Reduce of Etching Damage of PZT Thin Films in $Cl_2/CF_4$ Plasma with addition of Ar and $O_2$

$Cl_2/CF_4$ 플라즈마 Ar, $O_2$ 첨가에 따른 PZT 막막의 식각 손상 효과

In this study, recovery of plasma etching· damage in PZT thin film with additive gas and re-annealing after etching have been investigated. The PZT thin films were etched as a function of $Cl_2/CF_4$ with addition of Ar and $O_2$ with inductively induced plasma. The etch rates of PZT thin films were 1450 $\AA$/min at 30% additive Ar into $(Cl_2(80%)+CF_4 (20%))$ and 1100 $\AA$/min at 10% additive $O_2$ into $C(Cl_2(80%)+CF_4(20%))$. In order to recovery properties of PZT thin films after etching, the etched PZT thin films were re-annealed at various temperatures in at $O_2$ atmosphere. From the hysteresis curves, ferroelectrical properties are improved by $O_2$ re-annealing process. The improvement of ferroelectric behavior at annealed sample is consistent with the increase of the (100) and (200) PZT peaks revealed by x-ray diffraction (XRD). From x-ray photoelectron spectroscopy (XPS) analysis, intensity of Pb-O, Zr-O and Ti-O peak are increased and the chemical residue peak is reduced by $O_2$ re-annealing. The ferroelectric behavior consistent with the dielectric nature of $Ti_xO_y$ is recovered by $O_2$ recombination during rapid thermal annealing process.