• Journal of the Korean Association of Oral and Maxillofacial Surgeons
• /
• v.39 no.6
• /
• pp.269-273
• /
• 2013

Objectives: This study is designed to evaluate the mechanical stability of orthodontic mini-implants with vertical grooves in rabbits. Materials and Methods: This study was done from March 2011 to February 2012 in Dental Research Institute of Seoul National University. Thirty-two mini-implants in the control group and 32 in the rotation bump (RB) group were inserted in the tibias of 16 rabbits and were removed after two weeks and four weeks, respectively. The maximum insertion torque (MIT), maximum removal torque (MRT), torque ratio (TR) of MRT to MIT and removal angular momentum (RAM) were all measured at the time of removal. Results: There were no significant differences between the two groups in MIT and MRT at two weeks or four weeks. However, TR and RAM at four weeks in the RB group were significantly higher than in the control group (P<0.05). TR of the RB group was significantly increased at four weeks (P<0.05). In both groups, RAM at four weeks was significantly higher than at two weeks (P<0.05). Conclusion: These results suggest that RB of the mini-implant could provide resistance to the removal rotation, although it did not increase the MRT.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.2
• /
• pp.164-173
• /
• 2009

Purpose: The purpose of this study was to evaluate the effect of abutment material on screw-loosening before and after cyclic loading. Among the different materials of abutments, zirconia and metal abutment were used. Material and methods: Two types of implant systems: external butt joint(US II, Osstem Implant, Korea) and internal conical joint(GS II, Osstem Implant, Korea) were used. In each type, specimens were divided into two different kinds of abutments: zirconia and metal(n=5). The implant was rigidly held in a special holding to device ensure fixation. Abutment was connected to 30 Ncm with digital torque gauge, and was retightened in 30 Ncm after 10 minutes. The initial removal torque values were measured. The same specimens were tightened in 30 Ncm again and held in the cycling loading simulator(Instron, USA) according to ISO/FPIS 1480. Cycling loading tests were performed at loads 10 to 250 N, for 1 million cycles, at 14 Hz,(by subjecting sinusoidal wave from 10 to 250 N at a frequency of 14 Hz for 1 million cycles,) and then postload removal torque values were evaluated. Results: 1. In all samples, the removal values of abutment screw were lower than tightening torque values(30 Ncm), but the phenomenon of the screw loosening was not observed. 2. In both of the implant systems, initial and postload removal torque of zirconia abutment were significantly higher than those of metal abutment(P<.05). 3. In both of the implant systems, the difference in removal torque ratio between zirconia abutment and metal abutment was not significant(P>.05). 4. In metal abutments, the removal torque ratio of GS II system(internal conical joint system) was lower than that of US II system(external butt joint system)(P<.05). 5. In zirconia abutments, the difference in removal torque ratio between the two implant systems was not significant(P>.05). Conclusion: Zirconia abutment had a good screw joint stability in the condition of one million cycling loading.

• Journal of Periodontal and Implant Science
• /
• v.28 no.3
• /
• pp.401-408
• /
• 1998

Screw shaped implants of Titanium-13Zirconium-6Niobium(newly developed), Titanium-6Zirconium-6Sn-6Niobium(newly developed) and Titanium-6Aluminum-4Vanadium were machined with square top and inserted in rabbit bone for 3 months. Biomechanical tests(removal torque) showed Titanium-13Zirconium-6Niobium and Titanium-6Zirconium-6Sn-6Niobium to be more stable in the bone bed than those of Titanium-6Aluminum-4Vanadium. Titanium-13Zirconium-6Niobium implants demonstrated a mean removal torque of 31.59Ncm while Titanium-6Aluminum-4Vanadium demonstrated a mean removal torque of 25.27Ncm and Titanium-6Zirconium-6Sn-6Niobium revealed a mean removal torque of 37.44Ncm and were statistically significance in Wilcoxon Signed Rank test(P<0.05). Histomorphometrical comparisons were performed on $10\;{\mu}m$ thick undecalcified ground sections in the light microscope and Titanium-13Zirconium-6Niobium showed more mean bone-tometal contact ratio than to other twotitanium alloys but had no statistically significant differences were found among the three materials(P>0.01).

• Journal of Dental Rehabilitation and Applied Science
• /
• v.31 no.3
• /
• pp.203-211
• /
• 2015

Purpose: The purpose of this study was to investigate the reosseointegration periods when the rough surface implants, which had complete bone-implant ankylosis, suddenly losed the osseointegration. Materials and Methods: The implants with RBM surface treatment were inserted into both tibias of 23 rabbits. Two implants were submerged into each side. After six weeks, the primary removal torque was measured by Digital torque gauge, and then the implants were replaced and submerged to estimate the level of reosseointegration. After assigned healing periods for each group, the removal torque was measured again. BIC (Bone-Implant contact, %) ratio was measured through histomorphometric analysis.Paired t-test was processed by SPSS 14.0. One-way ANOVA and Tukey's post-hoc test was processed to analyze statistically significant differences among the groups. Results: In comparison with the primary removal torque, the secondary removal torque was increased after 11 days and significantly increased from 2 weeks. In fluorochrome labeling, the origin of mineralization was observed after 7 days, which showed as fluorescent bands around the bone-implant interfaces. After 11 days, the bone formation was apparent, and it is increased continuously with the passage of the time. Conclusion: In 11 days after the implant replacement, the secondary removal torque was almost as same as the primary value, and was significantly higher from 2 weeks. The mineralized shapes were observed in 7 days after the implant replacement, and then the bone formation appeared visibly in 11 days.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.5
• /
• pp.659-674
• /
• 2000

A large increase in the use of thin film coating of hydroxyapatite(HA) in implant dentistry is driven by the desire to take advantage of the excellent biocompatibility and high strength of HA coating. The purpose of this study was to evaluate the effects of HA-coated implants by ion Beam Assisted Deposition(IBAD) method in comparison to the sand-blasted and machined surfaces. Osteoblast culture test, removal torque test and histomorphometric analysis were performed and the following results obtained; 1. Examination of the osteoblast cultures displayed no difference in the secretion of alkaline phosphatase between the various specimen, but IBAD with pure HA specimen showed low alkaline phosphatase secretion(p<0.05). 2. Removal torque tests showed HA-coated implants by IBAD method to be similar in high value to the implants with sand-blasted surface than the implants with machined surface. And the ovariectomized group showed low mechanical test value than the normal group(p<0.05). 3. Histomorphometrical comparisons were performed on undecalcified ground sections. HA-coated implants by IBAD method demonstrated the highest mean bone-to-metal contact ratio on all threads and 3-best consecutive threads, and the implants with sand-blasted surface and implants with machined surface was in the next consecutive order(p<0.05). HA-coated implants showed slightly higher bone-to- metal contact ratio than sand-blasted implants, but no statistically significant difference was obtained between the two materials. The ovariectomized group showed lower value of bone-to-metal contact ratio than the normal group, but no statistically significant difference was obtained between the two groups. 4. Evaluation of bone volume on all threads and 3-best consecutive threads showed no statistically significant difference among the different surface treatment groups, but showed lower bone volume in ovariectomized group than in the normal group(p<0.05). According tn these results, thin film coated implants with HA showed high bone contact ratio, bone volume and removal torque strength in the short term, but long term observation is needed.

• The Journal of the Korean dental association
• /
• v.53 no.11
• /
• pp.804-816
• /
• 2015

PURPOSE: The aim of this study was to evaluate the influence of the oxide layer removal process in the Co-Cr-Mo (CCM) abutment after casting procedure on the prosthesis settlement and screw stability. MATERIALS AND METHODS: CCM abutments of four different interface conditions (CCM-M; machined, CCM-O; oxide layer formed, CCM-B; blasted, CCM-P; polished after blasted) and gold abutment (Gold-C; Cast with type III Gold alloy) were used. The initial settling values of abutments were evaluated according to the difference of implant-abutment length when the tightening torques were applied at 5 Ncm and 30 Ncm, and the settling values of abutments caused by loading were evaluated according to the difference of implant-abutment length before and after loading with 250 N, 100000 cycle. The loss ratios of removal torque for abutment screws were evaluated according to the difference in value of removal torques under 30 Ncm tightening torque applied before and after cyclic loading. RESULTS: The CCM-P and CCM-B group showed a higher initial settling value compared with the Gold-C group (P<.05), while the Gold-C group showed the highest settling values caused by loading (P<.05) and no significant differences were observed for between CCM groups (P>.05). The loss ratio of removal torque values for the CCM-B, CCM-P groups did not differ significantly from that of the Gold-C group (P>.05). CONCLUSION: Even though the oxide layer was removed by different methods, CCM abutment with internal conical connection structure showed lower abutment settling and similar screw loosening after cyclic loading compared with gold abutment.

• Journal of Periodontal and Implant Science
• /
• v.34 no.1
• /
• pp.177-193
• /
• 2004

Several experimental studies showed that the application of small amounts of electric current to bone stimulated osteogenesis at the site of the cathode and suggested that electrical currents promote osseointegration around dental implants. The purpose of this study was to determine the effect of direct microcurrent to endosseous titanium implants placed in bone defects. The right and left 2nd, 3rd and 4th mandibular premolars in ten mongrel dogs (15Kg of weight) were extracted. One monthe later, Ti-machined screw type implants(3.8 mm diameter x 8.5 mm length, $AVANA^{(R)}$, Ostem) were placed in surgically created circumferential defect area(width 5mm, depth 4mm). The implants were divided into three groups according to the treatment modalities: Control group- implants without electrical stimulation; Experimental group I- implants with allogenic demineralized freeze dried bone grafting; and Experimental group II-implants allogenic demineralized freeze dried bone grafting and electric stimulation. The animals were sacrificed in the 4th and 8th week after implant placement and un-decalcified specimens were prepared for histological and histometrical evaluation of bone-implant contact ratio (BIC) and bone formation area ratio (BFA) in defect area. Some specimens at 8 weeks after implantation were used for removal torque testing. Histologically, there was connective tissue infiltration in the coronal part of defect area in control and the experimental group I, whereas direct bone contact was found in the experimental group II without connective tissue invasion. Average BIC ratios at 4 weeks of healing were 60.1% in the experimental group II, 47.4% in the experimental group I and 42.7% in the control. Average BIC ratios at 8 weeks after implantation were 67.6% in the experimental group II, 55.9% in the experimental group I and 54.6% in the control. The average BFA ratio was 84.0% in the experimental group II, 71.8% in the experimental group I and 58.8% in the control at 4 weeks, and the BFA ratios were 89.6% in the experimental group II, 81.4% in the experimental group I and 70.5% in the control at 8 weeks after implantation. The experimental group II showed also significantly greater BIC and BFA ratios compared to the control and the experimental group I (p<0.05). The removal torque values at 8 weeks after implantation were 56 Ncm in the experimental group II, 49 Ncm in the experimental group I and 43 Ncm in the control. There was a statistically significant difference among 3 groups (p<0.05). These results suggest that electrical stimulation improve and accelerate bone healing around endosseous titanium implants in bone defect.

• The korean journal of orthodontics
• /
• v.47 no.4
• /
• pp.229-237
• /
• 2017

Objective: The aim of this study was to compare the initial stability as insertion and removal torque and the clinical applicability of novel orthodontic zirconia micro-implants made using a powder injection molding (PIM) technique with those parameters in conventional titanium micro-implants. Methods: Sixty zirconia and 60 titanium micro-implants of similar design (diameter, 1.6 mm; length, 8.0 mm) were inserted perpendicularly in solid polyurethane foam with varying densities of 20 pounds per cubic foot (pcf), 30 pcf, and 40 pcf. Primary stability was measured as maximum insertion torque (MIT) and maximum removal torque (MRT). To investigate clinical applicability, compressive and tensile forces were recorded at 0.01, 0.02, and 0.03 mm displacement of the implants at angles of $0^{\circ}$, $10^{\circ}$, $20^{\circ}$, $30^{\circ}$, and $40^{\circ}$. The biocompatibility of zirconia micro-implants was assessed via an experimental animal study. Results: There were no statistically significant differences between zirconia micro-implants and titanium alloy implants with regard to MIT, MRT, or the amount of movement in the angulated lateral displacement test. As angulation increased, the mean compressive and tensile forces required to displace both types of micro-implants increased substantially at all distances. The average bone-to-implant contact ratio of prototype zirconia micro-implants was $56.88{\pm}6.72%$. Conclusions: Zirconia micro-implants showed initial stability and clinical applicability for diverse orthodontic treatments comparable to that of titanium micro-implants under compressive and tensile forces.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.3
• /
• pp.557-565
• /
• 1997

Screw-shaped implants of commercially pure (c.p.) titanium, c.p. niobium, c.p. zirconium, and stainless steel(Sus 304) were inserted in the rabbit tibial bone over 12 weeks of follow-up. New developed torque gauge instrument was used to evaluate the implant holding power and a image analysis program coupled to a microscope was used for histomorphometry. The three best consecutive threads of each implant were measured. Quantitative analyses at 12 weeks revealed a partial bone contact to the four kinds investigated metals. There were no obvious adverse tissue reactions to any of the biomaterials. At 12 weeks the average removal torques for titanium, niobium and zirconium were better than that needed for Sus 304 screws, on the other hand high score of bony contact ratio of titanium and niobium were showed in comparison to those of zirconium and Sus 304. There was no significant differences in the amount of interfacial bone of zirconium and Sus 304 whereas there was significant difference in the torque forces of niobium and Sus 304. Three months after implant insertion, the average removal torque was 6.64 Ncm for the titanium, 6.57 Ncm for the niobium, 6.38 Ncm for the zirconium, and 4.25 Ncm for the Sus 304. On average bone contacts there were 51.24% in the titanium, 48.19% in the niobium, 31.79% in the zirconium, 23.54% in the Sus 304. Biocompatibility of the titanium, niobium and zirconium was acceptable level in comparison to the Sus 304.

• The Journal of the Korean dental association
• /
• v.54 no.7
• /
• pp.529-540
• /
• 2016

Objective: The objective of this study was to evaluate the osseointegration of narrow-diameter implant with trapezoid-shape and to evaluate the effect of coronal microthreads on trapezoid-shape narrow-diameter implant. Materials and Methods: The experimental narrow-diameter implants were classified into two groups according to absence or presence of coronal microthreads: trapezoid-shape narrow diameter implant (TN group) and trapezoid-shape narrow-diameter implant with microthreads (TNM group). They were installed alternately in bilateral mandible in three dogs. After 8 weeks, the animals were sacrificed. Resonance frequency analysis, removal torque test, and histometric analysis were performed. Results: Statistically higher implant stability quotient (ISQ) values were observed in TNM group than in TN group at the time of implant installation. However, significant ISQ values difference was not observed between groups at 8 weeks. Both groups showed significantly increased ISQ values at 8 weeks, compared to the time of implant installation. There was no significant difference between groups in removal torque test. Bone-implant contact ratio also showed no significant difference between groups in total and coronal part. Conclusion: Within the limitation of this study, it could be concluded that the trapezoid-shape design on narrow-diameter implant showed successful ossointegration, and the microthreads on coronal part did not result in significant bone-implant contact and biomechanical stability at 8 weeks.