• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.847-854
• /
• 1994

An amorphous single phase and coexistent amorphous and hcp-Mg phases in Mg-Zn-Ce system were found to form in the composition ranges of 20 to 40% Zn, 0 to 10% Ce and 5 to 20% Zn, 0 to 5% Ce, respectively. A $Mg_{85}Zn_{12}Ce_{3}$ amorphous alloy containing nanoscale hcp-Mg particles was found to form either by melt spinning or by heat treatment of melt -spun ribbon. The particle size of the hcp-Mg phase can be controlled in the range of 4 to 20 nm. The mixed phase alloy prepared thus has a good bending ductility and exhibits high ultimate tensile strength($\sigma_{B}$) ranging from 670 to 930 MPa and fracture elongation($\varepsilon_{f}$) of 5.2 to 2.0%. The highest specific strength($\sigma_{B}$/density =$\sigma_{s}$)$3.6 \times 10^5N \cdot m/kg$. It should be noted that the highest values of flB, US and ？1 are considerably higher than those (690MPa,$2.5 \times 10^5N \cdot m/kg$and 2.5%) for amorphous Mg-Zn-Ce alloys. The increase of the mechanical strengths by the formation of the mixed phase structure is presumably due to a dispersion hardening of the hcp supersaturated solution which has the hardness higher than that of the amorphous phase with the same composition.

• Journal of the Korea Concrete Institute
• /
• v.25 no.4
• /
• pp.447-455
• /
• 2013

In this study, reinforced concrete slabs with steps were experimentally studied to analyze their structural performance and to suggest reinforcing details in the step. Because the stepped slabs may behave very poorly in terms of bending strength, stiffness, deflection, cracking, etc., the study is aimed to suggest proper reinforcing details such that the same bending strength is obtained as that without steps. The bending strengths of 12 test specimens with a variety of different reinforcing detail types or other parameters were compared with each other. The specimen without any additional reinforcement in the step had a very low bending strength and significant damage, and the specimens with diagonal reinforcements in the step showed substantial early cracks, experienced hinging of the step, and had a substantial loss of the bending strength. In contrast, the specimens with a combination of U-bars, reversed U-bars, L-bars, and reversed L-bars performed very well and almost reached to 100% of the slab bending strength. The U-bars and reversed U-bars were effective in controling the diagonal cracks, while the L-bars and reversed L-bars were effective in preventing from yielding of slab reinforcement near the step.

• Journal of Korean Society of Steel Construction
• /
• v.24 no.5
• /
• pp.535-547
• /
• 2012

PSRC column is a concrete encased steel angle column. In the PSRC column, the steel angles placed at the corner of the cross-section resists bending moment and compression load. The lateral re-bars welded to steel angles resist the column shear and the bond between the steel angle and concrete. In the present study, current design procedures in KBC 2009 were applied to the flexure-compression, shear, and bond design of the PSRC composite column. To verify the validity of the design method and failure mode, simply supported 2/3 scaled PSRC and correlated SRC beams were tested under two point loading. The test parameters were the steel angle ratio and lateral bar spacing. The test results showed that the bending, shear, and bond strengths predicted by KBC 2009 correlated well with the test results. The flexural strength of the PSRC specimens was much greater than that of the SRC specimen with the same steel ratio because the steel angles were placed at the corner of the column section. However, when the bond resistance between the steel angle and concrete was not sufficient, brittle failures such as bond failure of the angle, spalling of cover concrete, and the tensile fracture of lateral re-bar occurred before the development of the yield strength of PSRC composite section. Further, if the weldability and toughness of the steel angle were insufficient, the specimen was failed by the fracture of the steel angle at the weld joint between the angle and lateral bars.

• Journal of the Korea Concrete Institute
• /
• v.22 no.4
• /
• pp.473-479
• /
• 2010

The objective of the paper is to experimentally investigate the effect of commercially avaliable fiber types such as polypropylene (PP), nylon (NY), polyvinyl alcohol (PVA) and cellulose (CL) on the engineering properties of concrete for pavement application. The results, showed the fluidity tends to decrease with fibers addition compared to that of plain concrete. As for the effect of fiber types on fluidity loss, use of NY appear to give the most favorable results among all of the fiber types investigated in this study while the effect of the fibers on air content was negligible. For the properties of hardened concrete, compressive and flexural strengths increased with fibers compared to plain concrete. The contribution of NY fibers to strength was the highest followed in the order by NY, PVA, PP, and CL. However, in the case of the splitting tensile strength, its values were increased with NY and PP only. For porosity based on MIP(mercury intrusion penetration) method, the number of around 1 was observed when NY was mixed resulting in increased cumulated amounts of porosity compared with that of plain mix. Thus, based on the consideration of fluidity and strength it was found that the addition of NY fiber showed the optimal results under the conditions applied in this study.

• Journal of the Korea Concrete Institute
• /
• v.16 no.5 s.83
• /
• pp.651-657
• /
• 2004

The effects of polymer-cement ratio, antifoamer content and shrinkage-reducing agent content on the air content, setting time, drying shrinkage and strength of high-fluidity polymer-modified mortars using redispersible polymer powder are examined. As a result, the air content of the polymer-modified mortars using redispersible polymer powder tends to decrease nth increasing polymer-cement ratio and antifoamer content. Regardless of the antifoamer content, the setting time of the polymer-modified mortars using redispersible polymer powder tends to delayed with increasing polymer-cement ratio. Irrespective of the antifoamer content, the drying shrinkage of the polymer-modified mortars using redispersible polymer powder tend to decrease with increasing polymer-cement ratio and shrinkage-reducing agent content. Regardless of the antifoamer content, the flexural and tensile strengths of the polymer-modified mortars using redispersible polymer powder tends to increase with increasing polymer-cement ratio, and tend to decrease with increasing shrinkage-reducing agent content. However, the compressive strength of the polymer-modified mortars using redispersible polymer powder decreases with increasing polymer-cement ratio and shrinkage-reducing agent content.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.5
• /
• pp.1765-1775
• /
• 2013

The application of FRP wire as a mean of improving strength and ductility capacity of concrete cylinders under axial compressive load through confinement is investigated experimentally in this study. An experimental investigation involves axial compressive test of three confining amounts of FRP wire and three concrete compressive strengths. The effectiveness of FRP wire confinement on the concrete microstructure were examined by evaluating the internal concrete damage using axial, circumferential, and volumetric strains. The axial stress-strain relations of FRP wire confined concrete showed bilinear behavior with transition region. It showed strain-hardening behavior in the post-cracking region. The load carrying capacity was linearly increased with increasing of the amount of FRP wire. The ultimate strength of the 35 MPa specimen confined with 3 layer of FRP wire was increased by 286% compared to control one. When the concrete were effectively confined with FRP wire, horizontal cracks were formed by shearing. It was developed from sudden expansion of the concrete due to confinement ruptures at one side while the FRP wire was still working in hindering expansion of concrete at the other side of the crack. The FRP wire failure strains obtained from FRP wire confined concrete tests were 55~90%, average 69.5%, of the FRP wire ultimate uniaxial tensile strain. It was as high as any other FRP confined method. The magnitude of FRP wire failure strain was related to the FRP wire effectiveness.

• Korean Journal of Materials Research
• /
• v.28 no.4
• /
• pp.254-259
• /
• 2018

General D-glass(Dielectric glass) fibers are adaptable to PCBs(Printed circuit boards) because they have a low dielectric constant of about 3.5~4.5. However, very few papers have appeared on the physical characteristics of D-glass fibers. D-glass fibers were fabricated via continuous spinning process using bulk D-glass. In order to fabricate the D-glass, raw materials were put into a Pt crucible, melted at $1650^{\circ}C$ for 2 hrs, and then annealed at $521{\pm}10^{\circ}C$ for 2 hrs. We obtained transparent clear glass. The transmittance and adaptable temperature for spinning of the bulk marble glass were characterized using a UV-visible spectrometer and a viscometer. Continuous spinning was carried out using direct melting spinning equipment as a function of the fiberizing temperature in the range of $1368^{\circ}C$ to $1460^{\circ}C$, while the winder speed was between 100 rpm and 200 rpm. We investigated the physical properties of the D-glass fibers. The average diameters of the glass fibers were measured by optical microscope and FE-SEM. The average diameters of the D-glass fibers were 21.36 um at 100 rpm and 34.06 um at 200 rpm. The mechanical properties of the fibers were confirmed using a UTM(Universal materials testing machine). The average tensile strengths of the D-glass fibers were 467.03 MPa at 100 rpm and 522.60 MPa at 200 rpm.

• Journal of the Korea Concrete Institute
• /
• v.17 no.1 s.85
• /
• pp.69-76
• /
• 2005

In this study, the high qualify recycled fine aggregate manufacturing system by the drying specific gravity separation method was evaluated. For the evaluation of the performance of the recycled aggregate, the engineering properties and durability of recycled aggregate has been tested. From the test results, the quality of recycled fing aggregates was improved by high quality recycled fine aggregate manufacturing system and satisfied with the quality standards of KS and JASS 5. Also, compressive and tensile strengths of recycled concrete show no critical difference caused by recycled fine aggregate replacement ratio. However, durability such as carbonation depth chloride ion penetration depth and drying shrinkage shows more deterioration than the concrete without recycled fine aggregate

• Composites Research
• /
• v.12 no.3
• /
• pp.8-16
• /
• 1999

Carbon woven fabric/C/SiC composites were fabricated by multiple impregnations of carbon woven fabric/carbon preform with the polymer precursor of SiC, i.e., polycarbosilane. In addition, two kinds of low density carbon/carbon preforms which had different fiber volume fraction and fiber orientation, i.e., a carbon woven fabric(${\thickapprox}$55 vol%)/carbon and a chopped carbon fiber${\thickapprox}$40 vol%)/carbon composites, were reaction-bonded with a silicon melt at 1$700^{\circ}C$ in a vacuum to fabricate dense carbon fiber/Si/SiC composites. The reaction-bonding process increased the density to ~2.1 g/$cm^3$ from 1.6 g/$cm^3$ and 1.15 g/$cm^3$ of a carbon woven and a chopped carbon preforms, respectively. All of the composites fractured with extensive fiber pull-out. The higher the density the higher the stiffness and proportional limit stress. The mechanical properties obtained from a three-point bend and tension tests were compared. The ratios of the peak tensile stresses to the bending strengths of a carbon woven and a chopped carbon composites were about one-third, respectively. The carbon woven fabric/Si/SiC composites with density of 2.06 g/$cm^3$ showed ~120 MPa of ultimate strength and ~80 MPa of proportional limit in bend testing.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.7
• /
• pp.735-742
• /
• 2014

A self-piercing rivet (SPR) is a mechanical component for joining dissimilar material sheets such as those of aluminum alloy and steel. Unlike conventional rivets, the SPR directly pierces sheets without the need for drilling them beforehand. However, the regular SPR can undergo buckling when it pierces a high-strength steel sheet, warranting the design of a helical SPR. In this study, the joining and forging processes using the helical SPR were simulated using the commercial FEM code, DEFORM-3D. High-tensile-strength steel sheets of different strengths were joined with aluminum alloy sheets using the designed helical SPR. The simulation results were found to agree with the experimental results, validating the optimal design of a helical SPR that can pierce high-strength steel sheets.