed to be a reliable method which provided satisfactory bond strength between the veneer ceramic and zirconia. This method might preserve the integrity of fixed dental crowns.

• The Journal of Advanced Prosthodontics
• /
• v.10 no.2
• /
• pp.101-112
• /
• 2018

PURPOSE. The purpose of this study was to investigate the effect of various surface treatments (ST) on the shear bond strength of resin composite to three bilayer dental ceramics made by CAD/CAM and two veneering ceramics. MATERIALS AND METHODS. Three different bilayer dental ceramics and two different veneering ceramics were used (Group A: IPS e.max CAD+IPS e.max Ceram; Group B: IPS e.max ZirCAD+IPS e.max Ceram, Group C: Vita Suprinity+Vita VM11; Group D: IPS e.max Ceram; Group E: Vita VM11). All groups were divided into eight subgroups according to the ST. Then, all test specimens were repaired with a nano hybrid resin composite. Half of the test specimens were subjected to thermocycling procedure and the other half was stored in distilled water at $37^{\circ}C$. Shear bond strength tests for all test specimens were carried out with a universal testing machine. RESULTS. There were statistically significant differences among the tested surface treatments within the all tested fracture types (P<.005). HF etching showed higher bond strength values in Groups A, C, D, and E than the other tested ST. However, bonding durability of all the surface-treated groups were similar after thermocycling (P>.00125). CONCLUSION. This study revealed that HF etching for glass ceramics and sandblasting for zirconia ceramics were adequate for repair of all ceramic restorations. The effect of ceramic type exposed on the fracture area was not significant on the repair bond strength of resin composites to different ceramic types.

• The Journal of Advanced Prosthodontics
• /
• v.4 no.3
• /
• pp.162-169
• /
• 2012

PURPOSE. Fracture of the veneering material of zirconia restorations frequently occurs in clinical situations. The purpose of this in vitro study was to compare the fracture strengths of zirconia crowns veneered with various ceramic materials by various techniques. MATERIALS AND METHODS. A 1.2 mm, $360^{\circ}$ chamfer preparation and occlusal reduction of 2 mm were performed on a first mandibular molar, and 45 model dies were fabricated in a titanium alloy by CAD/CAM system. Forty-five zirconia copings were fabricated and divided into three groups. In the first group (LT) zirconia copings were veneered with feldspathic porcelain by the layering technique. In the second group (HT) the glass ceramic was heat-pressed on the zirconia coping, and for the third group (ST) a CAD/CAM-fabricated high-strength anatomically shaped veneering cap was sintered onto the zirconia coping. All crowns were cemented onto their titanium dies with Rely $X^{TM}$ Unicem (3M ESPE) and loaded with a universal testing machine (Instron 5583) until failure. The mean fracture values were compared by an one-way ANOVA and a multiple comparison post-hoc test (${\alpha}$= 0.05). Scanning electron microscope was used to investigate the fractured interface. RESULTS. Mean fracture load and standard deviation was $4263.8{\pm}1110.8$ N for Group LT, $5070.8{\pm}1016.4$ for Group HT and $6242.0{\pm}1759.5$ N for Group ST. The values of Group ST were significantly higher than those of the other groups. CONCLUSION. Zirconia crowns veneered with CAD/CAM generated glass ceramics by the sintering technique are superior to those veneered with feldspathic porcelain by the layering technique or veneered with glass ceramics by the heat-pressing technique in terms of fracture strength.

• The Journal of Korean Academy of Prosthodontics
• /
• v.48 no.2
• /
• pp.151-157
• /
• 2010

Purpose: The purposes of this study was to evaluates shear bond strength between zirconia core and veneer-ceramic in order to examine the clinical practice of colored zirconia block fabricated by infiltration method into the metal chloride solution. Material and methods: CNU block and $Everest{(R)}$ ZS blank were used. VITA In-$Ceram{(R)}$2000 YZ Coloring liquid (LL1) and 3 aqueous metal chloride solutions containing chromium and molybdenum ingredients were used. 40 zirconia specimens were prepared into cuboid shape ($5{\times}5{\times}10 mm$). All specimens were divided into 5 groups by infiltrating into the coloring liquids. After that, porcelain was build up into the shape of $5{\times}5{\times}4mm^3$, followed by sintering. The maximum loading and shear bond strength was measured. Failure patterns and failure sites were examined. Results: 1. There were no statistical differences in shear bond strength between zirconia blocks (P > .05). 2. There were no statistically significant differences in shear bond strength between non-colored and colored zirconia blocks, while shear bond strength of non-colored zirconia blocks is higher than that of colored specimen (P > .05). 3. In the comparison with shear bond strength among colored zirconia blocks, there were no statistical differences according to kinds of coloring liquid (P > .05). 4. Mixed failure patterns were mainly observed in the failure between zirconia and veneering ceramic. The veneering ceramic failure of all specimens was observed in either interface of zirconia or veneering ceramic. Conclusion: Shear bond strength between colored zirconia and veneering ceramic shows lower tendency than non-colored zirconia, but there was clinically allowable value.

• Journal of Korean Dental Science
• /
• v.8 no.1
• /
• pp.28-35
• /
• 2015

Purpose: To investigate the influence of crown margin design on the stress distribution and to localize critical sites in maxillary canine under functional loading by using three dimensional finite element analysis. Materials and Methods: The bite force of 100 N, 150 N, and 200 N was applied with an angulation of $45^{\circ}$ to the longitudinal axis of tooth. Six models were restored with IPS e.max (Ivoclar Vivadent, Schaan, Liechtenstein) with a different margin design. With lingual ledge and various thicknesses, three different core ceramics were designed in each model. Result: In the core ceramic, the maximum tensile stresses were found at the labiocervical region. In the veneering ceramic the maximum tensile stresses were found at the area where the force was applied in all models. Conclusion: Shoulder and chamfer margin types are acceptable for all-ceramic rehabilitations. A ledge on the core ceramic at cervical region may affect the strength of all-ceramic crowns.