• Nuclear Engineering and Technology
• /
• v.55 no.2
• /
• pp.575-579
• /
• 2023

In this work, pure W and W-0.5wt%HfC alloy (WHC05) were fabricated by sintering and hot-rolling following the same processing route. After exposing to a high flux deuterium plasma irradiation with the D⁺ flux to three fluences of 6.00 × 10²⁴, 2.70 × 10²⁵ and 7.02 × 10²⁵ D/m², the evolution of surface morphology, deuterium retention and hardening behaviors in pure W and WHC05 has been studied. The SEM results show the formation of D blisters on the irradiated area, and with the increase of D implantation, the size of these blisters increases from 200 ~ 500 nm (2.70 × 10²⁵ D/m²) to 1 ~ 2 ㎛ (7.02 × 10²⁵ D/m²) in WHC05 and from 1 ~ 2 ㎛ (2.70 × 10²⁵ D/m²) to > 3 ㎛ (7.02 × 10²⁵ D/m²) in pure W, respectively. A higher D retention and obvious hardening are observed in pure W than that of the WHC05 alloy, indicating an improve radiation resistance in WHC05 compared to pure W.

• Journal of Navigation and Port Research
• /
• v.37 no.3
• /
• pp.257-262
• /
• 2013

A ship operating in rough sea may suffer from an undesirable motion which may severely degrade the performance of equipment onboard and give a person an uncomfortable feeling. Hence, roll stabilization received a considerable attention and various devices including bilge keels, stabilizing fins, gyroscopic, anti-rolling tanks, rudders and flaps have been conceived and utilized for the purpose. The Coanda effect is evident when a jet stream is applied tangential to a curved surface of a hydrofoil since then the jet increases the circulation around the foil and consequently the lift. Model tests and numerical simulation have been conducted to examine the practicality of a fixed type fin stabilizer augmented by the Coanda jet. The results show that the lift coefficient of the modified Coanda fin at the zero angle of attack identically coincides with that of the original fin at ${\alpha}=\26^{\circ}$ when Coanda jet is supplied at the rate of $C_j$ = 0.25. It is also shown that fixed type fin stabilizers for active control of the motions of ships and the other mobile units without rotation can be put to practical use if the Coanda effect is applied.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.57-58
• /
• 2006

The effects of lowering ECAP temperature during ECAP process and Post-ECAP annealing on microstructure, texture and mechanical properties of the AZ31 alloys have been investigated in the present study. The as-extruded materials were ECAP processed to 2 passes at 553K prior to subsequent pressing up to 6 passes at 523K or 493K. When this method of lowering ECAP temperature during ECAP was used, the rods could be successfully deformed up to 6 passes without any surface cracking. Grain refinement during ECAP process at 553K might have helped the material to endure further straining at lower deformation temperatures probably by increasing the strain accommodation effect by grain boundary sliding, causing stress relaxation. Texture modification during ECAP has a great influence on the strength of Mg alloys because HCP metals have limited number of slip systems. As slip is most prone to take place on basal planes in Mg at room temperature, the rotation of high fraction of basal planes to the directions favorable for slip as in ECAP decreases the yield stress appreciably. The strength of AZ31 Mg alloys increases with decrease of grain size if the texture is constant though ECAP deformation history is different. A standard positive strength dependence on the grain size for Mg alloys with the similar texture (Fig. 1) supports that the softening of ECAPed Mg alloys (a negative slope) typically observed despite the significant grain refinement is due to the texture modification where the rotation of basal planes occurs towards the orientation for easier slip. It could be predicted that if the original fiber texture is restored after ECAP treatment yielding marked grain refinement, yield stress as high as 500 MPa will be obtained at the grain size of ${\sim}1{\mu}m$. Differential speed rolling (DSR) with a high speed ratio between the upper and lower rolls was applied to alter the microstructure and texture of the AZ31 sheets. Significant grain refinement took place during the rolling owing to introduction of large shear deformation. Grain size as small as $1.4{\mu}m$ could be obtained at 423K after DSR. There was a good correlation between the (0002) pole intensity and tensile elongation. This result indicates that tensile ductility improvement in the asymmetrically rolled AZ31 Mg alloys is closely related to the weakening of basal texture during DSR. Further basal texture weakening occurred during annealing after DSR. According to Hall-Petch relation shown in Fig. 1, the strength of the asymmetrically rolled AZ31 is lower than that of the symmetrically rolled one when compared at the same grain size. This result was attributed to weakening of fiber texture during DSR. The DSRed AZ31, however, shows higher strength than the ECAPed AZ31 where texture has been completely replaced by a new texture associated with high Schmid factors.

• Journal of Korea Foundry Society
• /
• v.36 no.3
• /
• pp.81-87
• /
• 2016

In this study, the effect of scrap ratio on the mechanical properties of Zr alloys was studied. Oxygen content in the ingot cake increased rapidly with increasing fraction of scrap, which can be attributed to the surface oxide of scrap including small pieces of turning, chips, etc. Iron content did not increase much with the increasing addition of scrap, suggesting scrap materials was well reserved in the iron-free container. As-cast structure of Zr alloy with the scrap:sponge ratio displayed plate/or needle ${\alpha}$ phase and no appreciable change of the cast structure was observed with change of scrap fraction. The strength increases with increasing fraction of scrap, which can be attributed to the increase of oxygen content. The ductility decreased slightly with increase of scrap fraction. Dislocation-oxygen interaction is known to increase the strength at the expense of ductility. Ingot cake with intentionally added $Fe_2O_3$ exhibited the drastic decrease of the formability, even exhibited the brittle fracture behavior during rolling. The oxidation resistance, however, increased with the increase of scrap fraction because of high oxygen content, which may prevent more penetration and diffusion of oxygen into matrix.

• Corrosion Science and Technology
• /
• v.15 no.3
• /
• pp.141-146
• /
• 2016

By using Ni-Cr and Co-Cr alloys, porcelain fused to metal (PFM) samples were prepared to examine the interface and the surface corrosion behavior. The potentiodynamic polarization analysis showed that the corrosion current density of Co-Cr alloy ($1.61{\times}10^{-6}A/cm^2$) was three times lower than that of Ni-Cr alloy ($4.83{\times}10^{-6}A/cm^2$) at room temperature. A dental prosthesis consisting of the porcelain fused to Ni-Cr alloy extracted from a patient after approximately four years of usage was examined to assess its resistance to corrosion. OM and SEM images of the metal part revealed a typical pitting corrosion. As compared to porcelain fused to Ni-Cr alloy having a thick layer (${\sim}10{\mu}m$) of oxide at the interface, a relatively thin oxide layer (less than $5{\mu}m$) was formed on Co-Cr alloy, indicating that the interface between Co-Cr alloy and porcelain may have a better adhesion strength than the interface between Ni-Cr alloy and porcelain.

• Korean Journal of Materials Research
• /
• v.24 no.11
• /
• pp.585-590
• /
• 2014

Microstructural evolution in the thickness direction of an oxygen free copper processed by accumulative rollbonding (ARB) is investigated by electron back scatter diffraction (EBSD) measurement. For the ARB, two copper alloy sheets 1 mm thick, 30 mm wide and 300 mm long are first degreased and wire-brushed for sound bonding. The sheets are then stacked and roll-bonded by about 50% reduction rolling without lubrication at an ambient temperature. The bonded sheet is then cut to the two pieces of the same dimensions and the same procedure was repeated on the sheets up to eight cycles. The specimen after 1 cycle showed inhomogeneous microstructure in the thickness direction so that the grains near the surface were finer than those near the center. This inhomogeneity decreased with an increasing number of ARB cycles, and the grain sizes of the specimens after 3 cycles were almost identical. In addition, the aspect ratio of the grains decreased with an increasing number of ARB cycles due to the subdivision of the grains by shear deformation. The fraction of grains with high angle grain boundaries also increased with continuing process of the ARB so that it was higher than that of the low angle grain boundaries in specimens after 3 cycles. A discontinuous dynamic recrystallization occurred partially in specimens after 5 cycles.

• Journal of the Korean Society for Railway
• /
• v.11 no.2
• /
• pp.188-194
• /
• 2008

Brake disks for rolling stock are exposed to thermal fatigue during braking, and thermal cracks occur on surface of disks. Thermal cracks can cause serious accidents, deterioration of braking performance and increase of maintenance cost due to frequent exchange of friction materials. In this study, candidate materials with high-heat resistance were selected by searching the literature. By using cast specimens made of the candidate materials, chemical composition, crystal structure and graphite type were analyzed. In addition, friction coefficient and wear were measured and compared with values for the disk material in service. As a result, it was shown that the NiCrMo has highest tensile strength and lowest friction coefficient and the disk material in service has the most stable friction characteristics.

• Bulletin of the Society of Naval Architects of Korea
• /
• v.21 no.1
• /
• pp.3-12
• /
• 1984

Up to now, it has been common to treat the maneuvering motion of a ship as a 3-degree-freedom motion i.e. surge, sway and yaw on the sea surface, for the simplicity and mathematical calculation, and it is quite acceptable in the practical point of view. Meanwhile, considering the maneuverability of a ship under the special conditions such as in irregular waves, in wind or at high speed with small GM value, it is required that roll effect must be considered in the equation of ship motion. In this paper the author tried to build up the 4-degree-freedom motion equation by adding roll. And then, applying the M.M.G.'s mathematical model and with captive model test results the roll-coupled hydrodynamic derivatives were found. With these the author could make some simulating program for turning and zig-zag steering. Through the computer simulations, the effect of roll to the ship maneuver became clear. The effect of the wind force to the maneuverability was also found. Followings are such items that was found. 1) When roll is coupled in the maneuvering motion, the directional stability becomes worse and the turning diameter becomes smaller as roll becomes smaller as roll becomes larger. 2) When maneuver a ship in the wind, the roll becomes severe and the directional stability becomes worse. 3) When a ship turns to the starboard side, the wind blowing from 90 degree direction to starboard causes the largest roll and the largest turning diameter, and the wind from other direction doesn't change the turning diameter. 4) When a ship is travelling with a constant speed with rudder amidship, if steady wind blows from one direction, the ship turns toward that wind. This phenomenon is observed in the actual seaways.

• Journal of the Korean Society of Fashion and Beauty
• /
• v.4 no.4 s.10
• /
• pp.63-74
• /
• 2006

The purpose of the study was to investigate unique field of formative characteristics using copper wire, the present thesis aims at developing concept of hair art as a creative way, and recognizing the formative characteristics of copper wire as analyze and arrange the concept of hair art, formative, a way of practical application, material aspect, through literature, academic journals, photo data, and researched about prior piece, for example, architecture and costume with hair art, and then pieces of hair art were made. Influenced by the theory, applied the social phenomenon and the formative principles, produced the seven pieces which includes flying, composure, yahoo, harmony, balance, way, spring etc. The results of this research are outlined below. Firstly, It showed that the copper wire can express the mysterious and beautiful formative world, and it could know the possibility of design. Secondly, formative activity using copper wire can differ according to approach and interpretation, and it can be a works with aesthetic value. Thirdly, hair could be express the art of the three-dimensional forms which constitute the mixture of line, surface and space. Fourthly, the handicraft including beading, pleat, piping, rolling that used for works are proper to express the unique formative and the rich colors, and it can also express the transparency. So it showed that copper wire is a proper materials. So, hair art has enlarged the fields with development of technique, and changed to recognition of the hair art, and opened up a new field. Hair art will be positive fields to maximize the possibility, and not only the beauty artist but also the public will be communicate each other.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.9
• /
• pp.1043-1048
• /
• 2014

As micro screws feature reduced screw lengths and pitches, the resulting clamping force diminishes because of the reduced length of the actual joints. The elements of the clamping force are material, geometry, and friction. We studied the shrinking size of the screw and the methods to improve the clamping force by changing the material. We developed a micro screw using SWCH18A and SUS XM7 materials, and obtained the precision and thickness of the pitch through three-dimensional measurement. We also measured the external resistance of the micro screw by applying the Vicker's hardness test and conducted a break surface analysis using a break torque test and SEM for obtaining the break characteristics.