• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.865-868
• /
• 2008

As a part of a series of study, this study reviewed the fire proof characteristics of high performance concrete RC column members using non-stripping form that accompanied metal lath lateral confinement to prevent spalling of high performance concrete which is increasingly used recently, and the results are as follows. Flow and air amount both satisfied target range, and compressive strength, over 80MPa at age 28 days, showed high strength range. As for spalling characteristics, in the case of plain in which no fiber is mixed, severe spalling occurred, and in the case of 0.05% nylon("NY" hereinafter)+polypropylene("PP" hereinafter) fiber mixture, only surface area experienced partial spalling. Regarding non-stripping form changes, both non-stripping 25-20 and non-stripping 50-20 experienced spalling at finish material area, and non-stripping 50-20 showed better spalling proof performance than non-stripping 25-20. In the case of non-stripping 50-40, spalling was prevented, and while mass reduction rate was less than 10%, its temperature hysteresis showed the most excellent fire proof performance with base metal surface area maximum temperature $376.1^{\circ}C$.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.11a
• /
• pp.43-44
• /
• 2015

In this study, spalling property were evaluated from concrete with compressive strengths of 30MPa, 90MPa, 180MPa, applied with fast heating condition(ISO-834 standard heating curve) and slow heatign condition(1℃/min). As a result, the spalling property of concrete was shown differently with compressive and heatign rate. And It could be separated three as non spalling, surface spalling and explosive spalling.

• International Journal of Concrete Structures and Materials
• /
• v.18 no.2E
• /
• pp.103-109
• /
• 2006

Spalling is defined as damages to concrete exposed to high temperature during fire, causing cracks and localized bursting of small pieces of concrete. As the concrete strength increases, the degree of damage caused by spalling becomes more serious due to impaired permeability. It is reported that polypropylene(PP) fiber has an important role in protecting concrete from spalling, and the optimum dosage of PP fiber is 0.2%. However, this study was conducted on non-reinforced concrete specimens. The high-temperature behavior of high-strength reinforced concrete columns with various concrete strength and various quantity of PP fibers is investigated in this study. The results revealed that the ratio of unstressed residual strength of columns increased as the concrete strength increased and as the quantity of PP fiber increased from 0% to 0.2%. However, the effect of PP fiber quantity on residual strength of column was barely above 0.2%.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.05a
• /
• pp.33-36
• /
• 2011

Recently, It has increased to use ultra high strength concrete. It is effective to mix organic fibers for preventing spalling. But if fiber mixed, flowability of concrete is decreases. The aim of this study is to evaluation of fire resistance performance for fiber-mixed ultra high strength concrete on field application. As a result, flowability of nylon fiber mixed concrete is better than polyethylene fiber mixed. In non-fiber and polyethylene fiber mixed concrete, spalling occurred. And strain converged at 0.004. Also, residual strength could not evaluate. Nylon fiber mixed concrete is effective to prevent spalling. And it remians 50% residual strength compare with compressive strength at room temperature.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2008.05a
• /
• pp.87-91
• /
• 2008

The study examined fire resistance of concrete followed by change of mixed rate in PP and NY composite fiber and the results were as follows. In the event of fluidity in concrete not set, plane satisfied 600±100, its target slump flow, and fluidity was reduced as organic fiber's mixed rate was increased. Air amount satisfied 3.0±1.0, its target air amount, and didn't have distinct differences in reduction and increase according to organic fiber's kind and change of its mixed rate. However, it had a tendency that fluidity was reduced as the mixed rate was increased. In characteristics of hardening concrete, the 28th day compressive strength followed by organic fiber's kind and change of its mixed rate didn't have a lot of differences and satisfied high strength scope as about 70MPa. In spalling characteristics after fire resistance test, spalling was happened in non-mixture, plane combination, and P1N0. In other combinations, spalling resistance was happened. The relic compressive strength rate was 56%, the best condition, in P3N1(PP0.03%, NY0.01% compositeness) mixing PP fiber with NY fiber at once.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.12 no.1
• /
• pp.31-41
• /
• 2010

This paper presents both numerical and physical modeling approaches for the dilation and spalling of rock recognized as typical process of rock around an underground opening at depth. For physical approach, laboratory testing of rectangular beams using a synthetic rock was used to investigate the onset of dilation and spalling. The beams are axially compressed and subjected to 4-point bending to provide non-uniform compressive stresses which are similar to the maximum tangential stress distribution around circular openings. Discrete element numerical analyses using commercial code $PFC^{2D}$ (Particle Flow Code) were performed to evaluate the stress path at various locations in the beams. The findings from these approaches suggest that the onset of dilation in laboratory tests appears to be a good indicator for assessing the stress magnitudes required to initiate spalling.

• Fire Science and Engineering
• /
• v.24 no.3
• /
• pp.145-151
• /
• 2010

The fire in tunnel, when failed to extinguish at early stage, tends to easily develop to high temperature and spread to entire area of the tunnel because of considerable level of fire load and smoke control facility within the tunnel, resulting in severe damage to the people and tunnel structure. This study was intended to carry out the fire test with MHC fire curve, a scenario, which has the most rapid fire rise, on assumption of load ratio of 1, 20, 40, 60 and 70%, so as to identify the thermal characteristics of the concrete against spalling and the range of fire damage. The specimen was small scale sample as defined by EFNARC and the mixing ratio was based on 24 MPa, which is considered to be the normal strength. As a result of test, 16mm spalling was occurred on the lining under the non-load condition, while no spalling was occurred with 20% and 40% of load ratio. In case of 60% of load ratio, 24 mm of spalling was occurred and it failed in 10 minutes after heating in case of 70% load condition.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.553-556
• /
• 2004

This paper is to investigate the spalling and fire endurance of high performance RC column member with PP fiber and lateral confinement of metal lath and non fire resistance removal type form. According to test results, combination of PP fiber and metal lath as well as use fire resistance non removal type form had favorable fire resistance by discharging internal vapour pressure and lateral confining. After fire endurance test, compressive strength decreased markedly caused by internal expansion pressure and crack. Residual strength of plain concrete was decreased to $22\%$. The use of PP fiber and lateral confinement of metal lath and non removal type form enhanced the residual strength above $40\%$. Especially, the combination of $0.1\%$ of PP fiber and lateral confinement with the level of 2.3T exhibited more than $51\%$ of residual strength. Therefore, to improve fire endurance and spalling resistance, the combination of $0.1\%$ of PP fiber and metal lath with 2.3T can be the proper measure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.457-460
• /
• 2008

This study evaluated fire resistance performance for polypropylene/steel fiber reinforced high strength concrete column. Full-size columns were constructed and tested with or without fibers using ISO-834 fire curve. As the result of test, non-fiber high strength concrete column specimen occurred serious spalling and indicated rapidly internal temperature increase. Specimen with polypropylene fiber occurred not spalling. Specimen with hybrid fiber occurred not spalling as well as does not propagated temperature propagation. Therefore, hybrid fiber reinforced column specimen indicated a good fire resistance performance than other cases.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.305-306
• /
• 2009

This study is on basic experimental methods of easily verifying the fiber content in non-spalling concrete at construction sites. As a result, fiber content in a mixture can be effectively measured by using 15$\ell$ of water for dilution of specimens, dry bit trowel for tool, and microwave for drying.