Kang, Myoung-Gu;Kim, Kyoung-Tae;Kim, Chang-Il
- Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
- /
- 2001.11b
- /
- pp.21-25
- /
- 2001
In this study, recovery of plasma etching· damage in PZT thin film with additive gas and re-annealing after etching have been investigated. The PZT thin films were etched as a function of $Cl_2/CF_4$ with addition of Ar and $O_2$ with inductively induced plasma. The etch rates of PZT thin films were 1450 $\AA$/min at 30% additive Ar into $(Cl_2(80%)+CF_4 (20%))$ and 1100 $\AA$/min at 10% additive $O_2$ into $C(Cl_2(80%)+CF_4(20%))$. In order to recovery properties of PZT thin films after etching, the etched PZT thin films were re-annealed at various temperatures in at $O_2$ atmosphere. From the hysteresis curves, ferroelectrical properties are improved by $O_2$ re-annealing process. The improvement of ferroelectric behavior at annealed sample is consistent with the increase of the (100) and (200) PZT peaks revealed by x-ray diffraction (XRD). From x-ray photoelectron spectroscopy (XPS) analysis, intensity of Pb-O, Zr-O and Ti-O peak are increased and the chemical residue peak is reduced by $O_2$ re-annealing. The ferroelectric behavior consistent with the dielectric nature of $Ti_xO_y$ is recovered by $O_2$ recombination during rapid thermal annealing process.
PDF

Lee, Kyu-Il;Kang, Hyun-Il;Park, Young;Park, Ki-Yeub;Song, Joon-Tae
- Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
- /
- 2002.07b
- /
- pp.570-573
- /
- 2002
Pb(Zr0.52Ti0.48)O3 (PZT) thin films were deposited on the Pt/Ti bottom electrode by rf magnetron sputtering method from target containing 5%, 25% and 50% Pb excess for applying ferroelectric random access memory (FRAM). PZT films were deposited at $300^{\circ}C$ and then they were crystallized by rapid thermal annealing (RTA) at $700^{\circ}C$. After RTA treatment, our results showed that all PZT films indicated perovskite polycrystalline structure with preferred orientation (110) and no pyrochlore phase was observed by X-ray diffraction (XRD) and by Scanning electron microscopy (SEM). A well-fabricated PZT film of excess Pb 25% capacitor showed a leakage current density in the order of $2.63{\times}10^{-7}A/cm^2$ at 100kV/cm, a remanent polarization of $3.385{\mu}C/cm^2$ and a coercive field of 41.32 kV/cm. The results showed that Pb excess of target affects to electrical properties of PZT thin film.
PDF

Lee, Jung-Mi;Kim, Kyoung-Tae;Kim, Chang-Il
- Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
- /
- 2003.11a
- /
- pp.23-26
- /
- 2003
The BLT thin film and MgO buffer layer were fabricated using a metalorganic decomposition method and the DC sputtering technique. The MgO thin film was deposited as a buffer layer on $SiO_2/Si$ and BLT thin films were used as a ferroelectric layer. The electrical of the MFIS structure were investigated by varying the MgO layer thickness. TEM showsno interdiffusion and reaction that suppressed by using the MgO film as abuffer layer. The width of the memory window in the C-Y curves for the MFIS structure decreased with increasing thickness of the MgO layer Leakage current density decreased by about three orders of magnitude after using MgO buffer layer. The results show that the BLT and MgO-based MFIS structure is suitable for non-volatile memory FETs with large memory window.
PDF