• Clean Technology
• /
• v.24 no.1
• /
• pp.77-84
• /
• 2018

In this study, $Li_4Ti_5O_{12}$ anode materials for lithium ion battery were synthesized by dry ball-mill method. Polyvinyl chloride (PVC) as a carbon source was added to improve electrochemical properties. When the PVC was added after $Li_4Ti_5O_{12}$ formation, the spinel structure was well synthesized and it was confirmed by X-ray diffraction (XRD) experiments. When the carbon material was added before the synthesis and the heat treatment was performed, it was confirmed that a material having a different crystal structure was synthesized even when a small amount of carbon material was added. In the case of $Li_4Ti_5O_{12}$ without the carbon material, the electrical conductivity value was about $10{\mu}S\;m^{-1}$, which was very small and similar to that of the nonconductor. As the carbon was added, the electrical conductivity was greatly improved and increased up to 10,000 times. Electrochemical impedance spectroscopy (EIS) analysis showed that the size of semicircle corresponding to the resistance decreased with the carbon addition. This indicates that the resistance inside the electrode is reduced. According to the Cyclic voltammetry (CV) analysis, the potential difference between the oxidation peak and the reduction peak was reduced with carbon addition. This means that the rate of lithium ion insertion and deinsertion was increased. $Li_4Ti_5O_{12}$ with 9.5 wt% PVC added sample showed the best properties in rate capabilities of $180mA\;h\;g^{-1}$ at 0.2 C-rate, $165mA\;h\;g^{-1}$ at 0.5 C-rate, and $95.8mA\;h\;g^{-1}$ at 5 C-rate.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.2
• /
• pp.120-124
• /
• 2008

Carbon-coated $LiFePO_4$ and $LiMn_{0.4}Fe_{0.6}PO_4$ cathode materials for lithium batteries were synthesized by a sol-gel method. X-ray diffraction and scanning electron microscopy data showed that the cathode materials are pure crystalline and are surrounded by porous carbon. The initial discharge capacities of $LiFePO_4$ and $LiMn_{0.4}Fe_{0.6}PO_4$ with the liquid electrolyte of 1M $LiPF_6$ in EC/DMC are 132 mAh/g and 145 mAh/g, respectively, at current density of 0.1 C-rate. $LiFePO_4$ and $LiMn_{0.4}Fe_{0.6}PO_4$ with an electrospun polymer-based electrolyte exhibit initial discharge capacities of 114 and 130 mAh/g at 0.1 C-rate at room temperature, respectively.

• Journal of the Korean Electrochemical Society
• /
• v.17 no.2
• /
• pp.103-110
• /
• 2014

In the study, a room temperature ionic liquids as a co-solvent was used to evaluate the feasibility with various electrodes in Li-ion batteries. 1-Ethyl-1-methyl piperidinium bis(trifluoromethanesulfonyl) imide(PP12 TFSI) is an ionic liquid that melts at $85^{\circ}C$. Pure PP12 TFSI is not able to be used as an electrolyte because it is a solid salt at room temperature. PP12 TFSI is mixed with EC/DEC(1/1 vol.%) to prepare mixed solvents. The electrolyte 1.5M $LiPF_6$ in a mixed solvent having 44 wt.% PP12 TFSI is prepared to evaluated the various electrodes. The electrolytes provides good cycles life of cells with $LiNi_{0.5}Mn_{1.5}O_4(LNMO)$, $LiFePO_4(LFP)$, $Li_4Ti_5O_{12}(LTO)$ and artificial graphite. Further improvement of the cell performances can be accomplished by enhancing wettability of electrolytes to electrodes.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.6
• /
• pp.618-624
• /
• 2020

A portable power supply system for soldiers must be able to supply electric energy corresponding to the power consumption of combat support troops, and have a carrying load in a range that does not impair the combatant's ability to execute operations. In particular, as the total required power of combat equipment increases with the advances in the future soldier system, a portable, lightweight power supply system with high efficiency is essential. A fuel cell has a high energy-to-weight density compared to lithium batteries, which are used mainly as a military power source system. Therefore, it is capable of miniaturization and lightweight, making active R&D to a portable power supply system. In this paper, the characteristics of the fuel cell applied as a portable power supply system, and the R&D trends of domestic and foreign military portable fuel cell systems were investigated. The current status of domestic technology compared to the level of foreign development was analyzed. In addition, future technology development plans are presented based on the consideration factors when developing a portable fuel cell (power supply stability, portability, and cost reduction) so that it can be used when establishing a plan on the development of a portable fuel cell system for the future soldier system.

• Journal of the Korean Electrochemical Society
• /
• v.15 no.4
• /
• pp.222-229
• /
• 2012

We studied the electrochemical phenomena and increase of capacity according to the polymer composite electrode of two different polymeric materials with different the voltage range and capacity. Polyaniline (PANI) with relatively high voltage and small capacity and poly [1,2] bis-thio[1,8]-naphthylidine (PTND) with slightly low voltage and large capacity were used as polymer composite electrode materials. After PTND was synthesized, PANI was synthesized on the surface of PTND. The synthesis and the fine structure were analyzed by FT-IR, XPS, FE-SEM, and FE-TEM. Charge/discharge capacity and cyclic voltammetry measurements were carried out for the electrochemical performance as a polymer cathode active material for lithium secondary batteries. The discharge capacities of PANI/PTND after 1,5, and 10 cycles at 1.3~4.0 V voltage range and room temperature 167 mAh/g, 90 mAh/g, and 81 mAh/g. When we compared with PANI (80, 67, and 62 mAh/g), the discharge capacity after 10 cycles was improved about 30%. After 50 cycles, the discharge capacity of PANI/PTND was 67 mAh/g.

• Journal of the Korean Electrochemical Society
• /
• v.19 no.3
• /
• pp.87-94
• /
• 2016

In order to improve performances of submicrometer-sized Si negative electrode which shows larger volumetric change than nano-sized Si, composite binders are introduced by blending between poly(phenanthrenequinone) (PPQ) conductive polymer binder and poly(acrylic acid) (PAA) having good adhesion strength due to its carboxyl functional group. Blending between PPQ and PAA shows an effect that the adhesion strength of the Si electrode with the composite conductive binder is greatly improved after blending and this makes its better stable cycle performance. Blending ratios between PPQ and PAA in this work are 2:1, 1:1, 1:2 (by weight) and the best capacity retention at 50th cycle is observed in the electrode with the blending ratio 2:1 (named QA21). This is because that PPQ plays a role of conductive carbon among the Si particles or between Si particles and Cu current collector and PAA binds effectively the particles and the current collector. According to this synergetic effect, the internal resistance of the Si electrode with the blending ratio 2:1 is the smallest value. In addition, the Si electrode with PPQ-PAA composite binder shows the better stable cycle performance than the electrode with conventional super-P conductive carbon (20 wt.%).

• Journal of the Korean Electrochemical Society
• /
• v.12 no.1
• /
• pp.81-87
• /
• 2009

An indium-tin oxide (ITO) coated spinel manganese oxide (${LiMn_2}{O_4}$, LMO) is prepared and its high-temperature ($55^{\circ}C$) cycle performance and rate capability are examined. A severe electrolyte decomposition and film deposition is observed on the un-coated ${LiMn_2}{O_4}$ cathode, which leads to a significant electrode polarization and capacity fading. Such an electrode polarization is, however, greatly reduced for the ITO-coated (> 2 mol%) LMO cathode, which leads to an improved cycle performance. This can be rationalized by a suppression of electrolyte decomposition, which is in turn indebted to a decrease in the direct contact area between LMO and electrolyte. The suppression of film deposition on the ITO-coated LMO cathode is confirmed by infra-red spectroscopy. The rate capability is also improved by the surface coating, which may be resulted from a suppression of resistive film deposition and high electric conductivity of ITO itself.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.4
• /
• pp.284-288
• /
• 2008

Sn-thin film as high capacitive anode for thin film lithium-ion battery was prepared by organic-electrolyte electroplating using Sn(II) acetate. Electrolytic solution including $Li^+$ and $Sn^{2+}$ had 3 reduction peaks at cyclic voltammogram. Current peak at $2.0{\sim}2.5\;V$ region correspond to the electroplating of Sn on Ni substrate. This potential value is lower than 2.91 V vs. $Li^+/Li^{\circ}$, of the standard reduction potential of $Sn^{2+}$ under aqueous media. It is the result of high overpotential caused by high resistive organic electrolytic solution and low $Sn^{2+}$ concentration. Physical and electrochemical properties were evaluated using by XRD, FE-SEM, cyclic voltammogram and galvanostatic charge-discharge test. Crystallinity of electroplated Sn-anode on a Ni substrate could be increased through heat treatment at $150^{\circ}C$ for 2 h. Cyclic voltammogram shows reversible electrochemical reaction of reduction(alloying) and oxidation(de-alloying) at 0.25 V and 0.75 V, respectively. Thickness of Sn-thin film, which was calculated based on electrochemical capacity, was $7.35{\mu}m$. And reversible capacity of this cell was $400{\mu}Ah/cm^2$.

• Journal of the Korean Chemical Society
• /
• v.50 no.4
• /
• pp.315-320
• /
• 2006

manganese oxides have been prepared by Chimie Douce redox reaction between permanganate and chalcogen element fine powder under acidic condition (pH = 1). According to powder X-ray diffraction analyses, the S- and Se-doped manganese oxides are crystallized with layered birnessite and tunnel-type -MnO2 structures, respectively. On the contrary, Te-doped compound was found to be X-ray amorphous. According to EDS analyses, these compounds contain chalcogen dopants with the ratio of chalcogen/manganese = 4-7%. We have investigated the chemical bonding character of these materials with X-ray absorption spectroscopic (XAS) analysis. Mn K-edge XAS results clearly demonstrated that the manganese ions are stabilized in octahedral symmetry with the mixed oxidation states of +3/+4. On the other hand, according to Se K- and Te L1-edge XAS results, selenium and tellurium elements have the high oxidation states of +6, which is surely due to the oxidation of neutral chalcogen element by the strong oxidant permanganate ion. Taking into account their crystal structures and Mn oxidation states, the obtained manganese oxides are expected to be applicable as electrode materials for lithium secondary batteries.

• Clean Technology
• /
• v.22 no.4
• /
• pp.308-315
• /
• 2016

$SiO_x/ZnO$ composites were prepared from sol-gel method for excellent cycle life characteristics. The composites were coated by PVC as a carbon precursor. ZnO removal to create a void space therein was able to buffer the volume change during charge and discharge. To determine the crystal structure and the shape of the synthesized composite, XRD, SEM, TEM analysis was performed. The carbon contents in the composites were confirmed by TGA. The pore structure and pore size distribution of the composite was measured with the BET specific surface area analysis and BJH pore size distribution. Enhanced electric conductivity by carbon addition was determined from powder resistance measurement. Electrochemical properties were measured with the AC impedance and the charge and discharge cycle life characteristics. When carbon was coated on the $SiO_x/ZnO$ sample, the electrical conductivity and the discharge capacity were increased. After removal of ZnO with HCl the surface area of the sample was increased, but the discharge capacity was decreased. $SiO_x/ZnO$ sample without acarbon coating showed very low discharge capacity, and after carbon coating the sample showed high discharge capacity. For cycle life characteristics, $C-SiO_x/ZnO$ composite (Zn : Si : C = 1 : 1 : 8) with a capacity of $815mAh\;g^{-1}$ at 50 cycle and 0.2 C has higher capacity than existing graphite-based anode materials.