• Journal of the Korea Furniture Society
• /
• v.23 no.4
• /
• pp.435-439
• /
• 2012

This research was performed to evaluate surface performance of gold plated carbonized board. After the carbonization at $850^{\circ}C$, volume, weight, and density decreased by 65.25%, 71.35% and 17.64%, respectively. Abrasion resistance and surface hardness of non-carbonized board exhibited the highest values of 0.093 g/100 revolution and 26.43 N/$mm^2$, respectively. Gold plated carbonized board showed intermediate values, 0.587 g/100 revolution of abrasion resistance and 24.35 N/$mm^2$ of surface hardness. Carbonized board showed the lowest values, 0.863 g of abrasion resistance and 21.50 N/$mm^2$, of surface hardness. These results were thought to reflect propertional relationship between abrasion resistance and surface hardness. Abrasion resistance and surface hardness of carbonized board appeared able to be improved by surface treatment such as plating.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.1
• /
• pp.60-66
• /
• 2018

For new use development of carbonized board, we investigated the effect of carbonization temperature on the surface temperature of carbonized board manufactured from a plywood, particle board, MDF, and wood of Fraxinus rhynchophylla at different carbonization temperature ($400^{\circ}C{\sim}1100^{\circ}C$). The surface temperature of carbonized board precipitously increased until 12 minutes elapsed, after smoothly increased and thereafter which were stable after 20 minutes. The higher carbonization temperature increased density of carbonized board and surface temperature of carbonized board so that density is considered to influence surface temperature change. Moreover, carbonized boards kept heat for a long time because the descent velocity of carbonized boards' surface temperature was slower than that of heater's.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.2
• /
• pp.163-171
• /
• 2014

Environmental issues about indoor air quality have been increased and focused on volatile organic compounds (VOCs) caused cancer, asthma, and skin disease. Reducing VOCs has been attempted in many different methods such as using environmentally friendly materials and air cleaner or purifier. Charcoal is well known material for absorbing VOCs. Therefore, carbonized board from medium density fiberboard has been developed. We assumed that the source of carbonized boards can be any type of wood-based panels. In this study, carbonized boards were manufactured from oriented strand board (OSB) at 400, 600, 800, and $1000^{\circ}C$. Each carbonized OSB (c-OSB) was evaluated and determined physiomechanical characteristics such as exterior defects, dimensional shrinkage, modulus of elasticity, and bending strength. No external defects were observed on c-OSBs at all carbonizing conditions. As carbonizing temperature increased, less porosity between carbonized wood fibers was observed by SEM analysis. The higher rate of dimensional shrinkage was observed on c-OSB at $1000^{\circ}C$ (66%) than c-OSB at 400, 600, and $800^{\circ}C$ (47%, 58%, and 63%, respectively). The densities of c-OSBs were lower than original OSB, but there was no significant different among the c-OSBs. The bending strength of c-OSB increased 1.58 MPa (c-OSB at $400^{\circ}C$) to 8.03 MPa (c-OSB at $1000^{\circ}C$) as carbonization temperature increased. Carbonization temperature above $800^{\circ}C$ yielded higher bonding strength than that of gypsum board (4.6 MPa). In conclusion, c-OSB may be used in sealing and wall for decorating purpose without additional artwork compare to c-MDF which has smooth surface.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.1
• /
• pp.58-63
• /
• 2013

This study is a basic research for practical applications of carbonized boards, which measured thermal conductivity and electrical properties of carbonized boards manufactured at different carbonization temperature ($400{\sim}1,100^{\circ}C$) using a medium density fiberboard, particleboard, plywood and wood (Fraxinus rhynchophylla). The highest value of thermal conductivity was 0.1326 m/k at carbonization temperature of $900^{\circ}C$ in the carbonized particleboard. Overall, the higher density of carbonized board, thermal conductivity was faster. As the electrical resistivity decreased with increased carbonization temperature, it was almost close to conductor after carbonization temperature of $1,000^{\circ}C$. When electricity has worked on the carbonized board by high voltage, the current and the electric power increased and surface temperature of carbonized board was high.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.3
• /
• pp.327-334
• /
• 2017

This study was carried out to investigate the formaldehyde emission of building materials and effect of carbonized-board (c-board) on formaldehyde reduction using a chamber method. As a result, reduction performance of formaldehyde was in the order of c-board (90%), c-bamboo board (84%), diatomite-based panel (82%), allophane-based tile (78%), Pinus densiflora timber (58%), MDF (54%) and gypsum-based board (46%) for approximately 12 days. In $1.9m^3$ chamber filled with particleboard (PB), the formaldehyde reduction performance of c-board was significantly increased with increasing input amount of c-board for 68 days. In particular, the formaldehyde emissions can be reduced above 40% and 75% by input rate of 10% and 30% c-board, respectively, in given ratio of chamber volume and PB area.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.3
• /
• pp.424-429
• /
• 2016

In this study, the carbonized boards were manufactured from different types of wood-based panel and then their moisture absorption/desorption properties were investigated and compared. The carbonization temperature was maximum $600^{\circ}C$ with 2 h maintains. Test results showed higher absorption/desorption capacity on carbonized plywood than carbonized MDF, PB, and OSB, respectively. However, carbonized MDF, OSB, and plywood had similar absorption/desorption rate per hour. It means carbonized OSB and plywood can transfer moisture into deeper side and then possibly hold more amount of water. Based on SEM images, carbonized OSB and plywood showed more like wood structure, while carbonized MDF and PB had only wood fiber or/and chunk of wood fragments. Therefore, original wood structure may affect moisture absorption/desorption capacity. In order to manufacture high moisture absorbing/desorbing carbonized board, wood structure should be considered and then carbonized.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.3
• /
• pp.185-190
• /
• 2010

This study was focused to make a wooden plate that is engraved with writings or pictures on the medium density fiberboard (MDF), and then to produce a calligraphy-carving artwork by carbonization of the carved MDF. The external appearances and anatomical changes were investigated on the carbonized MDF and aesthetic characteristics was also discussed. No split and no twist were found after the carbonization (at $850^{\circ}C$) of the calligraphy-encarved MDF, shrinkages of the MDF were observed with portions of 21.8% in length, 18.8% in width and 43.5% in thickness, and 69.2% of weight loss with density decrease of 14.8% were observed as well. From the observation of the carbonized board by a scanning electron microscope, specific phenomena were found: the adhesives, surrounding the fiber's surface and pits, were carbonized, the woody fibers were changed smoothly, the pits were opened, the fiber' size was uniformized, and the organization was compacted. By the combination of handmade calligraphy-woodcarving and crack-free carbonizing methods, it was able to find a new method for manufacture carbonized calligraphy-woodcarving artwork. It is concluded that the calligraphy-woodcarving artwork using carbonized board can be a new access for the eco-friendly art that has the advantage of the functionality of charcoal and the aesthetic of calligraphy-woodcarving simultaneously.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.5
• /
• pp.555-562
• /
• 2014

Characteristics of carbonized fiberboard such as chemical materials absorption, electromagnetic shielding, and electrical and mechanical performance were determined in previous studies. The carbonized board therefore confirmed that having excellent abilities of these characteristics. In this study, the effect of density on physical properties and sound absorption properties of carbonized fiberboards at $800^{\circ}C$ were investigated for the potential use of carbonized fiberboards as a replacement of conventional sound absorbing material. The thickness of fiberboards after carbonization was reduced 49.9%, 40.7%, and 43.3% in low density fiberboard (LDF), medium density fiberboard (MDF), and high density fiberboard (HDF), respectively. Based on SEM images, porosity of carbonized fiberboard increased by carbonization due to removing adhesives. Moreover, carbonization did not destroy structure of wood fiber based on SEM results. Carbonization process influenced contraction of fiberboard. The sound absorption coefficient of carbonized low density fiberboard (c-LDF) was higher than those of carbonized medium density fiberboard (c-MDF) and carbonized high density fiberboard (c-HDF). This result was similar with original fiberboards, which indicated sound absorbing ability was not significantly changed by carbonization compared to that of original fiberboards. Therefore, the sound absorbing coefficient may depend on source, texture, and density of fiberboard rather than carbonization.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.4
• /
• pp.293-299
• /
• 2009

In manufacturing the crack-free carbonized boards using fiberboards, shrinking ratio, weight loss and density variation of carbonized boards at each carbonization temperature were investigated. Fiberboards with thickness of 3, 4.5, 6, and 18 mm were carbonized while pressed with pressure plates at different temperature from $400^{\circ}C$ to $1,000^{\circ}C$ using a ordinary laboratory furnace. Either of crack or twist was not observed in fiberboards by adapting the pressing carbonization method. The ratios of shrinkage of length, width, and thickness were 10~25%, 12~25%, and 28~48%, respectively, and shrinkage ratio of thickness was higher than those of length and width with increasing the carbonization temperature. Weight loss tended to increase with increasing the carbonization temperature, but low correlation between weight loss in thickness of fiberboards and carbonization temperature was observed. Density of 3 mm carbonized hardboard had the highest value and it tended to increase with increasing the carbonization temperature.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.5
• /
• pp.511-518
• /
• 2017

In recent years, many interests and researches on the insulations required the multiple performances other than insulation performance. The purpose of this paper is to find the optimal ratio between wood fiber and rice-husks charcoal to develop a structural board with carbonized rice-husks. Based on these rice-husks charcoals, basic research was carried out to develop thermal insulation materials with structural performance, and the following conclusions were obtained. The MC of the board using the carbonized rice-husks was 3.2-4.1% and the density was 0.58-0.68, indicating the possibility of excellent structural material. The bending strength was 9.1-32.6 MPa in the length direction and 9.2-34.1 MPa in the width direction. It is possible to obtain the bending strength of the normally used MDF level and to find the possibility of development of the thermal insulation material having the structural performances.