• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1018-1021
• /
• 2006

Powdered metal parts and components may be carburized successfully in a vacuum furnace by combining carburizing technology $VacCarb^{TM}$ with a hi-tech control system. This approach is different from traditional carburizing methods, because vacuum carburizing is a non-equilibrium process. It is not possible to set the carbon potential as in a traditional carburizing atmosphere and control its composition in order to obtain a desired carburized case. This paper presents test results that demonstrate that vacuum carburizing system $VacCarb^{TM}$ carburized P.M. materials faster than traditional steel with acceptable results. In the experiments conducted, PM samples with the lowest density and open porosity showed a dramatic increase in the surface carbon content up to 2.5%C and a 3 times deeper case. Currently the boost-diffusion technique is applied to control the surface carbon content and distribution in the case. In the first boost step, the flow of the carburizing gas has to be sufficient to saturate the austenite, while avoiding soot deposition and formation of massive carbides. To accomplish this goal, the proper gas flow rate has to be calculated. In the case of P.M. parts, more carbon can be absorbed by the part's surface because of the additional internal surface area created by pores present in the carburized case. This amount will depend on the density of the part, the densification grade of the surface layer and the stage of the surface. "as machined" or "as sintered". It is believed that enhanced gas diffusion after initial evacuation of the P.M. parts leads to faster carburization from within the pores, especially when pores are open . surface "as sintered" and interconnected . low density. A serious problem with vacuum carburizing is delivery of the carbon in a uniform manner to the work pieces. This led to the development of the different methods of carburizing gas circulation such as the pulse/pump method or the pulse/pause technique applied in SECO/WARWICK's $VacCarb^{TM}$ Technology. In both cases, each pressure change may deliver fresh carburizing atmosphere into the pores and leads to faster carburization from within the pores. Since today's control of vacuum carburizing is based largely on empirical results, presented experiments may lead to better understanding and improved control of the process.

• Transactions of the Korean hydrogen and new energy society
• /
• v.25 no.4
• /
• pp.344-354
• /
• 2014

Activated charcoal supported nickel molybdenum carbide (carburized Ni-Mo/AC) catalysts were prepared by wet-impregnation followed by temperature-programmed carburization using 20% $CH_4/H_2$ gas. The effects of pH and initial Ni/Mo mole ratio during wet-impregnation step on the characteristics of the carburized Ni-Mo/AC catalysts were investigated using ICP, XRD, XPS, BET and $CO_2$-TPD techniques, and correlated with the catalytic activity of the carburized Ni-Mo/AC in methane dry reforming reaction. Comparison of the results of methane dry reforming reaction kinetics with the results of characterization of the carburized Ni-Mo/AC catalyst showed that the catalytic activity in methane dry reforming reaction was higher at higher initial Ni/Mo mole ratio or at lower pH(3~natural value). This phenomenon was related to the crystal size of metallic Ni in the carburized Ni-Mo/AC catalyst.

• Resources Recycling
• /
• v.25 no.2
• /
• pp.10-16
• /
• 2016

In this study, the Ni base superalloy was recycled by Argon oxygen decarburization(AOD) process using an inconel 713C scrap. During AOD process, argon gas was continuously injected 1,000 sccm and oxygen gas was injected into 10, 20 and 30 minutes of 100, 250 and 500 sccm.. In early stage of oxygen injection, the oxygen dose increased with increasing Al, Cr, and Mo content and decreasing C content. And Al content was decreased by carburization with added elements in late stage Because of oxidation was occurred with Al, Cr etc. after the reaction of carbon has been finished. From the results, the ratio of ${\gamma}^{\prime}$ phase reduced due to decreasing of Al content for that reason Al is the main element to form the ${\gamma}^{\prime}$ phase. Also carbide reduced owing to decreasing of C content so the mechanical properties of the specimens excessively injected by excess $O_2$ gas were decreased.

• Journal of the Korean Society for Heat Treatment
• /
• v.5 no.4
• /
• pp.195-200
• /
• 1992

SCM 415 has been vacuum carburized in the carburizing pressure of 60-65kpa and the carburizing temperature of 1233k and 1273k after varied to 0-20 in the ratio of $N_2/C_3H_8$ and then diffusion treated for various times at 1123k. The results obtained from the experiment are as follows. 1. With increasing from 0 to 20 in ratio of $N_2/C_3H_8$ the sooting formation of surface after carburizing considerably decreased. 2. The hardness control and surface carbon content of carburizing surface has been modified by the addition of nitrogen to the propan. 3. The appoximate value of k is indirectry calculated at 1123k which results are obtained to $0.58{\times}10^{-2}(wt.%.S^{-1/2})$. 4. A great deal of propan by addition of nitrogen gas in carburizing gas was possible to saving without considerable change in case hardening depth. 5. The effective carburizing depth range is obtained to 0.8-1.1mm by diffusion temperature of 1123k after carburization at 1273k-3.6ks, and the surface hardness is increased as the increasing of $T_D/T_c$ in our experimental condition, and the maximum hardness as reachin distance from surface is decreased.

• Resources Recycling
• /
• v.13 no.5
• /
• pp.45-50
• /
• 2004

To investigate the characteristics of phases formed in iron carbides, super iron carbide was synthesized from hematite fines with $CO-H_2$ gas mixture after reduction under $H_2$ gas at $600^{\circ}C$. Before carburization, the surface of iron powder reduced was pre-treated in the atmosphere of 0.05 vol% $NH_3$-Ar. The synthesized iron carbides were comprehensively explored by C/S analyzer(Low C/S determinator), M$\"{o}$ssbauer spectroscopy, X-ray diffraction patterns(XRD), scanning electron microscopy(SEM), transmission electron microscopy(TEM), and Raman spectroscopy at various reaction time of 5, 10, 15, 20, 25, 30, and 35 min, respectively. By adding a small amount of $NH_3$ gas, the super iron carbides containing 10 wt% carbon were synthesized, and its addition stabilized iron carbides. It was found that the $NH_3$ treatment played a major role in the formation of iron carbide without decomposition($Fe_3C{\to}$3Fe+C) of iron carbides and precipitation of free carbon. It also succeed to synthesize super iron carbide, $Fe_5C_2$, as a stable single phase without involving Fe and $Fe_3C$ phases.