• Journal of Korean Society of Forest Science
• /
• v.96 no.1
• /
• pp.54-57
• /
• 2007

Urea-formaldehyde (UF) resin was formulated similarly to plywood resin in the laboratory. The synthesized UF resin adhesive was mixed with extender, filler and acid catalyst. The mixture contained 56.1% total solids and 43.9% water. The mixes was used to bond five Com-Ply types using Korean wood species. The Com-Ply made were tested for shear strength and wood failure according to KS F 3101 ordinary plywood as well as for bending strength per KS F 3104 particleboard. The performance test results showed good strength properties for all Com-Ply types made in this study. This result represented that the UF resin adhesive mix was adequate for bonding Com-Ply with domestic wood species.

• Journal of the Korean Wood Science and Technology
• /
• v.47 no.2
• /
• pp.239-248
• /
• 2019

This research presents an improvement of the physical and mechanical properties of composite board (com-ply) made of Oriented Strand Board (OSB) coated with wood veneer of Pine (Pinus merkusii), Avocado (Persea Americana) and Mahogany (Swietenia mahogany). 1.5 mm thick veneers of those three wood types were adhered to the surface of OSB using two adhesive types: epoxy and isocyanate. The adhesive with the glue spread of $250g\;m^{-2}$ applied using single glue line was spread and then cold pressed with the pressure of $15kg\;cm^{-2}$ for 3 hours. The research result showed an improving dimension stability of com-ply, but not found on all parameters of physical property test. The moisture content seemed to be influenced by the com-ply type, yet not related to its thickness swelling, water absorption and linear expansion. The exception took place in the parallel linear expansion when immersed for 2 hours. The highest to the lowest increases of MOE and MOR were consecutively found on OSB coated with wood veneer of Pine, Mahogany and Avocado. However, the increases were statistically insignificant. The highest increasing screw hold power was found at the com-ply type AE (avocado veneer and epoxy adhesive) that was by 28%.

• Journal of the Korean Wood Science and Technology
• /
• v.22 no.3
• /
• pp.17-25
• /
• 1994

This study was carried out to compare the properties of Com-Ply Boards with those of OSBs. These two kinds of boards were made of same flakes. Com-Ply Boards were covered with three different thickness veneers, such as 4mm, 3mm, and 2.5mm. All manufactured Com-Ply Boards and OSBs were 12mm thick. In MOR, all Com-Ply Boards were higher than OSB, and especially 3mm-veneer and 2.5mm-veneer Com-Ply Board were highest. But OSB showed 420kg/$cm^2$. 3mm-veneer Com-Ply Board showed the highest internal bonding 7.0kg/$cm^2$ and then 2.5mm-veneer showed 6.8kg/$cm^2$, and OSB showed 6.6kg/$cm^2$. Screw holding strength showed the high value 23.9kg/$cm^2$, 25.5kg/$cm^2$, and 29.3kg/$cm^2$ respectively at 3mm-veneer, 2.5mm-veneer Com-Ply Board and OSB. Thickness swelling of Com-Ply Boards was lower than that of OSB, but Water absorption of OSB was lower. Finally it was very encouraging that all properties of OSB without veneer, whose cost is higher than flake and whose properties is better, were not worse than those of Com-Ply Board with veneer. It seems That more researches on OSB will be required.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.6
• /
• pp.791-806
• /
• 2020

In this study, a block shear strength test was conducted to compare and analyze the strength and failure mode on the glued laminated timber, CLT, and Ply-lam CLT, which are mainly used for the construction of wood construction as engineering wood. Through this, the Ply-lam CLT manufacturing conditions for optimum production, such as the type of lamina, plywood, adhesive, and layer composition, were investigated. The results are as follow. Through block shear strength test, it showed high strength in the order of glued laminated timber, Ply-lam CLT and CLT. In particular, the shear strength of Ply-lam CLT, which is made of a composite structure of larch plywood and larch lamina, passed 7.1 N/㎟, which is a Korean industrial standards for block shear strength of structural glued laminated timber. In addition, in this study, there was no different in shear strength according to the adhesive type used for glulam, CLT, and Ply-lam CLT adhesion. However, in the case of Ply-lam CLT, the difference in shear strength of Ply-lam CLT was shown according to the type of lamina and plywood. The results showed high strength in the order of Larix kaempferi > Mixed light hardwood ≒ Pinus densiflora, sieb, et, Zucc plywood. The optimal configuration of Ply-lam CLT is when larch plywood and larch lamina are used, and it is decided that the adhesive can be used by selecting PRF and PUR according to the application. The results of block shear strength failure mode by type of wood based materials were analyzed. The failure mode showed shear parallel-to-grain for glulam, rolling shear for CLT, and shear parallel-to-grain and rolling for ply-lam CLT. This is closely related to shear strength results and is decided to indicate higher shear strength in Ply-lam CLT than in CLT due to rolling shear.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.6
• /
• pp.907-916
• /
• 2020

This research was conducted to investigate the linear expansion and resistance properties of a composite board (com-ply). This board was made of medium-density fiberboard (MDF) laminated using avocado (Persea americana), mahogany (Swietenia mahogani), and pine (Pinus merkusii) veneers. These three types of veneers were laminated on both surfaces of the MDF using adhesives, namely, epoxy and isocyanate. Glue (250 g·m^-2) was spread on the surface, followed by cold press for 3 h with an applied pressure of 15 kg·cm^-2. The research result revealed that com-ply exhibited an increased dimensional stability compared with MDF, indicated by reduction in water absorption, thickness swelling, and linear expansion. The com-ply made of the pine veneer and isocyanate adhesive exhibited high density, water absorption, thickness swelling, and screw withdrawal load. The com-ply that exhibited the strongest resistance to drywood termite attacks was the one made of the mahogany veneer and isocyanate adhesive. Moreover, the com-ply that exhibited the biggest weight loss (3.6 %) was made of the pine veneer and epoxy adhesive. The results of this research may facilitate in manufacturing com-ply using the selected veneer and adhesive without the application of hot press.

• Journal of the Korean Wood Science and Technology
• /
• v.20 no.3
• /
• pp.29-37
• /
• 1992

This research was carried out to investigate the effects of cyclic humidification on the dimensional stability of particleboard manufactured according the three specific gravity levels and com-ply fabricated with a core of particleboard and veneer or plywood as the face and back materials. Both the particleboard and com-ply were subjected to four cycles of 50-90-50% relative humidity. The results are summarized as follows: Particleboard and com-ply followed a clear pattern of increasing dimensions and weight on the adsorption cycle and decreasing dimensions and weight on the humidification cycle. After the fourth cycle, the dimensions and weight of both particleboard and com-ply were greater than those originally measured. The greater part of increase in occurred during the first humidification cycle. The specific gravity of particleboard has a significant effect thickness and volume change. The dimensional stability of com-ply was better than that of particleboard. In addition, the dimensional stability of com-ply bonded with plywood was better than that of com-ply bonded with veneer.

• Journal of the Korean Wood Science and Technology
• /
• v.12 no.2
• /
• pp.35-43
• /
• 1984

This study was carried out to investigate the block shear strength of the 2ply laminated wood composed of Pinus thunbergii with ureaformaldehyde resin as adhesives according to pressure (6, 9, 12, 15kg/$cm^2$), pressing time(5, 10, 20, 30 hrs.), amount of spread(54, 108, 217, 324g/$cm^2$), hardener(10, 20, 30, 40% of 10% $NH_4CL$ on resin) and extender(0, 5, 10, 15% wheat flour on resin), and the bending strength and bending young's modulus of laminated beam according to the number of ply. The results were summarized as follows; 1. According to pressing pressure with amount of spread 217g/$cm^2$ both dry and wet shear strength of laminated wood showed the highest in 15kg/$cm^2$, and hot-cold soaking treatment showed the highest in 9kg/$cm^2$, while all shear strength of dry, wet and hot-cold soaked laminated wood have been reduced with the increasing of pressing time. 2. According to amount of spread, adhesion strength with the dry, wet and hot-cold soaking treatments revealed the highest in 217g/$cm^2$ and have been reduced under or over 217g/$cm^2$ of spread. 3. According to addition of hardener and extender, all shear strength of laminated block with the dry, wet and hot-cold soaking treatments have been reduced in increasing of addition amount of hardener and extender. The bending strength of beam according to the number of ply showed the highest in 2ply laminated wood and horizontal loading beam to glue line had the higher in strength than the vertical loading.

• Journal of the Korean Wood Science and Technology
• /
• v.49 no.1
• /
• pp.57-66
• /
• 2021

In recent years, the use of cross laminated timber (CLT) has been evolving. In addition, CLT manufactured with various species such as Japanese cedar has been developed to utilize the local resources in each country. However most factories in Japan produce CLT by bonding the laminae in width direction for orthogonal layers, where grain of element is perpendicular to the grain of outer layer, and this process is considered to be one of the factors that reduce productivity. A new wood based material (hereinafter referred to as Ply-lam) using wooden panel such as plywood for the orthogonal layer was developed in order to improve productivity in CLT manufacturing and improve quality. Japanese cypress lamina was used for the parallel layer, where grain of element is parallel to the grain of outer layer, of CLT and Korean larch plywood was used for the orthogonal layer, in order to effectively use Korean larch and expand the utilization of Japanese cypress. The cross-sectional construction of the Ply-lam was 5-layers 5-plies, and the dimensions were 1000 mm (width) × 150 mm (depth) × 4000 mm (length). As a performance evaluation of the manufactured Ply-lam, strength tests such as out-of-plane bending, in-plane bending, out-of-plane shearing and in-plane shearing tests were carried out. As the result of this study, Ply-lam composed of Japanese cypress lamina panels and Korean larch plywood showed very higher out-of-plane bending strength compared to the standard strength of CLT. And the result obtained in other tests seems to show a sufficiently high value.

• Journal of the Korean Wood Science and Technology
• /
• v.26 no.1
• /
• pp.87-96
• /
• 1998

The bending performances were evaluated at the radiata pine plywood through veneer compositions encompassing veneer quality, ply-numbers and overlays of the high density- or medium density-phenol resin impregnated sheets (hereafter abbreviated as resin sheets) on the raw plywood. In addition, a prediction on the bending MOE of veneers and plywoods was carried out by the nondestructive testing with stresswave timer. The summarized results were as follows: I. Bending strength and bending MOE of resin sheets-overlaid plywoods in parallel surface grain direction through 5 and 7ply were increased by 13 to 45% and 17 to 34%, respectively. Resin sheets-overlay occurred an increasing effect of the strength efficiency i.e. strength perpendicular-to-grain direction versus that parallel-to-grain direction, showing the phenomenon that the plywood strength becomes greater at the perpendicular-to-grain direction of 7ply than at that of 5ply. Displacement at bending failure had a greater trend at 7ply than at 5ply, and was decreased by resin sheets-overlay. 2. After the nondestructive bending MOEs were measured for individual veneers, these veneers were rearranged in plywood-manufacture. In these plywoods, including resin sheets-overlay, the actual MOE was predictable with feasibility of $R^2$=0.53, and also the nondestructively-evaluated MOE was lower by 20% in raw plywood, and higher 20% in LVL than actual bending MOEs.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.2
• /
• pp.46-57
• /
• 2006

To estimate nondestructively strength performances of laminated woods, 3-ply parallel- and cross-laminated wood specimens exposed under atmosphere conditions after bending creep test were prepared for this study. The effects of density of species, arrangement of laminae and lamination types on dynamic MOE obtained by flexural vibration were investigated, and regression analyses were conducted in order to estimate static bending strength and bending creep performances. Dynamic MOE of parallel-laminated woods showed 1.0~1.2 times higher values than static bending MOE, and those of cross-laminated woods showed 1.0~1.4 times higher values than static bending MOE. The degree of anisotropy of dynamic MOE perpendicular to the grain of face laminae versus that parallel to the grain of face laminae was markedly decreased by cross-laminating. There were strong correlations between dynamic MOE by flexural vibration and static bending MOE (correlation coefficient r = 0.919~0.972) or bending MOR (correlation coefficient r = 0.811~0.947) of 3-ply laminated woods, and the correlation coefficient were higher in parallel-laminated woods than in cross-laminated woods. It indicated that static bending strength performances were able to be estimated from dynamic MOE by flexural vibration. Also, close correlations between the reciprocal of dynamic MOE by flexural vibration and initial compliance at 0.008 h of 3-ply laminated woods were found (correlation coefficient r = 0.873~0.991). However, the correlation coefficient between the reciprocal of dynamic MOE and creep compliance at 168 h of 3-ply laminated woods was considerably lower than those between dynamic MOE and initial compliance, and it was hard to estimate creep compliance with a high accuracy from dynamic MOE due to the variation of creep deformation.