• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.08a
• /
• pp.89.4-89
• /
• 1998

• Korean Journal of Materials Research
• /
• v.30 no.10
• /
• pp.502-508
• /
• 2020

This paper focuses on the electrical properties and stability against DC accelerated aging stress of ZnO-V₂O₅-MnO₂-Nb₂O₅-Bi₂O₃-Co₃O₄-Dy₂O₃ (ZVMNBCD) varistor ceramics sintered at 850 - 925 ℃. With the increase of sintering temperature, the average grain size increases from 4.4 to 11.8 mm, and the density of the sintered pellets decreases from 5.53 to 5.40 g/㎤ due to the volatility of V₂O₅, which has a low melting point. The breakdown field abruptly decreases from 8016 to 1,715 V/cm with the increase of the sintering temperature. The maximum non-ohmic coefficient (59) is obtained when the sample is sintered at 875 ℃. The samples sintered at below 900 ℃ exhibit a relatively low leakage current, less than 60 mA/㎠. The apparent dielectric constant increases due to the increase of the average grain size with the increase of the sintering temperature. The change tendency of dissipation factor at 1 kHz according to the sintering temperature coincides with the tendency of the leakage current. In terms of stability, the samples sintered at 900 ℃ exhibit both high non-ohmic coefficient (45) and excellent stability, 0.8% in 𝚫E_B/E_B and -0.7 % in 𝚫α/α after application of DC accelerated aging stress (0.85 E_B/85 ℃/24 h).

• Korean Journal of Materials Research
• /
• v.12 no.10
• /
• pp.791-795
• /
• 2002

We studied the physical properties of $Co_3$$O_4$-added Ni-Zn ferrite which were sintered at 1050~110$0^{\circ}C$ for 2 hours. X-ray diffraction showed a spinel structure, and optical microscopy showed grain sizes of 5 to 10 $\mu\textrm{m}$. As the sintering temperature was increased from $1050^{\circ}C$ to $1070^{\circ}C$, the initial permeability and magnetic induction increased, and both of the loss factor and the coercive force decreased. The Curie temperatures were about $^234~245{\circ}C$ with added $Co_3$$O_4$. The initial permeability was 350 to 420 and maximum magnetic induction density and coercive force 4870G to 4980G and 0.15 Oe to 0.21 Oe, respectively which were similar to those of Ni-Zn ferrite synthesized in the conventional process. The frequency of specimen was in the range of 1MHz to 300MHz. In the plot of initial permeability vs. frequencies, a $180^{\circ}C$ rotation of the magnetic domain could be perceived in a broad band of microwave before and after the resonance frequency.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.8
• /
• pp.664-670
• /
• 2002

The electrical characteristics of $ZnO-Pr_6O_{11}-CoO-Cr_2O_3-Y_2O_3$(ZPCCY)-based varistors were investigated with $Y_2O_3$ content in the range of 0.0~4.0 mol%. As $Y_2O_3$ content is increased, the average grain size was markedly decreased in the range of 18.6~3.2 $\mu m$ and the density of the ceramic was decreased in the range of 5.53 ~3.74 $g/\textrm{cm}^3$. While, the varistor voltage was increased in the range of 39.4~748.1 V/mm and the nonlinear exponent was in the range of 4.5~51.2 with increasing $Y_2O_3$ content. The addition of $Y_2O_3$ greatly enhanced the nonlinear properties of varistors, compared with the varistor without $Y_2O_3$. In particular, the varistors with $Y_2O_3$content of 0.5 mol% exhibited the highest nonlinearity, in which the nonlinear exponent is 51.2 and the leakage current is 1.3 $\mu A$. The donor concentration and the density of interface states were decreased in the range of (4.19~0.14) $\times$10$^{18}$ /㎤ and (5.38~1.15)${\times}10^{18}/\textrm{cm}^3$, respectively, with increasing $Y_2O_3$ content.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.10
• /
• pp.897-901
• /
• 2003

The microstructure and varistor characteristics of ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-Dy$_2$O$_3$(ZPCCD)-based ceramics were investigated with Dy$_2$O$_3$ content in the range of 0.0∼2.0 mol%. As Dy$_2$O$_3$ content is increased, the average grain size was decreased in the range of 18.6∼4.7 $\mu$m and the density was decreased in the range of 5.53∼4.34 g/cm$^3$. While, the varistor voltage was increased in the range of 39.4∼436.6 V/mm and the nonlinear exponent was in the range of 4.5-66.6 with increasing Dy$_2$O$_3$ content. The addition of Dy$_2$O$_3$ highly enhanced the nonlinear properties of varistors, compared with the ceramics without Dy$_2$O$_3$ Particularly, the ceramics with Dy$_2$O$_3$ content of 0.5 mol% exhibited the highest nonlinearity, in which the nonlinear exponent is 66.6 and the leakage current is 1.2 $\mu$A.A.A.

• Journal of Fisheries and Marine Sciences Education
• /
• v.19 no.1
• /
• pp.1-7
• /
• 2007

The purpose of this study was to investigate geochemical characteristics of surface sediments in the Keum river estuary adjacent to coastal area. For this study we collected the 21 surface sediments samples. Mean size of surface samples was $3.24{\sim}6.65{\phi}$ on inner estuary and was $2.15{\sim}3.42{\phi}$ on outside estuary. Surface samples were composed of silt on inner estuary and were composed of sand which was more larger than $4{\phi}$ on outside estuary. Most major elements except CaO, $Na_2O$ showed good relationships between variation of contents and grain size. Contents of $Al_2O_3$, $Fe_2O_3$, MgO, $K_2O$, $TiO_2$, $P_2O_5$ and $M_nO$ were increased predominately owing to the variation of mean size of surface samples. Contents of Co, Cr, Cu, Li, Sr, Zn, La, Ce, Pb, Rb, Nd have a good relationships with grain size but Ba, Th, Sm have not. All of major and minor elements contents except $K_2O$ and Ba were less than world mean contents of shallow surface sediments but apprehend a high pollution possibility on silt sediments in the estuaries.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.355-356
• /
• 2008

In this work, ZnO films doped with different contents of Indium (0.1at.%, 0.3at.%, 0.6at.%, respectively) were deposited on Si (111) substrate that has 1~20 $\Omega$cm by pulsed laser deposition (PLD) at $600^{\circ}C$ for 30min. The thickness of the films are about 250 nm. The structural, optical and electrical properties of the films were investigated using X-ray Diffraction (XRD), Atomic force microscope (AFM), Photoluminescence (PL) and Hall measurement. It has been found that RMS of the films is decreased and grain size is increased with increasing the contents of doped Indium. The results of the Photoluminescence properties were indicated that the films have UV emission about 380nm and shows a little red shitf with increasing contents of doped indium. The result of the Hall measurement shows that the concentration and resisitivity in doped ZnO are as changing as one order, respectively ${\sim}10^{18}/cm^2$, ${\sim}10^{-2}cm{\Omega}cm$.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.7
• /
• pp.2004-2008
• /
• 2014

This paper reports the facile synthesis methods of zinc oxide (ZnO) nanoparticles, Z1-Z10, using diethylene glycol (DEG) and polyethylene glycol (PEG400). The particle size and morphology were correlated with the PEG concentration and reaction time. With 0.75 mL of PEG400 in 150 mL of DEG and a 20 h reaction time, the ZnO nanoparticles began to disperse from a collective spherical grain shape. The ZnO nanoparticles were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and a $N_2$ adsorption-desorption studies. The Brunauer-Emmett-Teller (BET) surface areas of Z4, Z5 and Z10 were 157.083, 141.559 and 233.249 $m^2/g$, respectively. The observed pore diameters of Z4, Z5 and Z10 were 63.4, 42.0 and 134.0 ${\AA}$, respectively. The pore volumes of Z4, Z5 and Z10 were 0.249, 0.148 and 0.781 $cm^3/g$, respectively. The photocatalytic activity of the synthesized ZnO nanoparticles was evaluated by methylene blue (MB) degradation, and the activity showed a good correlation with the $N_2$ adsorption-desorption data.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.52.2-52.2
• /
• 2011

본 연구의 목적은 CIGS 태양전지의 두 가지 TCO층 중 AZO를 제외한 intrinsic ZnO의 전자빔 처리 영향에 대한 특성 분석을 하고자 함이다. 또한 추후 CIGS 태양전지를 제조하여 적용 시 전자빔 처리 전후의 특성이 어떻게 변하는지를 알아보기 위한 사전 실험이다. Intrinsic ZnO는 RF magnetron sputter 를 이용하여 약 100nm의 두께로 증착 하였다. 이때 공정 압력을 변수로 RF power는 80W로 설정 하였으며 Ar 분압은 10mtorr, 5mtorr, 1mtorr로 각각 달리 하며 증착 하였다. 이후 전자빔 처리를 위해 각각의 시편에 Argon flow 7sccm 상태에서 DC power 3kW, RF power 300W의 세기로 전자빔 처리를 실시 하였다. 전자빔 처리에 따른 전기적, 구조적 특성을 분석하기위해 Hall measurement와 SEM, XRD, UV-vis spectroscopy을 사용하였다. 먼저 Hall measurement 측정을 통한 전기적 분석 결과 비저항이 무한대에서 약 $40m{\Omega}{\cdot}cm$로 감소된 결과를 도출 할 수 있었으며, $2{\sim}3.4{\times}10^{18}/cm^3$ 이상의 carrier density 가 측정 되었다. UV-vis spectroscopy를 이용한 투과도 측정결과 모든 시편에서 Band gap이 감소하는 결과를 보였다. SEM, XRD를 이용한 분석결과 결정성 및 grain의 크기가 증가하는 결과를 얻을 수 있었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.11
• /
• pp.869-874
• /
• 2010

Magnetoelectric composites with compositions (1-x)[0.5PZT-0.25PNN-0.25PZN](ferroelectric) - x[$(Ni_{0.9}Zn_{0.1})Fe_2O_4$](ferrite) in which x varies as 0, 0.1, 0.2, 0.4, 0.6, 0.8, 1.0 were prepared by conventional ceramic process. The presence of two phases (ferroelectric phase with large grain and ferrite phase with small grain) in the particulate ceramic composites was confirmed by XRD, SEM and EDX. The ferroelectric and magnetic properties of the composites were studied by measuring the P-E and M-H hysterisis loop on the composite composition (x=0, 0.1, 0.2, 1), they were strongly affects of the phase content in composite. The magnetoelectric votage was measured as a function of DC magnetic field and the maximum magnetoelectric voltage coefficient of 14 mV/cm Oe was observed in x=0.2(80 mol% ferroelectric and 20 mol% ferrite phase).