• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.2
• /
• pp.98-102
• /
• 2010

This paper describes that single crystalline 3C-SiC (cubic silicon carbide) thin films have been deposited on carbonized Si(100) substrates using hexamethyldisilane (HMDS, $Si_2(CH_3){_6}$) as a safe organosilane single precursor and a nonflammable mixture of Ar and $H_2$ gas as the carrier gas by APCVD at $1280^{\circ}C$. The deposition was performed under various conditions to determine the optimized growth condition. The crystallinity of the 3C-SiC thin film was analyzed by XRD (X-ray diffraction). The surface morphology was also observed by AFM (atomic force microscopy) and voids between SiC and Si interfaces were measured by SEM (scanning electron microscopy). Finally, residual strain and hall mobility was investigated by surface profiler and hall measurement, respectively. From these results, the single crystalline 3C-SiC film had a good crystal quality without defects due to viods, a low residual stress, a very low roughness.

• Journal of Sensor Science and Technology
• /
• v.14 no.2
• /
• pp.63-68
• /
• 2005

The nano-grained Pd or Pt-doped $SnO_{2}$ thin films were deposited on the alumina substrate at ambient temperature or $300^{\circ}C$ by using an R.F. magnetron sputtering system and then annealed at $650^{\cir}C$ for 1 hour or 4 hours in air. The crystallinity and microstructure of the annealed films were analyzed. A grain size of the thin films was 30 nm to 50 nm. As a result of gas sensitivity measurements to an alcohol vapor of $36^{\circ}C$, the 2 wt.% Pt-doped $SnO_{2}$ thin-film sensor deposited at $300^{\circ}C$ and annealed at $650^{\circ}C$ for 4 hours showed the highest sensitivity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.248-249
• /
• 2007

The $V_{1.9}W_{0.1}O_5$ thin films deposited on Pt/Ti/$SiO_2$/Si substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.9}W_{0.1}O_5$ thin films annealed at $300^{\circ}C$ were 37.7, with a dielectric loss of 2.535, respectively. Also, the TCR values of the $V_{1.9}W_{0.1}O_5$ thin films annealed at $300^{\circ}C$ were about -3.7%/K.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.1
• /
• pp.29-33
• /
• 2018

Using a vanadium dioxide ($VO_2$) source, highly pure and amorphous vanadium oxide (VO) thin films were deposited using an e-beam evaporator at room temperature and high vacuum (<$10^{-7}$ Torr). Then, by controlling the post-annealing conditions such as $N_2:O_2$ pressure ratio and annealing time, we could easily synthesize a homogeneous $VO_2$ thin film and also mixed-phase VO thin films, including $VO_2$, $V_2O_5$, $V_3O_7$, $V_5O_9$, and $V_6O_{13}$. The crystallinity and phase of these were characterized by X-ray diffraction, and the surface morphology by FE-SEM. Moreover, the electrical properties and ethanol sensing measurements of the VO thin films were analyzed as a function of temperature. In general, mixed-phases as a self-doping effect have enhanced electrical properties, with a high carrier density and an enhanced response to ethanol. In summary, we developed an easy, scalable, and reproducible fabrication process for VO thin films that is a promising candidate for many potential electrical and optical applications.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.4
• /
• pp.318-324
• /
• 2007

We report on a strong violet luminescence emitted from the ZnO:Al films grown on glass substrate by radio-frequency magnetron sputtering. The growth of high-quality thin films and their optical properties are controlled by adjusting the mixture ratio of Ar and $O_2$, which is used as the sputtering gas. The crystallinity of the films is improved as the oxygen flow ratio is decreased, as evidenced in both x-ray diffractometer and atomic force microscope measurements. As for the violet luminescence measured by photoluminescence (PL) spectroscopy, the peak energy and intensity of the PL signal are decreased with increasing the oxygen flow ratio. The peak energy of the violet PL spectrum for the thin film with an oxygen flow ratio of 50 % is almost constant, regardless of the increase of laser Power and temperature. These results indicate that the violet PL signal is probably due to defects related to interstitial Zn atoms.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.69-69
• /
• 2010

The research is the structural and optical characteristics of the Cadmium Sulfide(CdS) film, nanowires and nanobelts grown on the $Al_2O_3$ substrate using the vapor phase epitaxy method. The field-emission scanning electron microscopy(FE-SEM) were used to identify the shape of the surface of the nanostructures and x-ray diffraction(XRD) and transmission electron microscopy (TEM) were used to evaluate the structural characterisitcs. As a result, the XRD was confirmed the CdS peak and the substrate peak and TEM showed single crystals with wurtzite hexagonal structure on the nanostructures. As for the optical characteristic of the nanostructures, photoluminescence(PL) and micro-raman spectrum were measured. The PL measurements confirmed the emission peak related bound exciton to neutral donor($D^0X$) peak and free exciton(FX) peak. The micro-raman spectrum showed that the peak of the nanostructures were similar to the pure crystalline CdS peak and each peak were overtone of LO phonon of the hexagonal CdS of the longitudinal optical(LO) phonon mode. Therefore, it is confirmed that the CdS nanostructures grown in this research have superior crystallinity.

• Korean Journal of Metals and Materials
• /
• v.48 no.5
• /
• pp.445-448
• /
• 2010

For an enhanced thermoelectric performance, one-dimensional heterostructure nanowires were created that consisted of aBi core and Te shell. The structure was fabricated by depositing Te in-situ onto a Bi nanowire grown by our unique OFF-ON (on-film formation of nanowires) method. After examining a cross-sectional TEM image, it was found that diffusive interface was formed between Bi and Te. Selected area electron diffraction revealed that the crystallinity of the Te shell was some what lower compared to the highly single-crystalline Bi core. The Bi-Te core/shell nanowires can be a smart structure that suppresses phonon transport by several scattering mechanisms, making the OFF-ON method the simplest way to realize that structure.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.148-148
• /
• 2011

Recently, there have been many research activities to develop the large-area plasma source, which is able to generate the high-density plasma with relatively good uniformity, for the plasma processing in the thin-film solar cell and display panel industries. The large-area CCP sources have been applied to the PECVD process as well as the etching. Especially, the PECVD processes for the depositions of various films such as a-Si:H, ${\mu}c$-Si:H, Si3N4, and SiO2 take a significant portion of processes. In order to achieve higher deposition rate (DR), good uniformity in large-area reactor, and good film quality (low defect density, high film strength, etc.), the application of VHF (>40 MHz) CCP is indispensible. However, the electromagnetic wave effect in the VHF CCP becomes an issue to resolve for the achievement of good uniformity of plasma and film. Here, we propose a new electrode as part of a method to resolve the standing wave effect in the large-area VHF CCP. The electrode is split up a series of strip-type electrodes and the strip-type electrodes and the ground ones are arranged by turns. The standing wave effect in the longitudinal direction of the strip-type electrode is reduced by using the multi-feeding method of VHF power and the uniformity in the transverse direction of the electrodes is achieved by controlling the gas flow and the gap length between the powered electrodes and the substrate. Also, we provide the process results for the growths of the a-Si:H and the ${\mu}c$-Si:H films. The high DR (2.4 nm/s for a-Si:H film and 1.5 nm/s for the ${\mu}c$-Si:H film), the controllable crystallinity (~70%) for the ${\mu}c$-Si:H film, and the relatively good uniformity (1% for a-Si:H film and 7% for the ${\mu}c$-Si:H film) can be obtained at the high frequency of 40 MHz in the large-area discharge (280 mm${\times}$540 mm). Finally, we will discuss the issues in expanding the multi-electrode to the 8G class large-area plasma processing (2.2 m${\times}$2.4 m) and in improving the process efficiency.

• The Journal of the Korea institute of electronic communication sciences
• /
• v.18 no.5
• /
• pp.797-802
• /
• 2023

We prepared GZO (Ga₂O₃ : 5 wt %, ZnO : 95 wt %) thin film on glass substrate according to the substrate temperature using the pulsed laser deposition method and investigated electrical and optical properties of the thin film. Through the XRD measurements, their were confirmed that all GZO thin films grew preferentially in c-axis and the GZO thin film deposited at 300℃ showed the best crystallinity with a FWHM of 0.38°. As the substrate temperature increased from 150 to 300℃, the resistivity of GZO thin film tend to decrease, while the average transmittance in the visible light region was not significantly affected. The figure of merit of the GZO thin film deposited at 300℃ was 2.05×10⁴ Ω^-1·cm^-1, which was the best value, the resistivity and the average transmittance in the visible light region were 3.72 × 10^-4 Ω·cm and 87.71 %, respectively. In this study, it was found that GZO thin film is very promising material for transparent conducting thin film.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.24.1-24.1
• /
• 2009

Tantalum carbo-nitride($T_aC_xN_y$) films were deposited with chemical vapor deposition(CVD) using tert-butylimido tris-diethylamido tantalum (TBTDET, $^tBu-N=Ta-(NEt_2)_3$, $Et=C_2H_5$, $^tBu=C(CH_3)_3$) between $350^{\circ}C$ and $600^{\circ}C$ with argon as a carrier gas. Fourier transform infrared (FT-IR)spectroscopy was used to study the thermal decomposition behavior of TBTDET in the gas phase. When the temperature was increased, C-H and C-N bonding of TBTDET disappeared and the peaks of ethylene appeared above $450^{\circ}C$ in the gas phase. The growth rate and film density of $T_aC_xN_y$ film were in the range of 0.1nm/min to 1.30nm/min and of $8.92g/cm^3$ to $10.6g/cm^3$ depending on the deposition temperature. $T_aC_xN_y$ films deposited below $400^{\circ}C$ were amorphous and became polycrystal line above $500^{\circ}C$. It was confirmed that the $T_aC_xN_y$ film was a mixture of TaC, graphite, $Ta_3N_5$, TaN, and $Ta_2O_5$ phases and the oxide phase was formed from the post deposition oxygen uptake. With the increase of the deposition temperature, the TaN phase was increased over TaC and $Ta_3N_5$ and crystallinity, work function, conductivity and density of the film were increased. Also the oxygen uptake was decreased due to the increase of the film density. With the increase of the TaC phase in $T_aC_xN_y$ film, the work function was decreased to 4.25eV and with the increase of the TaN phase in $T_aC_xN_y$ film,it was increased to 4.48eV.