• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.05b
• /
• pp.53-56
• /
• 2009

This study reviewed the characteristics of concrete made of performance improving mixture materials based on KOH as a means to resolve the problems of initial quality reduction that result in concretes with blast furnace slag powder. Summarizing the results, first as the characteristics of fresh concrete, liquidity was found to reduce in general with increased BS substitution ratio. Objective range of liquidity was not satisfied in all mixes according to the use of performance improving mixture materials. Air capacity was satisfied to the objective range in all mixes. As the characteristics of hardened concrete, while compressive strength showed a decreasing trend with increasing BS substitution ratio at early age, increasing trend was shown by the plain with increasing BS substitution ratio at later age. On the other hand, K1 and K2 were only effective among mixture materials at early age, but K1F30 showed excellent strength at both early and later ages.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.34 no.5
• /
• pp.13-18
• /
• 2018

In this research, regarding the type three blast furnace slag (BS) regulated by KS F 2563 and supplied to actual ready mixed concrete plant, the fineness on specification and actually measured fineness by Blain test were compared, and by applying the hydrometer method used for early prediction of concrete strength, the feasibility of the hydrometer method for acquisition inspection of BS was analyzed. Additionally, the influence of various fineness of BS on properties of cement mortar was also assessed. According to the experimental results of this research, correlation of fineness values between specification and actually measured data were not matched. In the case of the rapid evaluation method using hydrometer, a good relation was shown between the fineness data obtained from hydrometer and Blain test. furthermore, from the cement mortar properties test, there was a good relation was obtained between fineness data from rapid evaluation method by hydrometer and cement mortar properties, while there was no clear relation between fineness data from specification and cement mortar properties. Hence, as a qulity controlling method of BS fineness, a rapid evaluation method using hydrometer is suggested as a new method.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.297-298
• /
• 2023

In the concrete industry, efforts are being made to reduce CO₂ emissions, and technologies that collect, store, and utilize CO₂ have recently been studied. This study analyzed the change in compressive strength after the accelerated carbonation test of Non-Sintered Cement(NSC) mortar. Type C Fly Ash and Type F Fly Ash were mixed in a 1:1 ratio and then mixed with Blast Furnace Slag fine powder to produce NSC. The mortar produced was cured underwater until the target age. In addition, an accelerated carbonation test was conducted under the condition of a concentration of 5 (±1.0%) of CO₂ gas for 14 days. The mortar compressive strength was measured before and after 14 days of accelerated carbonation test based on the 7th and 28th days of age. As a result of the experiment, the compressive strength was improved in all binder. In general, the compressive strength of NSC mortar subjected to the accelerated carbonation test was similar to that of Ordinary Portland Cement(OPC) mortar not subjected to the accelerated carbonation test.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.106-113
• /
• 2010

We were tried to draw a conclusions related to additive amount of gypsum in blast furnace slag in the study. In the result, fluidity of concrete decreased with an increase of gypsum and was not satisfied with KS standard in the cases of natural gypsum and limestone sludge more than 2.6% addition. Early compressive strength of concrete containing desulfurized gypsum, fluosilicic acid gypsum and phosphoric acid gypsum were improved respectively but calcined lime sludge and lime powder were not influenced on strength. If available, additive gypsum should be managed less than 2.0% owing to low fluidity. In low temperature, fluosilicic acid gypsum was to advantages on the fluidity while desulfurized gypsum was in high temperature. There also are conclusions that additive gypsum was to be 2.6% in winter and in summer; it's to be fewer than 2.6%.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.63-64
• /
• 2022

In this study, the quality of mineral admixture, Comparison of blast-furnace slag(BS) and fly ash(FA)in Korea and China. In the case of BS, Korea is mainly classified into 1 type to 4 types according to the specific surface area, whereas China is classified into S105, 95, and 75 according to the activity index of 28 days of age. In the case of FA, Korea is like BS, is mainly classified into types 1 to 4 according to specific surface area, whereas China is classified into F, C (class F, class C) by ingredients and class I, II, and III according to powder and ignition loss.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.3
• /
• pp.252-258
• /
• 2014

With the vision of 'a low carbon green develop' various industrial by-products were used as replacement of cement, in order to reduce $CO_2$ emissions from the manufacturing process of cement. Blast furnace slag is one of the industrial by-products. Due to the similar chemical compositions to ordinary Portland cement, blast furnace slag have been widely used in concrete with minimum side effects. Hence, in recent years, alkali activated slag-based composites are extensively studied by many researchers. However, the alkali activator can cause a number of problems in practice. Therefore, in this study, an alternative way of activating the slag was investigated. To activate the slag without using an alkali activator, calcium sulfate dihydrate was chosen and mixed with natural recycled fine aggregate. Fundamental properties of the slag-based mortar were tested to evaluate the effect of calcium sulfate dihydrate.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.2
• /
• pp.107-114
• /
• 2014

The objective of this study is to evaluate the strength development of blast furnace slag concrete in response to the use of recycled aggregate as alkali activator. The influence of the amount of recycled aggregate was evaluated depending on different ratios of replacement for each RFA and RCA to NFA and NCA, respectively. The results indicated that as replacement of RFA and RCA increased, their strength exhibited to be increased. This was due to the fact that the latent hydraulic properties of blast furnace slag was activated by the alkali in recycled aggregates. However, in case of 365-days, it showed lower compressive strength than using NA(natural aggregates) which could be explained as the exhaustively use of alkali containing in RA. The specimens using RA showed about 90% of compressive strength comparing with specimens using NA.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.43-44
• /
• 2023

This study evaluated the mechanical and electrical properties of low-cement mortar using a large amount of industrial by-products to reduce carbon emissions from the cement industry. As types of industrial by-products, blast furnace slag and fly ash, which are representative materials, were used, and ultra-high fly ash was mixed and evaluated to solve the problem of initial strength loss. In addition, in order to evaluate the electrical properties, 1% of MWCNT was incorporated relative to the powder mass. As experimental items, the compressive strength was measured on the 1st, 3rd, 7th and 28th days of age, and the rate of change in electrical resistance was measured on the 28th day of age. As a result of the experiment, the initial strength of the test specimen mixed with blast furnace slag and fly ash was significantly lower than that of 100% cement, and the specimen mixed with blast furnace slag showed strength equal to that of cement at 28 days of age. As an electrical characteristic, the electrical resistance was reduced when the load was loaded, and this reason is judged to be the effect of improving the conductivity as the connection between CNTs is narrowed by the compressive load.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.552-559
• /
• 2023

The purpose of this study is to evaluate the crack reduction performance of blast furnace slag concrete mixed with expansive and swelling admixtures. As a basic performance test, various ingredients such as blast furnace slag fine powder (BFS), calcium sulfoaluminate (CSA), bentonite, and hydroxypropyl methyl cellulose (HPMC) were used, and the results showed that bentonite showed superior performance compared to HPMC. Afterwards, a MOCK-UP test was conducted to evaluate cracking and drying shrinkage according to the mixing ratio. As a result, when bentonite and a small amount of calcium phosphate were added, drying shrinkage was reduced and cracking was reduced. In particular, a cement mixture consisting of 30 % BFS, 1 % bentonite, and 1 % calcium phosphate showed optimal crack-free performance. It is believed that BFS concrete will contribute to compensating for shrinkage through continuous expansion activity and can be used for field applications.

• Computers and Concrete
• /
• v.20 no.1
• /
• pp.77-84
• /
• 2017

Shirasu, a pyroclastic flow deposit, showed considerable performance as aluminosilicate source in geopolymer, based on past research. However, the polymerization reactivity was somewhat lower compared to the traditional fly ash based geopolymer even though the long-term strength was fairly good. The present study concentrates on the development of higher initial strength performance of Shirasu based geopolymer by utilizing ground granulated blast furnace slag as an admixture. Mortars with various mix proportions were adopted to study the effect of parametric changes on strength development along with the addition of slag in different percentages. A combination of sodium hydroxide and sodium silicate was used as alkaline activators considering parameters like molar ratios of alkali to geopolymer water and silica to alkali molar ratio. The mortars were cured at elevated temperatures under different curing conditions to analyze the effect on strength development. Compressive strength test, mercury intrusion porosimetry and X-ray powder diffraction were carried out to assess the strength performance and microstructure of slag-Shirasu based geopolymer. Based on the experimental study, it was observed that the initial and long-term strength development of Slag-Shirasu geopolymer were improved by the addition of slag.