Abstract
Urea-formaldehyde (UF) resin was formulated similarly to plywood resin in the laboratory. The synthesized UF resin adhesive was mixed with extender, filler and acid catalyst. The mixture contained 56.1% total solids and 43.9% water. The mixes was used to bond five Com-Ply types using Korean wood species. The Com-Ply made were tested for shear strength and wood failure according to KS F 3101 ordinary plywood as well as for bending strength per KS F 3104 particleboard. The performance test results showed good strength properties for all Com-Ply types made in this study. This result represented that the UF resin adhesive mix was adequate for bonding Com-Ply with domestic wood species.
요소수지접착제를 합판제조용 접착제와 유사하게 실험실에서 합성하고, 합성한 요소수지접착제를 증량제, 충전제, 산경화촉매제와 혼합하였다. 요소수지접착제 혼합물의 고형분량은 56.1%이고, 물은 43.9%였다. 국산재와 요소수지접착제 혼합물로 5종류의 Com-Ply를 제조하고, KS F 3101 보통합판의 인장 전단 접착력 시험 및 KS F 3104 파티클보드의 휨파괴계수 시험을 수행했다. 성능 평가된 결과는 제조된 5종류의 Com-Ply에서 모두 적합한 결과를 보여줬다. 이런 결과는 본 연구에서 사용된 요소수지접착제 혼합물이 국산재 Com-Ply제조에 적합하다는 것이다.